Abstract: Closed-cell and/or open-cell cellular perfluoroelastomeric materials are described which may be adapted for use in sealing members and laminates which improve low temperature elastomeric properties of perfluoroelastomeric materials. A variety of unique medical devices based on cellular and solid perfluoroelastomers are also described. The closed-cell cellular perfluoroelastomers are formed by combining a perfluoroelastomeric composition and a curing agent with a plurality of microspheres and/or a gas generating agent at a temperature high enough to soften the perfluoroelastomeric composition, but not high enough to expand the microspheres or activate the gas generating agent and then further heating the composition, microspheres and/or gas generating agents to cure the elastomer, expand the microspheres and/or activate the gas generating agent.

Abstract: A process for curing a heat-weldable roofing membrane by applying elemental sulfur on the exterior surface of the roofing membrane, said membrane being a blend of (a) 50-80% by weight of an ethylene/propylene/nonconjugated diene elastomer and (b) 20-50% by weight of an ethylene-containing polymer selected from the group consisting of polyethylene, an ethylene alpha-monoolefin copolymer wherein the monoolefin contains from 3-12 carbon atoms and is present in amounts of 2-8% by weight, and an ethylene/vinyl acetate copolymer having a vinyl acetate content up to about 10% by weight, said membrane containing a cure accelerator. The roofing membrane is exposed to ambient outdoor temperatures resulting in migration of sulfur to the interior of the membrane where, together with the cure accelerator, it effects cure of the membrane.

Abstract: A curable laminated article, useful for roofing application, comprising at least two layers, each layer comprising a blend of (a) 50-80% by weight of an ethylene/propylene/nonconjugated diene elastomer and (b) 20-50% by weight of an ethylene-containing polymer selected from the group consisting of polyethylene, an ethylene alpha-monoolefin copolymer wherein the monoolefin contains from 3-12 carbon atoms and is present in amounts of 2-8% by weight, and as ethylene/vinyl acetate copolymer having a vinyl acetate content up to about 10% by weight, and wherein each alternate layer contains either elemental sulfur as the crosslinking agent for the elastomer or a cure accelerator so that the elastomer in the laminated article subsequently cures when elemental sulfur and the accelerator in each layer migrate to an adjacent layer when the laminate is exposed to elevated temperatures.