Abstract: Disclosed is a method which can readily design an agricultural chemical-containing resin composition having a desired release rate history and can produce the agricultural chemical-containing resin composition. Specifically disclosed is a method for producing an agricultural chemical-containing resin composition, including: respectively selecting an acetamiprid content AcSA and a hydrophilic white carbon content CaSA in the composition relative to the total mass of acetamiprid, a styrene-maleic anhydride copolymer or a styrene-maleic anhydride copolymer-mixed resin, and hydrophilic white carbon, so as to satisfy the inequations of: 0.524×AcSA+1.422×CaSA?6.009?40% by mass, 5% by mass?AcSA?35% by mass, and CaSA?0.1% by mass; and mixing the acetamiprid, the styrene-maleic anhydride copolymer or the styrene-maleic anhydride copolymer-mixed resin, and the hydrophilic white carbon, so that the thus selected contents AcSA and CaSA can be achieved.

Abstract: Disclosed is a method which can readily design an agricultural chemical-containing resin composition having a desired release rate history and can produce the agricultural chemical-containing resin composition. Specifically disclosed is a method for producing an agricultural chemical-containing resin composition, including: respectively selecting an acetamiprid content AcSA and a hydrophilic white carbon content CaSA in the composition relative to the total mass of acetamiprid, a styrene-maleic anhydride copolymer or a styrene-maleic anhydride copolymer-mixed resin, and hydrophilic white carbon, so as to satisfy the inequations of: 0.524×AcSA+1.422×CaSA?6.009?40% by mass, 5% by mass?AcSA?35% by mass, and CaSA?0.1% by mass; and mixing the acetamiprid, the styrene-maleic anhydride copolymer or the styrene-maleic anhydride copolymer-mixed resin, and the hydrophilic white carbon, so that the thus selected contents AcSA and CaSA can be achieved.

Abstract: Disclosed is a method which can readily design an agricultural chemical-containing resin composition having a desired release rate history and can produce the agricultural chemical-containing resin composition. Specifically disclosed is a method for producing an agricultural chemical-containing resin composition, including: respectively selecting an acetamiprid content AcSA and a hydrophilic white carbon content CaSA in the composition relative to the total mass of acetamiprid, a styrene-maleic anhydride copolymer or a styrene-maleic anhydride copolymer-mixed resin, and hydrophilic white carbon, so as to satisfy the inequations of: 0.524×AcSA+1.422×CaSA?6.009?40% by mass, 5% by mass?AcSA?35% by mass, and CaSA?0.1% by mass; and mixing the acetamiprid, the styrene-maleic anhydride copolymer or the styrene-maleic anhydride copolymer-mixed resin, and the hydrophilic white carbon, so that the thus selected contents AcSA and CaSA can be achieved.

Abstract: Disclosed is a method which can readily design an agricultural chemical-containing resin composition having a desired release rate history and can produce the agricultural chemical-containing resin composition. Specifically disclosed is a method for producing an agricultural chemical-containing resin composition, including: respectively selecting an acetamiprid content AcSA and a hydrophilic white carbon content CaSA in the composition relative to the total mass of acetamiprid, a styrene-maleic anhydride copolymer or a styrene-maleic anhydride copolymer-mixed resin, and hydrophilic white carbon, so as to satisfy the inequations of: 0.524×AcSA+1.422×CaSA?6.009?40% by mass, 5% by mass?AcSA?35% by mass, and CaSA?0.1% by mass; and mixing the acetamiprid, the styrene-maleic anhydride copolymer or the styrene-maleic anhydride copolymer-mixed resin, and the hydrophilic white carbon, so that the thus selected contents AcSA and CaSA can be achieved.

Abstract: A high-strength austenitic steel having a fully austenite structure and consisting essentially of 0.02 to 0.15 wt % of C, not greater than 1.5 wt % of Si, not greater than 2.5 wt % of Mn, 8 to 20 wt % of Ni, 13 to 25 wt % of Cr, 0.02 to 0.25 wt % of Al, not greater than 0.1 wt % of N, at least one of 0.001 to 0.01 wt % of B, 0.02 to 0.5 wt % of Nb, 0.01 to 0.2 wt % of Ti and 0.02 to 0.6 wt % of V and the balance substantialy Fe, with the weight ratio (Al/N) ranging between 1 and 4.5. This steel is suitable for use as the material of, for example, inner casing of steam turbine, valve body incorporated in the steam turbine, rotor shaft, and chemical equipment such as reaction pipe and vessel for styrene monomer producing facility.

Abstract: A boiler tube having a double-tube structure constituted by an inner tube and an outer tube integrated with each other. The inner tube is made of an alloy consisting essentially of, by weight, 0.02 to 0.15% of C, 0.5 to 3.5% of Si, not greater than 2% of Mn, 25 to 40% of Ni, 20.5 to 27% of Cr, 0.5 to 3% of Mo, not greater than 1% of Nb and the balance Fe and having a substantially fully austenite structure. The outer tube is made of an alloy consisting essentially of, by weight, 0.02 to 0.2% of C, not greater than 3.5% of Si, not greater than 2% of Mn, 33 to 45% of Ni, 30 to 40% of Cr and the balance Fe and having a substantially fully austenite structure. The inner tube made of the alloy having the composition specified above exhibits a high resistance to steam oxidation without any reduction in high-temperature strength even at elevated steam temperature, while the outer tube made of the alloy having the composition specified above exhibits a superior resistance to corrosion by coal combustion gas.

Abstract: A heat-resistant and corrosion-resistant weld metal alloy consisting essentially of, by weight, less than 0.08% of C, 0.1 to 1.0% of Si, 2 to 3% of Mn, 32 to 42% of Ni, 21 to 25% of Cr, 0.8 to 1.7% of Mo, 0.1 to 1.0% of Nb, up to 0.5% of Ti, up to 2% of Co, up to 2% of Cu, up to 1% of W, up to 0.2% of N, up to 1.0% of V, up to 1.0% of Zr, up to 1.0% of Ta and the balance Fe, wherein the following conditions are met: Ti+Zr.ltoreq.1.0%, Ni+Co.ltoreq.42%, W+V.ltoreq.1.0%, Nb+Ta.ltoreq.1.0%, and 4.ltoreq.Nb/C.ltoreq.15; and an austenitic welded structure composed of an austenitic structural alloy and of a weld metal of the above-mentioned kind are provided by the invention.