Abstract: Process for the manufacture of a material on the basis of calcium- and/or magnesium carbonate having a reduced decrepitation tendency, wherein a material on the basis of calcium- and/or magnesium carbonate is treated with at least one additive selected among alkali metal compounds and/or acids and/or alkaline earth metal compounds in an amount of 0.05 to 5 wt. % based on the amount of the material on the basis of calcium- and/or magnesium carbonate. Also claimed are the material obtainable by the process and showing reduced decrepitation tendency and the use of such material in the manufacture of glass.

Abstract: Process for the manufacture of a material on the basis of calcium- and/or magnesium carbonate having a reduced decrepitation tendency, wherein a material on the basis of calcium- and/or magnesium carbonate is treated with at least one additive selected among alkali metal compounds and/or acids and/or alkaline earth metal compounds in an amount of 0.05 to 5 wt. % based on the amount of the material on the basis of calcium- and/or magnesium carbonate. Also claimed are the material obtainable by the process and showing reduced decripitation tendency and the use of such material in the manufacture of glass.

Abstract: Process for the manufacture of a material on the basis of calcium- and/or magnesium carbonate having a reduced decrepitation tendency, wherein a material on the basis of calcium- and/or magnesium carbonate is treated with at least one additive selected among alkali metal compounds and/or acids and/or alkaline earth metal compounds in an amount of 0.05 to 5 wt. % based on the amount of the material on the basis of calcium- and/or magnesium carbonate. Also claimed are the material obtainable by the process and showing reduced decripitation tendancy and the use of such material in the manufacture of glass.

Abstract: In order to also be able to economically use iron ore dust which is created by the extraction and preparation of iron ore and has not been usable until now, the invention proposes an agglomerated stone comprising (in wt. %) 6-15% of a cement binding agent, up to 20% of a carbon carrier, up to 20% of residual and recyclable substances, optionally up to 10% of a coagulation and solidification accelerator and the remainder consisting of iron ore in a stone format in the form of particles having a particle size of less than 3 mm as well as possessing after three days an initial strength of at least 5 N/mm2 and after 28 days a cold compression strength of at least 20 N/mm2. As a result of the particular hardness St and form stability thereof even at high temperatures T, agglomerated stones according to the invention are especially suitable for use in shaft, corex or blast furnaces. The invention also relates to a method for producing agglomerated stones according to the invention.

Abstract: The invention concerns a method for dehydrating sludge, comprising adding a basic agent to sludge having a pH not more than 8, adding to the sludge at least one organic flocculating constituent, by adding said basic agent, increasing the sludge pH to a value not more than a pH at which occurs degradation of said at least one organic constituent, flocculating the sludge and separating in the flocculated sludge dehydrated sludge from a liquid phase, said basic agent being a magnesian limestone compound of formula xCaCO3,(1?x)[yMg(OH)2+(1?Y) MgO], wherein 0,45:=x=0,75, and 0=y=, the treated sludge having, until after said separation, said value less than a pH at which occurs degradation of said at least one organic constituent.

Abstract: In order to also be able to economically use iron ore dust which is created by the extraction and preparation of iron ore and has not been usable until now, the invention proposes an agglomerated stone comprising (in wt. %) 6-15% of a cement binding agent, up to 20% of a carbon carrier, up to 20% of residual and recyclable substances, optionally up to 10% of a coagulation and solidification accelerator and the remainder consisting of iron ore in a stone format in the form of particles having a particle size of less than 3 mm as well as possessing after three days an initial strength of at least 5 N/mm2 and after 28 days a cold compression strength of at least 20 N/mm2. As a result of the particular hardness St and form stability thereof even at high temperatures T, agglomerated stones according to the invention are especially suitable for use in shaft, corex or blast furnaces. The invention also relates to a method for producing agglomerated stones according to the invention.

Abstract: The invention concerns a method for dehydrating sludge, comprising adding a basic agent to sludge having a pH not more than 8, adding to the sludge at least one organic flocculating constituent, by adding said basic agent, increasing the sludge pH to a value not more than a pH at which occurs degradation of said at least one organic constituent, flocculating the sludge and separating in the flocculated sludge dehydrated sludge from a liquid phase, said basic agent being a magnesian limestone compound of formula xCaCO3,(1?x)[yMg(OH)2+(1?Y) MgO], wherein 0,45:=x=0,75, and 0=y=, the treated sludge having, until after said separation, said value less than a pH at which occurs degradation of said at least one organic constituent.