Abstract: It is provided that a multifilament and a braid that are capable of being processed into products in a wide range of temperature and are excellent in dimensional stability and abrasion resistance. A multifilament comprising 5 or more monofilaments and a braid comprising the multifilament, wherein the multifilament contains polyethylene having an intrinsic viscosity [?] of 5.0 dL/g or more and 40.0 dL/g or less and substantially including ethylene as a repeating unit, the monofilament has a titer of 3 dtex or more and 40 dtex or less, the multifilament has a thermal shrinkage of 0.20% or less at 70° C. and a thermal shrinkage of 3.0% or less at 120° C., and a stress Raman shift factor under the condition of applying a load that is 10% of a breaking load to the monofilament is 5.0 cm?1 or less.

Abstract: It is provided that a multifilament and a braid that are capable of being processed into products in a wide range of temperature and are excellent in dimensional stability and abrasion resistance. A multifilament comprising 5 or more monofilaments, wherein the multifilament contains polyethylene having an intrinsic viscosity [?] of 5.0 dL/g or more and 40.0 dL/g or less and substantially including ethylene as a repeating unit, and shows 1000 times or more in number of reciprocating abrasions at break in an abrasion resistance test measured at a load of 5 cN/dtex in accordance with JIS L-1095.

Abstract: It is provided that a multifilament and a braid that are capable of being processed into products in a wide range of temperature and are excellent in dimensional stability and abrasion resistance. A multifilament comprising 5 or more monofilaments and a braid comprising the multifilament, wherein the multifilament contains polyethylene having an intrinsic viscosity [?] of 5.0 dL/g or more and 40.0 dL/g or less and substantially including ethylene as a repeating unit, the monofilament has a titer of 3 dtex or more and 40 dtex or less, the multifilament has a thermal shrinkage of 0.20% or less at 70° C. and a thermal shrinkage of 3.0% or less at 120° C., and a stress Raman shift factor under the condition of applying a load that is 10% of a breaking load to the monofilament is 5.0 cm?1 or less.

Abstract: It is provided that a multifilament and a braid that are capable of being processed into products in a wide range of temperature and are excellent in dimensional stability and abrasion resistance. A multifilament comprising 5 or more monofilaments, wherein the multifilament contains polyethylene having an intrinsic viscosity [?] of 5.0 dL/g or more and 40.0 dL/g or less and substantially including ethylene as a repeating unit, and wherein a difference between a maximum value and a minimum value in a ratio of a diffraction peak intensity of orthorhombic crystal (200) plane to a diffraction peak intensity of orthorhombic crystal (110) plane in a monofilament cross section is 0.22 or less.

Abstract: It is provided that a multifilament and a braid that are capable of being processed into products in a wide range of temperature and are excellent in dimensional stability and abrasion resistance. A multifilament comprising 5 or more monofilaments, wherein the multifilament contains polyethylene having an intrinsic viscosity [?] of 5.0 dL/g or more and 40.0 dL/g or less and substantially including ethylene as a repeating unit, and shows 1000 times or more in number of reciprocating abrasions at break in an abrasion resistance test measured at a load of 5 cN/dtex in accordance with JIS L-1095.

Abstract: It is provided that a multifilament and a braid that are capable of being processed into products in a wide range of temperature and are excellent in dimensional stability and abrasion resistance. A multifilament comprising 5 or more monofilaments, wherein the multifilament contains polyethylene having an intrinsic viscosity [?] of 5.0 dL/g or more and 40.0 dL/g or less and substantially including ethylene as a repeating unit, and wherein a difference between a maximum value and a minimum value in a ratio of a diffraction peak intensity of orthorhombic crystal (200) plane to a diffraction peak intensity of orthorhombic crystal (110) plane in a monofilament cross section is 0.22 or less.

Abstract: An image projected onto a screen from a projector is generated as follows. Specifically, two virtual viewpoints that correspond to the right eye and the left eye of a viewer are set in a virtual three-dimensional space, and two virtual planes are set to be circumscribed to the screen (plane of projection). A plane image is generated by perspective projection transformation of a game space onto the virtual plane based on each virtual viewpoint. A projection image is generated from each plane image according to the relationship between the pixel position of the virtual plane and the pixel position of the projection image that is defined so that the plane image is observed without distortion when observing the screen from a presumed viewing position to generate a right-eye projection image and a left-eye projection image.