Abstract: A biaxially oriented polyphenylene sulfide film contains polyphenylene sulfide and polyether imide, wherein the contents of the polyphenylene sulfide and the polyether imide are 70 to 99 parts by weight and 1 to 30 parts by weight respectively when the total amount of the polyphenylene sulfide and the polyether imide is taken as 100 parts by weight, and further contains a compound having one or more groups selected from an epoxy group, an amino group and an isocyanate group as a compatibilizing agent in an amount of 0.1 to 10 parts by weight based on 100 parts by weight of the polyphenylene sulfide and polyether imide in total, and the polyether imide forms a dispersed phase with an average particle diameter of 10 to 500 nm and the biaxially oriented polyphenylene sulfide film exhibits a tensile elongation at break of 110 to 250% in both the longitudinal direction and width direction.

Abstract: A biaxially oriented polyarylene sulfide film which has an excellent elongation at break and flatness is provided. The biaxially oriented film may be a biaxially oriented polyarylene sulfide film which is substantially composed of a polyarylene sulfide resin (A), wherein one of the elongations at break in the machine direction and in the transverse direction of the film is not lower than 110%; one of the breaking stresses in the machine direction and in the transverse direction of the film of the film is not higher than 200 MPa; and both of the heat shrinkage ratio in the machine direction of the film and that in the transverse direction of the film at 260° C. for 10 minutes are not less than 0% and not more than 10%.

Abstract: A biaxially oriented polyarylene sulfide film is provided having an excellent heat resistance, dimensional stability, electrical properties and chemical resistance, which has an excellent heat moldability, film-forming stability and flatness brought about by the decrease in breaking stress and increase in the elongation at break at 200° C. A biaxially oriented polyarylene sulfide film made of a polyarylene sulfide resin composition having a melt crystallization temperature of not lower than 160° C. and not higher than 220° C., the biaxially oriented polyarylene sulfide film comprising 70 to 99 parts by weight of the polyarylene sulfide and 1 to 30 parts by weight of thermoplastic resin A; the thermoplastic resin A constituting a dispersed phase having an average dispersion diameter of 50 nm to 500 nm; the biaxially oriented polyarylene sulfide film having a breaking stress at 200° C.

Abstract: There are provided a microporous film for an electric storage device separator, which can increase energy density and power density when used in an electric storage device, and which is excellent in handling properties in a processing step to the electric storage device, as well as an electric storage device separator and an electric storage device, using the microporous film. Specifically, provided is a microporous film for an electric storage device separator, characterized by including a porosity of 70% or more, a strength of 40 MPa or more in a longitudinal direction, an average pore size of from 40 to 400 nm, anuclear pores, and exhibiting biaxial orientation.

Abstract: A biaxially oriented white polypropylene film containing a core layer (layer A) and a skin layer (layer B), said layer B is laminated at least on one surface of said layer A, wherein said layer A contains a polypropylene resin having ?-crystal activity and 1 to 20 mass % particle (a) having an average dispersed diameter of 60 to 400 nm, and wherein, said layer B contains a polypropylene resin and 0.05 to 5 mass % particle (b) of an average dispersed diameter of 1 to 4 ?m. The present invention provides a biaxially oriented white polypropylene film excellent in film quality and productivity and capable of making sensitivity and productivity compatible in a high level when used as a base for a receiving sheet, and a receiving sheet for thermal transfer recording made thereof.

Abstract: It is aimed to provide a polyarylene sulfide film for an acoustic instrument vibrating plate excellent in heat resistance, molding processability, acoustic properties, and also heat moldability. Provided is a polyarylene sulfide film wherein the elongation at break in either a longitudinal direction or a width direction of the film is 100% or more and 250% or less, and the Young's modulus in either a longitudinal direction or a width direction of the film is 1.5 GPa or more and less than 4 GPa.

Abstract: A biaxially oriented polyarylene sulfide film and laminated polyarylene sulfide sheets of the film contain polyarylene sulfide and other thermoplastic resin A different from the polyarylene sulfide, wherein the contents of the polyarylene sulfide and the thermoplastic resin A are 70 to 99 parts by weight and 1 to 30 parts by weight respectively when the total amount of the polyarylene sulfide and the thermoplastic resin A is taken as 100 parts by weight and the resin thermoplastic A forms a dispersed phase with an average particle diameter of 10 to 500 nm and the biaxially oriented polyarylene sulfide film exhibits a tensile elongation at break of 110 to 250% in at least one of the longitudinal direction and width direction and a tensile fracture elongation of 80 to 250% in the other direction.

Abstract: A biaxially stretched polypropylene film of the present invention has high stiffness in the film longitudinal direction and can be manufactured by a conventional longitudinal-transverse sequential biaxial stretching method, since the biaxially stretched polypropylene film comprises a polypropylene which comprises a polypropylene having controlled specific values of a melt strength (MS) and a melt flow rate (MFR) at 230° C. or consists of a polypropylene having controlled specific values of a melt strength (MS) and a melt flow rate (MFR) at 230° C. and/or a Trouton ratio of the polypropylene is controlled at a specific value, moreover, the biaxially stretched polypropylene film contains regulated longitudinal fibrils.

Abstract: A microporous polypropylene film where film formability is improved in accordance with a ?-crystal technique which allows microporous films to be continuously manufactured at low cost is disclosed. In addition, a microporous polypropylene film of which the specific gravity is further reduced is provided. Furthermore, a microporous polypropylene film with a significantly high permeability is provided. In addition, manufacturing methods for these microporous polypropylene films are provided.

Abstract: A biaxially oriented white polypropylene film for thermal transfer recording including a film containing polypropylene resin having a ?-crystal ratio of about 30% or more and a melting temperature of about 140 to about 172° C., and which has substantially non-nucleus voids, a void ratio of about 30 to about 80% and a sum of strengths of longitudinal direction and of transverse direction of the film at 2% elongation (F2 value) being in the range of about 10 to about 70 MPa and a surface glossiness being in the range of about 10 to about 145%.

Abstract: A biaxially stretched polypropylene film of the present invention has high stiffness in the film longitudinal direction and can be manufactured by a conventional longitudinal-transverse sequential biaxial stretching method, since the biaxially stretched polypropylene film comprises a polypropylene which comprises a polypropylene having controlled specific values of a melt strength (MS) and a melt flow rate (MFR) at 230° C. or consists of a polypropylene having controlled specific values of a melt strength (MS) and a melt flow rate (MFR) at 230° C. and/or a Trouton ratio of the polypropylene is controlled at a specific value, moreover, the biaxially stretched polypropylene film contains regulated longitudinal fibrils.

Abstract: Disclosed is a biodegradable oriented film of a plasticizer-containing biodegradable resin, of which the both surfaces are coated with at least one thin layer and of which the loop stiffness change (&Dgr;R) after heat treatment at 130° C. for 30 minutes is at most 20%. This is favorable for wrapping films.

Abstract: A method of forming a polymer that simultaneously provides an improved level of impact resistance and processability in which an .alpha.-olefin monomer is subjected to polymerization in the presence of a Ziegler-Natta catalyst system and a blend of electron donors including dicyclopentyldimethoxysilane (DCPMS) and propyltriethoxysilane (PTES). The polymer so formed will have a relationship between a first melt flow rate of a homopolymer formed by polymerizing an .alpha.-olefin monomer in the presence of a Ziegler-Natta catalyst system and a first electron donor (MFR (a)), and a second melt flow rate of a homopolymer formed polymerizing an .alpha.-olefin monomer in the presence of the Ziegler-Natta catalyst system and a second electron donor (MFR (b)), is defined by the equation:1.2.ltoreq.log [MFR(b)/MFR(a)].ltoreq.1.

Abstract: A polypropylene resin composition including (A) 50-90 parts by weight of a polypropylene resin including (a) 3-30 weight % of stereoblock polypropylene having a weight-average molecular weight of 5,000-1,000,000, a percentage of five continuous propylene monomer units in which all propylene bonds are meso bonds and a percentage of five continuous propylene monomer units in which all propylene bonds are racemic bonds being 70% or more and 5% or more, respectively relative to the all propylene bonds, and (b) 70-97 weight % of an ultra-high stereospecific polypropylene having a melt flow rate of 0.1-1,000 g/10 minutes, an average meso chain length Nm calculated from a triad percentage determined from .sup.13 C-NMR spectrum by the following formula of Nm=2[mm]/[mr]+1, wherein [mm] is (isotactic triad/total triad).times.100 (%) and [mr] is (heterotactic triad/total triad).times.100 (%), meeting a relation of Nm>250+29.

Abstract: The pressure to the cracks in the concrete building and the like exerted by a binding material supplied thereinto is buffered by the expansion of a pressure buffering portion located somewhere between the supply pump and the supply pipe and after the supply pump is disconnected, the binding material supplying operation is succeeded by the pressure buffering portion which, having therein reserved the binding material by expansion, forces the binding material out into the cracks by contraction.