Abstract: Poly(arylene sulfide) resins are modified by melt mixing a resin with a basic additive to form a resin product composition. The basic additive is selected from the group consisting of inorganic hydroxides, inorganic oxides and organic metal salts wherein the metals are from Group IA, IIA, or IIB and the salts are of carboxylic acids and phenols. The product compositions are suitable for injection molding, film forming and fiber spinning processes.

Abstract: Improved coatings derived from arylene sulfide polymers are provided by use of powdered or liquid slurry coating formulations comprising a metal oxide and an arylene sulfide polymer which has an extrusion rate of about 80 to about 400 grams/10 minutes.

Abstract: A poly(arylene sulfide) coating composition, method of preparing the composition, and method of coating are disclosed. The composition comprises a finely-divided poly(arylene sulfide) having from about 75 to about 99 mole percent para-polymerized aromatic units and from about 1 to about 25 mole percent ortho- or meta- polymerized aromatic units and, optionally, from about 0.1 to about 2 mole percent trifunctionally-polymerization aromatic units. The coating resin can be prepared in a polymerization reaction medium containing a molar excess of base, with respect to sulfur present, and can be washed with water at at least about 100.degree. C. to lower the curing temperature of the coating composition. The compositions are particularly suited for application in which curing temperatures of 350.degree. C. or lower are desired.

Abstract: In a process for preparing aromatic polyesters (polyarylates) by heating a bisphenol (e.g., Bisphenol-A), at least one dicarboxylic acid (e.g., terephthalic acid and isophthalic acid) and acetic anhydride, a gamma-butyrolactone, such as gamma-butyrolactone, is employed a diluent, reducing sublimation of reactants, and resulting in higher molecular weight of the polymer.

Abstract: A process for preparing aromatic polyesters (polyarylates) by heating a bisphenol (e.g., Bisphenol-A), at least one dicarboxylic acid (e.g., terephthalic acid and isophthalic acid) and acetic anhydride, in a carefully programmed sequence of steps, resulting in a polymer of suitable inherent viscosity and good color.