Abstract: The invention relates to a method of manufacturing a ceramic molding, comprising the following steps: a) providing three or more ceramic powder layers that are arranged in layers, one on top of the other, to form a compression-molded element and sintering the compression-molded element obtained in step b) to form a ceramic molding, characterized in that the ceramic powder layers have different compositions, each ceramic powder layer comprising a mixture of at least two different base powders and each base powder containing at least 80 wt. % ZrO2 and at least 0.02 wt. % Al2O3, each weight amount being relative to the total weight of the constituents of the base powder.

Abstract: The invention relates to a sintered molding with a color gradient for use in the manufacture of dental restorations, obtainable by sintering a compression-molded element comprising five or more different ceramic powder layers, each powder layer comprising at least two different base powders and each base powder containing at least 80 wt. % ZrO2, each weight amount being relative to the total weight of the base powder.

Abstract: The present invention relates to a process for producing a workpiece made of glass ceramics, and to the workpiece obtainable by the process according to the invention. Further, the invention relates to the use of the workpiece obtained as a dental restoration, and to a process allowing the translucency of a workpiece to be controlled.

Abstract: A non-dense sintered ceramic molded body having at least two layers, wherein a first powdery ceramic material forming a layer is contacted with at least a second powdery material forming at least a second layer. The body has a color gradient and maintains dimensional stability during sintering and forming. An admixing component and a common sintering temperature are used to control the volume decrease of the layers during sintering.

Abstract: A process for producing a non-dense sintered ceramic molded body having at least two layers, wherein a first powdery ceramic material forming a layer is contacted with at least a second powdery material forming at least a second layer; said first powdery material has a presintering temperature T1 that is higher than the presintering temperature TS of said at least second powdery ceramic material; the course of a curve of shrinkage S1 of said at least first powdery ceramic material differs from the course of a curve of shrinkage S2 of said at least second powdery material, wherein curve of shrinkage S1 is shifted towards higher temperatures as compared to curve of shrinkage S2; and the layers are subjected to a common temperature treatment at a presintering temperature TS that is lower than the presintering temperature T1 and at least equal to T3 to cause sintering that remains in a stage of sintering that has not proceeded to the theoretical density; wherein the curve of shrinkage S1 is modified by admixing

Abstract: The invention relates to glass ceramics based on the lithium metasilicate system (Li2O.SiO2(Li2SiO3)), which are mechanically processible in a simple manner in an intermediate stage of the crystallization and, after complete crystallization, represent a high-strength, highly translucent and chemically stable glass ceramic.

Abstract: A process for producing a non-dense sintered ceramic molded body having at least two layers, wherein a first powdery ceramic material forming a layer is contacted with at least a second powdery material forming at least a second layer; said first powdery material has a presintering temperature T1 that is higher than the presintering temperature Ts of said at least second powdery ceramic material; the course of a curve of shrinkage S1 of said at least first powdery ceramic material differs from the course of a curve of shrinkage S2 of said at least second powdery material, wherein curve of shrinkage S1 is shifted towards higher temperatures as compared to curve of shrinkage S2; and the layers are subjected to a common temperature treatment at a presintering temperature Ts that is lower than the presintering temperature T1 and at least equal to T3 to cause sintering that remains in a stage of sintering that has not proceeded to the theoretical density; wherein the curve of shrinkage S1 is modified by admixing a

Abstract: The present invention relates to a process for producing a workpiece made of glass ceramics, and to the workpiece obtainable by the process according to the invention. Further, the invention relates to the use of the workpiece obtained as a dental restoration, and to a process allowing the translucency of a workpiece to be controlled.

Abstract: The invention refers to a method for producing a dental restoration comprising a lithium silicate glass or glass ceramic as well as a dental restoration inself. The invention further refers to a ingot with the same composition having a defined strength.

Abstract: The invention relates to glass ceramics based on the lithium metasilicate system (Li2O.SiO2 (Li2SiO3)), which are mechanically processible in a simple manner in an intermediate stage of the crystallization and, after complete crystallization, represent a high-strength, highly translucent and chemically stable glass ceramic.

Abstract: The invention relates to glass ceramics, which show high strength, high translucency, high chemical stability and which are still mechanically processible. The invention further refers to a method for producing a dental restoration comprising such glass or glass ceramic as well as the dental restoration itself.

Abstract: The invention relates to glass ceramics based on the lithium metasilicate system (Li2OSiO2(Li2SiO3)), which are mechanically processible in a simple manner in an intermediate stage of the crystallization and, after complete crystallization, represent a high-strength, highly translucent and chemically stable glass ceramic.

Abstract: A process for producing a non-dense sintered ceramic molded body having at least two layers, wherein a first powdery ceramic material forming a layer is contacted with at least a second powdery material forming at least a second layer; said first powdery material has a presintering temperature T1 that is higher than the presintering temperature Ts of said at least second powdery ceramic material; the course of a curve of shrinkage S1 of said at least first powdery ceramic material differs from the course of a curve of shrinkage S2 of said at least second powdery material, wherein curve of shrinkage S1 is shifted towards higher temperatures as compared to curve of shrinkage S2; and the layers are subjected to a common temperature treatment at a presintering temperature Ts that is lower than the presintering temperature T1 and at least equal to T3 to cause sintering that remains in a stage of sintering that has not proceeded to the theoretical density; wherein the curve of shrinkage S1 is modified by admixing a

Abstract: The invention refers to a method for producing a dental restoration comprising a lithium silicate glass or glass ceramic as well as a dental restoration inself. The invention further refers to a ingot with the same composition having a defined strength.

Abstract: The invention relates to glass ceramics, which show high strength, high translucency, high chemical stability and which are still mechanically processible. The invention further refers to a method for producing a dental restoration comprising such glass or glass ceramic as well as the dental restoration itself.

Abstract: The invention relates to glass ceramics based on the lithium metasilicate system (Li2O SiO2 (Li2SiO3)), which are mechanically processible in a simple manner in an intermediate stage of the crystallization and, after complete crystallization, represent a high- strength, highly translucent and chemically stable glass ceramic.