Abstract: Even when a tin-based polymerization catalyst and a phosphorus-based compound are present in a poly-L-lactic acid (A) and a poly-D-lactic acid (B), by using a specific proportion of an organic acid metal salt or an organic metal salt for stereocomplex crystallization, a stereocomplex polylactic acid composition having a high stereocomplex crystallinity and a high stereocomplex crystal melting point, a small stereocomplex crystal melting point depression even after remelting, a small decrease in the molecular weight, excellent forming processability, and also heat resistance can be provided.

Abstract: A thermosetting resin composition which produces no free isocyanate even when a carbodiimide compound is used and provides a cured resin having high heat resistance. The thermosetting resin composition makes it possible to reduce the curing temperature, cures in a short time and provides a cured rein having a high glass transition temperature. The thermosetting resin composition includes: (A) an epoxy resin (component A); and (B) a cyclic carbodiimide compound (component B) including a cyclic structure having one carbodiimide group in which first nitrogen and second nitrogen are bonded together by a bond group and having 8 to 50 atoms forming the cyclic structure and/or (b) a polyvalent amine-based curing agent (component b).

Abstract: A thermosetting resin composition which produces no free isocyanate even when a carbodiimide compound is used and provides a cured resin having high heat resistance. The thermosetting resin composition makes it possible to reduce the curing temperature, cures in a short time and provides a cured rein having a high glass transition temperature.

Abstract: A thermosetting resin composition which produces no free isocyanate even when a carbodiimide compound is used and provides a cured resin having high heat resistance. The thermosetting resin composition makes it possible to reduce the curing temperature, cures in a short time and provides a cured rein having a high glass transition temperature.

Abstract: Even when a tin-based polymerization catalyst and a phosphorus-based compound are present in a poly-L-lactic acid (A) and a poly-D-lactic acid (B), by using a specific proportion of an organic acid metal salt or an organic metal salt for stereocomplex crystallization, a stereocomplex polylactic acid composition having a high stereocomplex crystallinity and a high stereocomplex crystal melting point, a small stereocomplex crystal melting point depression even after remelting, a small decrease in the molecular weight, excellent forming processability, and also heat resistance can be provided.

Abstract: Provided are a resin composition controlled such that after keeping a shape thereof under a severe environment as in high-temperature hot water or in hot water under chemically severe condition, such as an acidic or basic condition, etc., for a fixed period of time, it is quickly decomposed; and a structure thereof.