Abstract: Provided is a method for producing a water-resistant aluminum nitride powder capable of adding a good water-resistant property to an aluminum nitride powder wherein yttria exists on a particle surface. The method is for producing a water-resistant aluminum nitride powder by carrying out a treatment to a particle surface of an aluminum nitride powder, the method including the successive steps of (i) making an aluminum nitride powder contact with an acid solution wherein yttria exists at least on a particle surface of the aluminum nitride powder; and (ii) making the aluminum nitride powder contact with a phosphorous acid compound, wherein the amount of yttria which is extracted when the aluminum nitride powder is filtered, washed with water, and dried after the step (i) and is thereafter subjected to extraction with 1 mol/L hydrochloric acid is no more than 1000 mg per 100 g of the aluminum nitride powder.

Abstract: Provided is a method for producing a water-resistant aluminum nitride powder capable of adding a good water-resistant property to an aluminum nitride powder wherein yttria exists on a particle surface. The method is for producing a water-resistant aluminum nitride powder by carrying out a treatment to a particle surface of an aluminum nitride powder, the method including the successive steps of (i) making an aluminum nitride powder contact with an acid solution wherein yttria exists at least on a particle surface of the aluminum nitride powder; and (ii) making the aluminum nitride powder contact with a phosphorous acid compound, wherein the amount of yttria which is extracted when the aluminum nitride powder is filtered, washed with water, and dried after the step (i) and is thereafter subjected to extraction with 1 mol/L hydrochloric acid is no more than 1000 mg per 100 g of the aluminum nitride powder.

Abstract: The present invention relates to a method of manufacturing water resistant aluminum nitride powder, the method comprises; in a solvent, performing phosphoric acid compound treatment in which at least one phosphoric acid compound selected from the group consisting of phosphoric acid, metal salts of phosphoric acid and organic phosphoric acid having an organic group with 12 or less carbon atoms is contacted with aluminum nitride powder dispersed in the solvent so that the ratio of median diameter/primary particle diameter is 1.4 to 5, thereby the phosphoric acid compound is present on the surface of the aluminum nitride powder at a rate of 0.5 to 10 mg/m2 in the orthophosphoric acid ion equivalence.