Abstract: An isocyanate-reactive composition containing a blowing agent that includes HFC 134a and water characterized by a vapor pressure which is lower than that of comparable compositions which do not include the stabilizing composition of the present invention. The stabilizing composition of the present invention includes an ethoxylated nonylphenol and propylene carbonate. This stabilizing composition is included in the isocyanate-reactive composition in an amount sufficient to promote the solubility of the blowing agent. The isocyanate-reactive composition may be stored at ambient conditions rather than under pressure and may be hand mixed with an isocyanate to produce a foam. The isocyanate-reactive composition containing blowing agent of the present invention may be used to produce foams having good physical properties after storage at ambient temperature and pressure for periods as long as 3 months.

Abstract: The present invention relates to polyol compositions which can be used to produce dimensionally stable, low density water-blown rigid foams which have acceptable compressive strengths and acceptable k-factors. In one embodiment of the present invention, the polyol compositions are composed of at least one aromatic amine-initiated polyether polyol and at least one polyether polyol having a functionality greater than or equal to 2.5 in which at least 50% by weight of the polyol composition is aromatic amine-initiated polyether polyol and in which no more than 50% by weight of the polyol composition is polyether polyol having a functionality greater than or equal to 2.5.

Abstract: The present invention provides a rigid polyurethane foam formed by the reaction product, at an isocyanate index of about 160 or less, of a polyisocyanate, a polyol component containing an aromatic polyester polyol, and a sucrose-initiated polyether polyol and a flame retardant component made from a chlorine-containing combustion modifier and a bromine-containing combustion modifier in the presence of a hydrocarbon or hydrofluorocarbon blowing agent. The inventive polyurethane foam contains, based on the weight of the foam, at least about 3 wt. % chlorine, from about 1 wt. % to about 2 wt. % bromine and less than about 1 wt. % phosphorus, and exhibits good properties, good processing and good adhesion to metal whilst satisfying the ASTM E-84 Class I burn requirement.

Abstract: The present invention provides a rigid polyurethane spray foam, which is made using cyclopentane as the blowing agent and which is useful for pipe insulation because of its ability to withstand high-temperatures (>250° F.). The inventive foams may be sprayed with existing foam spraying equipment because the foams are reacted at about a 1:1.25 polyol to isocyanate ratio.

Abstract: The present invention relates to polyol compositions which can be used to produce dimensionally stable, low density water-blown rigid foams which have acceptable compressive strengths and acceptable k-factors. In one embodiment of the present invention, the polyol compositions are composed of at least one aromatic amine-initiated polyether polyol and at least one polyether polyol having a functionality greater than or equal to 2.5 in which at least 50% by weight of the polyol composition is aromatic amine-initiated polyether polyol and in which no more than 50% by weight of the polyol composition is polyether polyol having a functionality greater than or equal to 2.5.

Abstract: An isocyanate-reactive composition containing a blowing agent that is generally a gas at ambient temperature and pressure which is storage stable is produced by including a phenol or alkylphenol having at least one phenolic hydroxyl group in the isocyanate-reactive composition in an amount sufficient to promote the solubility of the blowing agent. The isocyanate-reactive composition may be stored at ambient conditions rather than under pressure. The isocyanate-reactive composition containing blowing agent may be used to produce foams having good physical properties after storage at ambient temperature and pressure for periods as long as 3 months.