Abstract: In integrated circuit technology; an electromigration and diffusion sensitive conductor of a metal such as copper and processing procedure therefore is provided, wherein, at a planarized chemical mechanical processed interfacing surface, the conductor metal is positioned in a region of a selectable low K eff dielectric material surrounded by a material selected to be protection from outdiffusion and a source of a film thickness cap that is to form over the conductor metal and/or serve as a catalytic layer for electroless selective deposition of a CoWP capping .

Abstract: A method for forming a ultralow dielectric constant layer with controlled biaxial stress is described incorporating the steps of forming a layer containing Si, C, O and H by one of PECVD and spin-on coating and curing the film in an environment containing very low concentrations of oxygen and water each less than 10 ppm. A material is also described by using the method with a dielectric constant of not more than 2.8. The invention overcomes the problem of forming films with low biaxial stress less than 46 MPa.

Abstract: A method for forming a ultralow dielectric constant layer with controlled biaxial stress is described incorporating the steps of forming a layer containing Si, C, O and H by one of PECVD and spin-on coating and curing the film in an environment containing very low concentrations of oxygen and water each less than 10 ppm. A material is also described by using the method with a dielectric constant of not more than 2.8. The invention overcomes the problem of forming films with low biaxial stress less than 46 MPa.

Abstract: A method for forming a ultralow dielectric constant layer with controlled biaxial stress is described incorporating the steps of forming a layer containing Si, C, O and H by one of PECVD and spin-on coating and curing the film in an environment containing very low concentrations of oxygen and water each less than 10 ppm. A material is also described by using the method with a dielectric constant of not more than 2.8. The invention overcomes the problem of forming films with low biaxial stress less than 46 MPa.

Abstract: A carrier structure and method for fabricating a carrier structure with through-vias each having a conductive structure with an effective coefficient of thermal expansion which is less than or closely matched to that of the substrate, and having an effective elastic modulus value which is less than or closely matches that of the substrate. The conductive structure may include concentric via fill areas having differing materials disposed concentrically therein, a core of the substrate material surrounded by an annular ring of conductive material, a core of CTE-matched non-conductive material surrounded by an annular ring of conductive material, a conductive via having an inner void with low CTE, or a full fill of a conductive composite material such as a metal-ceramic paste which has been sintered or fused.

Abstract: In a multilevel microelectronic integrated circuit, air comprises permanent line level dielectric and ultra low-K materials are via level dielectric. The air is supplied to line level subsequent to removal of sacrificial material by clean thermal decomposition and assisted diffusion of byproducts through porosities in the IC structure. Optionally, air is also included within porosities in the via level dielectric. By incorporating air to the extent produced in the invention, intralevel and interlevel dielectric values are minimized.

Abstract: In integrated circuit technology; an electromigration and diffusion sensitive conductor of a metal such as copper and processing procedure therefore is provided, wherein, at a planarized chemical mechanical processed interfacing surface, the conductor metal is positioned in a region of a selectable low K eff dielectric material surrounded by a material selected to be protection from outdiffusion and a source of a film thickness cap that is to form over the conductor metal and/or serve as a catalytic layer for electroless selective deposition of a CoWP capping layer.