Abstract: A method of making a reflective coated glass article includes providing a glass substrate. A first gaseous mixture is formed. The first gaseous mixture includes a silane compound and inert gas. The first gaseous mixture is delivered to a location above a major surface of the glass substrate to deposit a first coating layer directly on the major surface of the glass substrate. The first coating layer is deposited at a thickness of 5-50 nm. A second gaseous mixture is formed. The second gaseous mixture includes a silane compound, a radical scavenger and molecular oxygen. The second gaseous mixture is delivered to a location above the first coating layer. A second coating layer is deposited at a thickness of 5-50 nm over the first coating layer. The coated glass article exhibits a total visible light reflectance (Illuminant D65, ten degree observer) of 45% or more from a coated side of the coated glass article.

Abstract: A coated glass article includes a glass substrate and an anti-reflective coating formed over a first major surface of the glass substrate. The anti-reflective coating includes a color suppression interlayer and a first coating layer deposited over the color suppression interlayer. The first coating layer includes tin oxide and a dopant. The dopant includes antimony, molybdenum, or iron. A second coating layer is deposited over the first coating layer. The second coating layer includes an oxide of silicon. The coated glass article exhibits a total visible light transmittance of 70% or more and a film side visible light reflectance of less than 6.0%.

Abstract: A method of making a reflective coated glass article includes providing a glass substrate. A first gaseous mixture is formed. The first gaseous mixture includes a silane compound and inert gas. The first gaseous mixture is delivered to a location above a major surface of the glass substrate to deposit a first coating layer directly on the major surface of the glass substrate. The first coating layer is deposited at a thickness of 5-50 nm. A second gaseous mixture is formed. The second gaseous mixture includes a silane compound, a radical scavenger and molecular oxygen. The second gaseous mixture is delivered to a location above the first coating layer. A second coating layer is deposited at a thickness of 5-50 nm over the first coating layer. The coated glass article exhibits a total visible light reflectance (Illuminant D65, ten degree observer) of 45% or more from a coated side of the coated glass article.

Abstract: A coated glass article includes a glass substrate and an anti-reflective coating formed over a first major surface of the glass substrate. The anti-reflective coating includes a color suppression interlayer and a first coating layer deposited over the color suppression interlayer. The first coating layer includes tin oxide and a dopant. The dopant includes antimony, molybdenum, or iron. A second coating layer is deposited over the first coating layer. The second coating layer includes an oxide of silicon. The coated glass article exhibits a total visible light transmittance of 70% or more and a film side visible light reflectance of less than 6.0%.