Abstract: A method for laser welding of one or more workpieces made from press hardenable steel, in a butt joint, in which the workpiece or the workpieces have a thickness of at least 1.8 mm and/or a jump in thickness of at least 0.4 mm arises at the butt joint including supplying filler wire into a molten bath generated by a laser beam. In order to ensure that the weld seam can reliably harden into a martensitic structure during the hot forming (press hardening), the filler wire contains at least one alloy element from the group of manganese, chromium, molybdenum, silicon and nickel, wherein the at least one alloy element is present in the filler wire with a mass proportion that is larger by 0.1% by weight than the mass proportion of the element in the press hardenable steel of the workpiece or the workpieces.

Abstract: A method for joint-welding coated metal sheets in a butt joint. At least one pulverulent welding additive in the form of a gas-powder flow is added to the weld melt via at least one flow duct, such that the gas-powder flow leaving the flow duct is directed towards the weld melt at a speed of at least 2 m/s, such that the welding additive mixes turbulently with the weld melt and flow eddies form in the weld melt. A device including at least one welding head for producing and/or focussing an energy beam and at least one flow duct for supplying gas-powder flow, the flow duct having a longitudinal axis, the longitudinal axis and the beam axis of the energy beam being at an angle between 15 and 75 degrees. The flow duct is adapted to set the gas powder flow to a speed of at least 2 m/s.

Abstract: A method for laser welding of one or more workpieces made from press hardenable steel, in a butt joint, in which the workpiece or the workpieces have a thickness of at least 1.8 mm and/or a jump in thickness of at least 0.4 mm arises at the butt joint including supplying filler wire into a molten bath generated by a laser beam. In order to ensure that the weld seam can reliably harden into a martensitic structure during the hot forming (press hardening), the filler wire contains at least one alloy element from the group of manganese, chromium, molybdenum, silicon and nickel, wherein the at least one alloy element is present in the filler wire with a mass proportion that is larger by 0.1% by weight than the mass proportion of the element in the press hardenable steel of the workpiece or the workpieces.

Abstract: A method for joint-welding coated metal sheets in a butt joint. At least one pulverulent welding additive in the form of a gas-powder flow is added to the weld melt via at least one flow duct such that the gas-powder flow leaving the flow duct is directed towards the weld melt at a speed of at least 2 m/s, such that the welding additive mixes turbulently with the weld melt and flow eddies form in the weld melt. A device including at least one welding head for producing and/or focussing an energy beam and at least one flow duct for supplying gas-powder flow, the flow duct having a longitudinal axis, the longitudinal axis and the beam axis of the energy beam being at an angle between 15 and 75 degrees. The flow duct is adapted to set the gas powder flow to a speed of at least 2 m/s.

Abstract: A method includes producing sheet steel products, in which steel blanks or steel strips of different thicknesses and/or material grades are welded together along a joint formed by edges of the steel blanks or steel strips. In order that the welding seam of such a sheet steel product does not lose the hardened microstructure obtained by abrupt cooling during warm forming with heating to an austenization temperature, before the welding process, a viscous liquid, such as a paste, or a solid, pulverulent, or aerosol-like substance that contains at least one component that increases the strength of the weld seam that is to be produced, is applied to at least one weld edge of the steel blanks or steel strips that are to be welded together.

Abstract: A method for laser welding of one or more workpieces made from press hardenable steel, in a butt joint, in which the workpiece or the workpieces have a thickness of at least 1.8 mm and/or a jump in thickness of at least 0.4 mm arises at the butt joint including supplying filler wire into a molten bath generated by a laser beam. In order to ensure that the weld seam can reliably harden into a martensitic structure during the hot forming (press hardening), the filler wire contains at least one alloy element from the group of manganese, chromium, molybdenum, silicon and nickel, wherein the at least one alloy element is present in the filler wire with a mass proportion that is larger by at least 0.1% by weight than the mass proportion of the element in the press hardenable steel of the workpiece or the workpieces.