Abstract: The present invention relates to a process for adhering a textile material to an elastomer, the process comprising the steps of pretreating the textile material with at least one polyester of an ?-?-unsaturated carboxylic acid, contacting the pretreated textile material with an unvulcanized elastomer, and vulcanizing the product obtained. The present invention additionally encompasses an elastomer article obtainable by this process and also the use of a polyester of an ?-?-unsaturated carboxylic acid for improving the adhesion of a textile material to an elastomer.

Abstract: A method for producing a sheet-like composite fabric material, in particular a rubberized fabric or a fabric provided with a polymer preparation, for covering drive belts, the composite fabric material comprising a textile integrated in a matrix of elastomeric material, preferably at least one fabric layer integrated in a rubber matrix, the textile or the fabric layer and the elastomeric material being introduced into a gap between a band and a cylindrical molding wheel and molded to form a composite material between the band and the molding wheel at a temperature below the vulcanization temperature, the band looping around the molding wheel at a looping angle under pressure. Likewise disclosed is a drive belt with a covering of composite material produced according to the invention.

Abstract: The present invention relates to a process for adhering a textile material to an elastomer, the process comprising the steps of pretreating the textile material with at least one polyester of an ?-?-unsaturated carboxylic acid, contacting the pretreated textile material with an unvulcanized elastomer, and vulcanizing the product obtained. The present invention additionally encompasses an elastomer article obtainable by this process and also the use of a polyester of an ?-?-unsaturated carboxylic acid for improving the adhesion of a textile material to an elastomer.

Abstract: A method for producing a sheet-like composite fabric material, in particular a rubberized fabric or a fabric provided with a polymer preparation, for covering drive belts, the composite fabric material comprising a textile integrated in a matrix of elastomeric material, preferably at least one fabric layer integrated in a rubber matrix, the textile or the fabric layer and the elastomeric material being introduced into a gap between a band and a cylindrical molding wheel and molded to form a composite material between the band and the molding wheel at a temperature below the vulcanization temperature, the band looping around the molding wheel at a looping angle under pressure. Likewise disclosed is a drive belt with a covering of composite material produced according to the invention.

Abstract: A drive belt with a main body made of a polymeric material having resilient properties, comprising a top layer as the belt rear face and a base having a force transfer zone, wherein moreover at least one tension cord is embedded in the main body. Three drive belt variants are specified. In addition, the top layer and/or the force transfer zone are/is provided with a pressure-resistant coating. The drive belt is characterized in that at least the top layer and/or the base are/is free from carbon black and free from polycyclic aromatic hydrocarbons (PAH). The tension cord and/or abrasion-resistant coating are/is preferably prepared with an adhesive system that is likewise free from carbon black and PAH.

Abstract: The invention relates to an elastomeric product which contains a radical cross-linked rubber mixture, especially drive belts. For the production of elastomeric products, especially drive belts, having a long service life and producible in an environmentally friendly way, the rubber mixture contains (a) 0.1 to 50 phr of at least one carboxylic acid, which is at least ?,? unsaturated and ?,? unsaturated and preferably has at least one allylic hydrogen atom; and, (b) 0.1 to 50 phr of at least one salt-former as co-activator.

Abstract: The invention relates to a drive belt (1), particularly a toothed belt, having an elastic base body, comprising a cover layer (2) as the belt back, and a subframe (4) having a power transmission zone (7), wherein the base body is made from oil-resistant vulcanized rubber on the basis of a copolymer comprising butadiene and acrylonitrile, particularly HNBR, wherein according to the invention the proportion of acrylonitrile (CAN proportion) is <33% by weight with regard to the total weight of the copolymer. The particularly advantageous CAN proportion is 20 to 35% by weight. The power transmission zone (7) is typically also equipped with a textile cover (8), which is further provided with an oil-resistant protective layer (9), which is preferably made from PTFE.

Abstract: An HNBR-based toothed rubber belt (10) with a glass, carbon and/or aramid cord reinforcement (5) has a modified tooth covering (6) made of polyamide 6.6 fabric having weft threads (64) entirely or partly replaced in the peripheral/longitudinal direction of the belt by yarns made of polyether ether ketone (PEEK), polyimide (PI) and/or meta-aramid (M-A) or modified with PEEK, PI and/or M-A.

Abstract: The invention relates to an elastomeric product which contains a radical cross-linked rubber mixture, especially drive belts. For the production of elastomeric products, especially drive belts, having a long service life and producible in an environmentally friendly way, the rubber mixture contains (a) 0.1 to 50 phr of at least one carboxylic acid, which is at least ?,? unsaturated and ?,? unsaturated and preferably has at least one allylic hydrogen atom; and, (b) 0.1 to 50 phr of at least one salt-former as co-activator.

Abstract: A rubber mixture containing at least one rubber component, at least one filler, and conventional additives that it contain at least one first gel as a filler, which is essentially comprised of a rubber, has a particle size of 3×10−9 to 1×10−6 m, and has a swelling index in toluene of 1 to 15, and at least the surface of this gel has acid or base groups, where these groups have not been produced by means of reaction with dithiophosphoric acid, and comprises: a) at least one second gel as an additional filler, which is essentially comprised of a rubber, has a particle size of 3×10−9 to 1×10−6 m, and has a swelling index in toluene of 1 to 15, which is in a position to undergo a neutralization reaction with the acid or base groups of the first gel and/or b) contains at least one substance as an additional additive, which is capable of undergoing a neutralization reaction with the acid or base groups of at least one gel.

Abstract: A rubber composition which contains a rubber mixture that can be vulcanized with a vulcanizing agent, which includes at least one rubber component, at least one filler having nucleophilic groups, gel particles comprising a rubber, having a particle size between about 3×10−9 and about 1×10−6 m and a swelling index in toluene of about 1 to about 15 and whose surface has electrophilic centers, and a substance acting as a coupling agent between the filler having nucleophilic groups and the additional filler, the substance acting as a coupling agent having the following structure: X—R1—Si—(R2)3, wherein X is a nucleophilic group, R1 is an alkyl group having up to about 6 carbon atoms or a phenyl group, and R2 may be the same as or different from each other and from R1 and is an alkyl or alkoxy group having up to 6 carbon atoms and at least one of R2 is an alkoxy group.

Abstract: A rubber composition, which contains a rubber mixture that can be vulcanized with a vulcanizing agent, which includes at least one rubber component, at least one filler, gel particles comprising a rubber, having a particle size between about 3.times.10.sup.-9 and about 1.times.10.sup.-6 m and a swelling index in toluene of about 1 to about 15 and whose surface has electrophilic centers, and a substance which acts as a coupling agent between the gel particles and which has the structure A--R--A, wherein A is a nucleophilic group, and R is a saturated or unsaturated hydrocarbon group. The rubber composition has improved hysteresis behavior in the vulcanized state so that when this rubber composition is used in tires, the rolling resistance is reduced and the wet slippage behavior is improved in relation to the conventional rubber compositions. A method of formulating the rubber composition as well as a composition useful for tire treads and vehicle tires containing the composition are disclosed.

Abstract: Unvulcanized rubber mixture that can be cross linked with sulfur, including: (A) 100 weight parts of total mass of unvulcanized rubber including: about 40 to 100 weight parts of styrene-butadiene-copolymer (S-SBR) that is produced in solution; and (B) relative to the 100 weight parts of total mass of unvulcanized rubber: about 50 to 80 pphr silicic acid, about 3 to 7 pphr silanization agent, about 0.1 to 0.5 pphr tetrabenzylthiuramdisulfide (TBzTD), and about 1 to 3 pphr benzothiazyl-2-cyclohexylsulfenamide (CBS). A vulcanization process, including vulcanizing the unvulcanized rubber mixture. A tire including a tread that is produced from the unvulcanized rubber mixture.