Abstract: A catalyst for the selective catalytic reduction of NOx comprises a zeolitic material which comprises (A) one or more zeolites having a GME framework structure containing YO2 and X2O3, and optionally further comprises one or more zeolites having a CHA framework structure containing YO2 and X2O3, and/or comprises, (B) one or more zeolite intergrowth phases of one or more zeolites having a GME framework structure containing YO2 and X2O3 and one or more zeolites having a CHA framework structure containing YO2 and X2O3, wherein Y is a tetravalent element, and X is a trivalent element, and the zeolitic material contains Cu and/or Fe as non-framework elements in an amount ranging from 0.1 to 15 wt. % calculated as the element and based on 100 wt. % of YO contained in the zeolitic material. Also provided are a process for its preparation, and a use in a method for the selective catalytic reduction of NOx.

Abstract: The present invention relates to a process for the preparation of a catalyst for selective catalytic reduction comprising • (i) preparing a mixture comprising a metal-organic framework material comprising an ion of a metal or metalloid selected from groups 2-5, groups 7-9, and groups 11-14 of the Periodic Table of the Elements, and at least one at least monodentate organic compound, a zeolitic material containing a metal as a non-framework element, optionally a solvent system, and optionally a pasting agent, • (ii) calcining of the mixture obtained in (i); and further relates to a catalyst per se comprising a composite material containing an amorphous mesoporous metal and/or metalloid oxide and a zeolitic material, wherein the zeolitic material contains a metal as non-framework element, as well as to the use of said catalyst.

Abstract: The present invention relates to a process for the production of a transition metal containing zeolite comprising expanding a layered silicate with a swelling agent and introducing the transition metal into the interlayer expanded silicate prior to calcination thereof for obtaining the transition metal containing zeolite. The present invention further relates to a zeolite containing transition metal nanoparticles as obtainable or obtained according to the inventive process, as well as to a zeolite containing nanoparticles per se. Finally the present invention relates to the use of a zeolite containing transition metal nanoparticles as obtainable or obtained according to the inventive process, as well as to the use of a zeolite containing nanoparticles per se.

Abstract: A zeolitic material having framework type CHA, comprising a transition metal M and an alkali metal A, and having a framework structure comprising a tetravalent element Y, a trivalent element X and O, wherein the transition metal M is a transition I metal of groups 7 to 12 of the periodic table, A is one or more of K and Cs, Y is one or more of Si, Ge, Ti, Sn and Zr, and X is one or more of Al, B, Ga and In. A process for preparing such a zeolitic material. Use of such a zeolitic material.

Abstract: Provided is a crystalline layered silicate, having an X-ray diffraction pattern comprising reflections at 2-theta values of (5.3±0.2)°, (8.6±0.2)°, (9.8±0.2)°, (21.7±0.2)° and (22.7±0.2). Also provided are a process for preparing the crystalline layered silicate and uses of the layered silicate. The process comprises steps of: (i) preparing a synthesis mixture comprising water, a source of Si, and a structure directing agent comprising a diethyldimethylammonium compound; (ii) subjecting the synthesis mixture obtained from (i) to hydrothermal synthesis conditions comprising heating the synthesis mixture obtained from (i) to a temperature in the range of from 110 to 180° C. and keeping the synthesis mixture at a temperature in this range under autogenous pressure for 1 to 6 days, obtaining a mother liquor comprising the crystalline layered silicate.

Abstract: A process for preparing a zeolitic material comprising Ti, having framework type CHA and having a framework structure which comprises Si and O, said process comprising (i) preparing a pre-synthesis mixture comprising water, a CHA framework structure directing agent, and a zeolitic material comprising Ti, having framework type MFI and having a framework structure which comprises Si and O; (ii) removing water from the pre-synthesis mixture obtained from (i) by heating the pre-synthesis mixture to a temperature of less than 100° C. at a pressure of less than 1 bar (abs); (iii) hydrothermally crystallizing the zeolitic material comprising Ti, having framework type CHA and having a framework structure which comprises Si and O.

Abstract: The present invention relates to a process for the preparation of a zeolitic material having a CHA-type framework structure comprising YO2 and X2O3, wherein said process comprises the steps of: (1) providing a mixture comprising one or more sources for YO2, one or more sources for X2O3, one or more optionally substituted ethyltrimethylammonium cation-containing compounds, and one or more tetraalkylammonium cation R1R2R3R4N+-containing compounds as structure directing agent; (2) crystallizing the mixture obtained in step (1) for obtaining a zeolitic material having a CHA-type framework structure; wherein Y is a tetravalent element and X is a trivalent element, wherein R1, R2, and R3 independently from one another stand for alkyl, wherein R4 stands for cycloalkyl, and wherein the YO2:X2O3 molar ratio of the mixture in (1) ranges from 2 to 1,000, as well as to zeolitic materials which may be obtained according to the inventive process and to their use.

Abstract: A process for preparing a zeolitic material containing YO2 and X2O3, where Y and X represent a tetravalent element and a trivalent element, respectively, is described. The process includes (1) a step of preparing a mixture containing one or more structure directing agents, seed crystals, and a first zeolitic material containing YO2 and X2O3 and having FAU-, GIS-, MOR-, and/or LTA-type framework structures; and (2) a step of heating the mixture for obtaining a second zeolitic material containing YO2 and X2O3 and having a different framework structure than the first zeolitic material. The mixture prepared in (1) and heated in (2) contains 1000 wt % or less of H2O based on 100 wt % of YO2 in the framework structure of the first zeolitic material. A zeolitic material obtainable and/or obtained by the process and its use are also described.

Abstract: Provided are a process for the preparation of an iron containing zeolitic material having an AEI framework structure using a quaternary phosphonium cation, as well as an iron containing zeolitic material per se as obtainable or obtained according to the process. Furthermore, an exhaust gas treatment system comprising the iron containing zeolitic material and the use of the iron containing zeolitic material as a catalyst are provided.

Abstract: A zeolitic material having framework type CHA, comprising a transition metal M and an alkali metal A, and having a framework structure comprising a tetravalent element Y, a trivalent element X and 0, wherein the transition metal M is a transition metal of groups 7 to 12 of the periodic table, A is one or more of K and Cs, Y is one or more of Si, Ge, Ti, Sn and Zr, and X is one or more of Al, B, Ga and In. A process for preparing such a zeolitic material. Use of such a zeolitic material.

Abstract: A composition comprising a support material which comprises silicon carbide on the surface of which a zeolitic material of the AEI/CHA family is supported, wherein at least 99 weight-% of the framework structure of the zeolitic material consist of a tetravalent element Y which is one or more of Si, Ge, Ti, Sn and V; a trivalent element X which is one or more of Al, Ga, In, and B; O; and H.

Abstract: The present invention relates to a process for the production of a zeolitic material having a BEA-type framework structure comprising YO2 and X2O3, wherein said process comprises the steps of (1) preparing a mixture comprising one or more sources for YO2 and one or more sources for X2O3; (2) crystallizing the mixture obtained in step (1); (3) subjecting the zeolitic material having a BEA-type framework structure obtained in step (2) to an ion-exchange procedure with Cu; and (4) subjecting the Cu ion-exchanged zeolitic material obtained in step (3) to an ion-exchange procedure with Fe; wherein Y is a tetravalent element, and X is a trivalent element, wherein the mixture provided in step (1) and crystallized in step (2) further comprises seed crystals comprising one or more zeolitic materials having a BEA-type framework structure, and wherein the mixture provided in step (1) and crystallized in step (2) does not contain an organotemplate as a structure-directing agent, as well as to the zeolitic material having

Abstract: The present invention relates to a method for the preparation of a treated zeolitic material having a BEA framework structure including the steps of: (i) providing a zeolitic material having a BEA framework structure, wherein the BEA framework structure includes YO2 and X2O3, wherein Y is a tetravalent element, and X is a trivalent element, and wherein the zeolitic material having a BEA framework structure is obtainable and/or obtained from an organotemplate-free synthetic process; (ii) calcining the zeolitic material provided in step (i) at a temperature of 650° C. or more; and (iii) treating the calcined zeolitic material obtained from step (ii) with an aqueous solution having a pH of 5 or less, as well as to zeolitic materials per se preferably obtainable according to the inventive method and to their use, and to a process for converting oxygenates to olefins employing the inventive zeolitic materials.

Abstract: A process for preparing a zeolitic material containing YO2 and X2O3, where Y and X represent a tetravalent element and a trivalent element, respectively, is described. The process includes (1) a step of preparing a mixture containing one or more structure directing agents, seed crystals, and a first zeolitic material containing YO2 and X2O3 and having FAU-, GIS-, MOR-, and/or LTA-type framework structures; and (2) a step of heating the mixture for obtaining a second zeolitic material containing YO2 and X2O3 and having a different framework structure than the first zeolitic material. The mixture prepared in (1) and heated in (2) contains 1000 wt % or less of H2O based on 100 wt % of YO2 in the framework structure of the first zeolitic material. A zeolitic material obtainable and/or obtained by the process and its use are also described.

Abstract: The present invention relates to a process for the preparation of a zeolitic material having a CHA-type framework structure comprising YO2 and X2O3, wherein said process comprises the steps of: (1) providing a mixture comprising one or more sources for YO2, one or more sources for X2O3, one or more tetraalkylammonium cation R1R2R3R4N+-containing compounds, and one or more tetraalkylammonium cation R5R6R7R8N+-containing compounds as structure directing agent; (2) crystallizing the mixture obtained in step (1) for obtaining a zeolitic material having a CHA-type framework structure; wherein Y is a tetravalent element and X is a trivalent element, wherein R1, R2, R3, R4, R5, R6, and R7 independently from one another stand for alkyl, and wherein R8 stands for cycloalkyl, as well as to zeolitic materials which may be obtained according to the inventive process and to their use.

Abstract: The present invention relates to a process for the preparation of a catalyst for selective catalytic reduction comprising• (i) preparing a mixture comprising a metal-organic framework material comprising an ion of a metal or metalloid selected from groups 2-5, groups 7-9, and groups 11-14 of the Periodic Table of the Elements, and at least one at least monodentate organic compound, a zeolitic material containing a metal as a non-framework element, optionally a solvent system, and optionally a pasting agent,• (ii) calcining of the mixture obtained in (i); and further relates to a catalyst per se comprising a composite material containing an amorphous mesoporous metal and/or metalloid oxide and a zeolitic material, wherein the zeolitic material contains a metal as non-framework element, as well as to the use of said catalyst.

Abstract: A catalyst for the selective catalytic reduction of NOx comprises a zeolitic material which comprises (A) one or more zeolites having a GME framework structure containing YO2 and X2O3, and optionally further comprises one or more zeolites having a CHA framework structure containing YO2 and X2O3, and/or comprises, (B) one or more zeolite intergrowth phases of one or more zeolites having a GME framework structure containing YO2 and X2O3 and one or more zeolites having a CHA framework structure containing YO2 and X2O3, wherein Y is a tetravalent element, and X is a trivalent element, and the zeolitic material contains Cu and/or Fe as non-framework elements in an amount ranging from 0.1 to 15 wt. % calculated as the element and based on 100 wt. % of YO contained in the zeolitic material. Also provided are a process for its preparation, and a use in a method for the selective catalytic reduction of NOx.

Abstract: The present invention relates to a process for the preparation of a zeolitic material comprising the steps of: (1) providing a mixture comprising one or more sources for YO2 and one or more alkenyltrialkylammonium cation R1R2R3R4N+-containing compounds as structure directing agent; and (2) crystallizing the mixture obtained in step (1) to obtain a zeolitic material; wherein Y is a tetravalent element, and wherein R1, R2, and R3 independently from one another stand for alkyl; and R4 stands for alkenyl, as well as to zeolitic materials which may be obtained according to the inventive process and to their use.

Abstract: The present invention relates to a catalyst for the conversion of oxygenates to olefins, wherein the catalyst comprises one or more zeolites of the MFI, MEL and/or MWW structure type and particles of one or more metal oxides, the one or more zeolites of the MFI, MEL and/or MWW structure type comprising one or more alkaline earth metals selected from the group consisting of Mg, Ca, Sr, Ba and combinations of two or more thereof, wherein the catalyst displays a water uptake of 9.0 wt.-% or less, as well as to a process for the production thereof and to its use, in particular in a process for converting oxygenates to olefins.

Abstract: The present invention relates to a process for the preparation of a zeolitic material having a CHA-type framework structure comprising YO2 and X2O3, wherein said process comprises the steps of: (1) providing a mixture comprising one or more sources for YO2, one or more sources for X2O3, one or more optionally substituted ethyltrimethylammonium cation-containing compounds, and one or more tetraalkylammonium cation R1R2R3R4N+-containing compounds as structure directing agent; (2) crystallizing the mixture obtained in step (1) for obtaining a zeolitic material having a CHA-type framework structure; wherein Y is a tetravalent element and X is a trivalent element, wherein R1, R2, and R3 independently from one another stand for alkyl, wherein R4 stands for cycloalkyl, and wherein the YO2:X2O3 molar ratio of the mixture in (1) ranges from 2 to 1,000, as well as to zeolitic materials which may be obtained according to the inventive process and to their use.