Abstract: The invention relates to a novel polyolefin composition having a reduced occurrence of flow marks especially at high injection speeds. The novel polyolefin compositions comprise a heterophasic polypropylene composition, ethylene/propylene elastomer and an inorganic filler.

Abstract: Exterior automotive article comprising a composition comprising a polypropylene, an elastomeric copolymer, and a mineral filler, wherein said polypropylene (PP) has a comonomer content of equal or below 1.0 wt.-%, the comonomers are ethylene and/or at least one C4 to C20 a-olefin, and <2,1> erythro regiodefects of equal or more than 0.4 mol.-%, said elastomeric copolymer (EC) comprises units derived from ethylene and at least one C3 to C10 a-olefin, said composition (C) has a melt flow rate MFR2 (230° C.) in the range of 5 to 80 g/lOmin.

Abstract: Composition having a melt flow rate MFR2 (230° C.) in the range of 10 to 50 g/10 min. said composition comprises two heterophasic polypropylenes comprising a propylene homopolymer matrix and an elastomeric copolymer, a plastomer and a mineral filler, wherein—said two heterophasic polypropylenes have different melt flow rates, —the first heterophasic polypropylene has a melt flow rate MFR2 (230° C.) in the range of 3.0 to 30.0 g/10 min and—the second heterophasic polypropylene has a xylene cold soluble (XCS) content in the range of 7.0 to 20.0 wt.-%.

Abstract: The present invention relates to a polyolefin composition comprising (a) a heterophasic propylene copolymer, wherein the xylene cold soluble fraction of the heterophasic propylene copolymer has an intrinsic viscosity of lower than 2.0 dl/g, (b) a high density polyethylene having a density of at least 940 kg/m3, (c) a linear low density polyethylene, and (d) an inorganic filler, wherein the polyolefin composition has a MFR2 (230° C.) of at least 20 g/10 min.

Abstract: Heterophasic polypropylene composition comprising (A) 45 to 70 wt % of a propylene homo- or copolymer matrix with an MFR2 in accordance with ISO 1133 (230° C., 2.16 kg load) of ?80 g/10 min and (B) 25 to 40 wt % of an elastomeric propylene-ethylene copolymer, having an intrinsic viscosity IV (ISO 1628, with decalin as solvent) of ?3.3 dl/g and an ethylene content of 20 to 50 wt %, (C) 0-15 wt % of an elastomeric ethylene/alpha-olefin random copolymer (D) 3-25 parts per weight of inorganic filler, the heterophasic polypropylene compositions having a total MFR2 (230° C./2.16 kg) in accordance with ISO 1133 of ?5 g/10 min, a Charpy notched impact strength according to ISO 179/1eA at +23° C. of ?15.0 kJ/m2, preferably ?25.0 kJ/m2, a minimum value for the Charpy notched impact strength according to ISO 179/1eA at ?20° C. of ?7.0 kJ/m2, preferably ?10.0 kJ/m2 and a tensile modulus according to ISO 527-3 of ?1200 MPa; their preparation and use for producing injection moulded articles being free of flow marks.

Abstract: Heterophasic polypropylene composition comprising (A) 45 to 70 wt % of a propylene homo- or copolymer matrix with an MFR2 in accordance with ISO 1133 (230° C., 2.16 kg load) of ?80 g/10 min and (B) 25 to 40 wt % of an elastomeric propylene-ethylene copolymer, having an intrinsic viscosity IV (ISO 1628, with decalin as solvent) of ?3.3 dl/g and an ethylene content of 20 to 50 wt %, (C) 0-15 wt % of an elastomeric ethylene/alpha-olefin random copolymer (D) 3-25 parts per weight of inorganic filler, the heterophasic polypropylene compositions having a total MFR2 (230° C./2.16 kg) in accordance with ISO 1133 of ?5 g/10 min, a Charpy notched impact strength according to ISO 179/1eA at +23° C. of ?15.0 kJ/m2, preferably ?25.0 kJ/m2, a minimum value for the Charpy notched impact strength according to ISO 179/1eA at ?20° C. of ?7.0 kJ/m2, preferably ?10.0 kJ/m2 and a tensile modulus according to ISO 527-3 of ?1200 MPa; their preparation and use for producing injection moulded articles being free of flow marks.

Abstract: Heterophasic polypropylene composition comprising (A) 45 to 70 wt % of a propylene homo- or copolymer matrix with an MFR2 in accordance with ISO 1133 (230° C., 2.16 kg load) of ?80 g/10 min and (B) 25 to 40 wt % of an elastomeric propylene-ethylene copolymer, having an intrinsic viscosity IV (ISO 1628, with decalin as solvent) of ?3.3 dl/g and an ethylene content of 20 to 50 wt %, (C) 0-15 wt % of an elastomeric ethylene/alpha-olefin random copolymer (D) 3-25 parts per weight of inorganic filler, the heterophasic polypropylene compositions having a total MFR2 (230° C./2.16 kg) in accordance with ISO 1133 of ?5 g/10 min, a Charpy notched impact strength according to ISO 179/1eA at +23° C. of ?15.0 kJ/m2, preferably ?25.0 kJ/m2, a minimum value for the Charpy notched impact strength according to ISO 179/1eA at ?200 C of ?7.0 kJ/m2, preferably ?10.0 kJ/m2 and a tensile modulus according to ISO 527-3 of ?1200 MPa; their preparation and use for producing injection molded articles being free of flow marks.

Abstract: Fiber reinforced composition comprising a heterophasic propylene copolymer, a propylene homopolymer and/or a propylene copolymer, and fibers, wherein the propylene copolymer comprises not more than 2.0 wt.-% C2 to C10 ?-olefins other than propylene, the propylene homopolymer and the propylene copolymer have a melt flow rate MFR2 (230° C.) of at least 500 g/10 min, and the composition has a melt flow rate MFR2 (230° C.) of at least 10 g/10 min.

Abstract: Heterophasic polypropylene composition comprising (A) 45 to 70 wt % of a propylene homo- or copolymer matrix with an MFR2 in accordance with ISO 1133 (230° C., 2.16 kg load) of ?80 g/10 min and (B) 25 to 40 wt % of an elastomeric propylene-ethylene copolymer, having an intrinsic viscosity IV (ISO 1628, with decalin as solvent) of ? 3.3 dl/g and an ethylene content of 20 to 50 wt %, (C) 0-15 wt % of an elastomeric ethylene/alpha-olefin random copolymer (D) 3-25 parts per weight of inorganic filler, the heterophasic polypropylene compositions having a total MFR2 (230° C./2.16 kg) in accordance with ISO 1133 of ?5 g/10 min, a Charpy notched impact strength according to ISO 179/1eA at +23° C. of ?15.0 kJ/m2, preferably ?25.0 kJ/m2, a minimum value for the Charpy notched impact strength according to ISO 179/1eA at ?200 C of ?7.0 kJ/m2, preferably ?10.0 kJ/m2 and a tensile modulus according to ISO 527-3 of ?1200 MPa; their preparation and use for producing injection moulded articles being free of flow marks.

Abstract: Composition having a melt flow rate MFR2 (230° C.) in the range of 10 to 50 g/10 min. said composition comprises two heterophasic polypropylenes comprising a propylene homopolymer matrix and an elastomeric copolymer, a plastomer and a mineral filler, wherein said two heterophasic polypropylenes have different melt flow rates, the first heterophasic polypropylene has a melt flow rate MFR2 (230° C.) in the range of 3.0 to 30.0 g/10 min and the second heterophasic polypropylene has a xylene cold soluble (XCS) content in the range of 7.0 to 20.0 wt.-%.

Abstract: The invention relates to novel polyolefin compositions having a low coefficient of thermal expansion (CLTE), high stiffness and high flowability. The novel compositions comprise a heterophasic propylene copolymer, an inorganic filler, an ethylene/alpha-olefin elastomer and at least two different alpha-nucleating agents.