Abstract: A polymer suitable for use in a thin film hinge (living hinge) comprising from about 0.1 to about 5 weight % of a C4-8 comonomer and the balance ethylene, said composition having a density as determined according to ASTM D 792 from about 0.945 to about 0.965 g/cm3; a melt index as determined according to ASTM D1238 (2.16 kg/190° C.) from about 10 to about 20 g/10 min; a weight average molecular weight (Mw) from about 45,000 to about 55,000 g/mol; a polydispersity from about 2.5 to about 3.1 and when molded into a strip having a length of about 13 cm and gross thickness from about 50 to about 70 mil (about 1 to about 2 mm) and completely bent over end to end four times to create a thinned region or crease having a thickness from about 15 to about 30 mil (about 0.3 to about 0.7 mm) tested by bending and releasing the deformed thinned region of the strip through a radius of curvature from about 180 to about 190° about a rounded plate goes through not less than 500 cycles without breaking.

Abstract: A polymer suitable for use in a thin film hinge (living hinge) comprising from about 0.1 to about 5 weight % of a C4-8 comonomer and the balance ethylene, said composition having a density as determined according to ASTM D 792 from about 0.945 to about 0.965 g/cm3; a melt index as determined according to ASTM D1238 (2.16 kg/190° C.) from about 10 to about 20 g/10 min; a weight average molecular weight (Mw) from about 45,000 to about 55,000 g/mol; a polydispersity from about 2.5 to about 3.1 and when molded into a strip having a length of about 13 cm and gross thickness from about 50 to about 70 mil (about 1 to about 2 mm) and completely bent over end to end four times to create a thinned region or crease having a thickness from about 15 to about 30 mil (about 0.3 to about 0.7 mm) tested by bending and releasing the deformed thinned region of the strip through a radius of curvature from about 180 to about 190° about a rounded plate goes through not less than 500 cycles without breaking.

Abstract: A polymer suitable for use in a thin film hinge (living hinge) comprising from about 0.1 to about 5 weight % of a C4-8 comonomer and the balance ethylene, said composition having a density as determined according to ASTM D 792 from about 0.945 to about 0.965 g/cm3; a melt index as determined according to ASTM D1238 (2.16 kg/190° C.) from about 10 to about 20 g/10 min; a weight average molecular weight (Mw) from about 45,000 to about 55,000 g/mol; a polydispersity from about 2.5 to about 3.1 and when molded into a strip having a length of about 13 cm and gross thickness from about 50 to about 70 mil (about 1 to about 2 mm) and completely bent over end to end four times to create a thinned region or crease having a thickness from about 15 to about 30 mil (about 0.3 to about 0.7 mm) tested by bending and releasing the deformed thinned region of the strip through a radius of curvature from about 180 to about 190° about a rounded plate goes through not less than 500 cycles without breaking.

Abstract: A polymer suitable for use in a thin film hinge (living hinge) comprising from about 0.1 to about 5 weight % of a C4-8 comonomer and the balance ethylene, said composition having a density as determined according to ASTM D 792 from about 0.945 to about 0.965 g/cm3; a melt index as determined according to ASTM D1238 (2.16 kg/190° C.) from about 10 to about 20 g/10 min; a weight average molecular weight (Mw) from about 45,000 to about 55,000 g/mol; a polydispersity from about 2.5 to about 3.1 and when molded into a strip having a length of about 13 cm and gross thickness from about 50 to about 70 mil (about 1 to about 2 mm) and completely bent over end to end four times to create a thinned region or crease having a thickness from about 15 to about 30 mil (about 0.3 to about 0.7 mm) tested by bending and releasing the deformed thinned region of the strip through a radius of curvature from about 180 to about 190° about a rounded plate goes through not less than 500 cycles without breaking.

Abstract: A polymer suitable for use in a thin film hinge (living hinge) comprising from about 0.1 to about 5 weight % of a C4-8 comonomer and the balance ethylene, said composition having a density as determined according to ASTM D 792 from about 0.945 to about 0.965 g/cm3; a melt index as determined according to ASTM D1238 (2.16 kg/190° C.) from about 10 to about 20 g/10 min; a weight average molecular weight (Mw) from about 45,000 to about 55,000 g/mol; a polydispersity from about 2.5 to about 3.1 and when molded into a strip having a length of about 13 cm and gross thickness from about 50 to about 70 mil (about 1 to about 2 mm) and completely bent over end to end four times to create a thinned region or crease having a thickness from about 15 to about 30 mil (about 0.3 to about 0.7 mm) tested by bending and releasing the deformed thinned region of the strip through a radius of curvature from about 180 to about 190° about a rounded plate goes through not less than 500 cycles without breaking.

Abstract: A polymer suitable for use in a thin film hinge (living hinge) comprising from about 0.1 to about 5 weight % of a C4-8 comonomer and the balance ethylene, said composition having a density as determined according to ASTM D 792 from about 0.945 to about 0.965 g/cm3; a melt index as determined according to ASTM D1238 (2.16 kg/190° C.) from about 10 to about 20 g/10 min; a weight average molecular weight (Mw) from about 45,000 to about 55,000 g/mol; a polydispersity from about 2.5 to about 3.1 and when molded into a strip having a length of about 13 cm and gross thickness from about 50 to about 70 mil (about 1 to about 2 mm) and completely bent over end to end four times to create a thinned region or crease having a thickness from about 15 to about 30 mil (about 0.3 to about 0.7 mm) tested by bending and releasing the deformed thinned region of the strip through a radius of curvature from about 180 to about 190° about a rounded plate goes through not less than 500 cycles without breaking.

Abstract: A polymer suitable for use in a thin film hinge (living hinge) comprising from about 0.1 to about 5 weight % of a C4-8 comonomer and the balance ethylene, said composition having a density as determined according to ASTM D 792 from about 0.945 to about 0.965 g/cm3; a melt index as determined according to ASTM D1238 (2.16 kg/190° C.) from about 10 to about 20 g/10 min; a weight average molecular weight (Mw) from about 45,000 to about 55,000 g/mol; a polydispersity from about 2.5 to about 3.1 and when molded into a strip having a length of about 13 cm and gross thickness from about 50 to about 70 mil (about 1 to about 2 mm) and completely bent over end to end four times to create a thinned region or crease having a thickness from about 15 to about 30 mil (about 0.3 to about 0.7 mm) tested by bending and releasing the deformed thinned region of the strip through a radius of curvature from about 180 to about 190° about a rounded plate goes through not less than 500 cycles without breaking.

Abstract: A polymer suitable for use in a thin film hinge (living hinge) comprising from about 0.1 to about 5 weight % of a C4-8 comonomer and the balance ethylene, said composition having a density as determined according to ASTM D 792 from about 0.945 to about 0.965 g/cm3; a melt index as determined according to ASTM D1238 (2.16 kg/190° C.) from about 10 to about 20 g/10 min; a weight average molecular weight (Mw) from about 45,000 to about 55,000 g/mol; a polydispersity from about 2.5 to about 3.1 and when molded into a strip having a length of about 13 cm and gross thickness from about 50 to about 70 mil (about 1 to about 2 mm) and completely bent over end to end four times to create a thinned region or crease having a thickness from about 15 to about 30 mil (about 0.3 to about 0.7 mm) tested by bending and releasing the deformed thinned region of the strip through a radius of curvature from about 180 to about 190° about a rounded plate goes through not less than 500 cycles without breaking.

Abstract: A dual reactor solution polymerization process gives high density polyethylene compositions containing a first ethylene copolymer and a second ethylene copolymer and which have high dimensional stability, excellent processability as well as good organoleptic properties and reasonable stress cracking resistance. The polyethylene compositions are suitable for compression molding or injection molding applications and are useful, for example, in the manufacture of caps and closures for bottles, and for example, in bottles containing non-pressurized liquids.

Abstract: A plastic may be selected for a thin web application by finite element analysis of the part including the properties, including Poission's ratio of potential polymers from which the part may be made and subjecting the computer model of the part to loads to determine the deflection of the part under a specified series of loads or when the part breaks or subjecting the part to a number of use cycles to determine when the part fails. The process is iteratively repeated for each plastic and the results are compared to select a preferred plastic for the part.

Abstract: A polymer suitable for use in a thin film hinge (living hinge) comprising from about 0.1 to about 5 weight % of a C4-8 comonomer and the balance ethylene, said composition having a density as determined according to ASTM D 792 from about 0.945 to about 0.965 g/cm3; a melt index as determined according to ASTM D1238 (2.16 kg/190° C.) from about 10 to about 20 g/10 min; a weight average molecular weight (Mw) from about 45,000 to about 55,000 g/mol; a polydispersity from about 2.5 to about 3.1 and when molded into a strip having a length of about 13 cm and gross thickness from about 50 to about 70 mil (about 1 to about 2 mm) and completely bent over end to end four times to create a thinned region or crease having a thickness from about 15 to about 30 mil (about 0.3 to about 0.7 mm) tested by bending and releasing the deformed thinned region of the strip through a radius of curvature from about 180 to about 190° about a rounded plate goes through not less than 500 cycles without breaking.

Abstract: A dual reactor solution polymerization process gives high density polyethylene compositions containing a first ethylene copolymer and a second ethylene copolymer and which have high dimensional stability, excellent processability as well as good organoleptic properties and reasonable stress cracking resistance. The polyethylene compositions are suitable for compression molding or injection molding applications and are useful, for example, in the manufacture of caps and closures for bottles, and for example, in bottles containing non-pressurized liquids.

Abstract: A plastic may be selected for a thin web application by finite element analysis of the part including the properties, including Poission's ratio of potential polymers from which the part may be made and subjecting the computer model of the part to loads to determine the deflection of the part under a specified series of loads or when the part breaks or subjecting the part to a number of use cycles to determine when the part fails. The process is iteratively repeated for each plastic and the results are compared to select a preferred plastic for the part.