Abstract: The present invention relates to a method for the manufacture of galvannealed metal sheet, wherein a hot strip is produced from an IF steel containing 0.01 to 0.1 wt. % silicon, wherein the hot strip is coiled at a coiler temperature no lower than 700° C. and no higher than 750° C., wherein a cold strip is rolled from the coiled hot strip, wherein the cold strip is recrystallization-annealed in an annealing furnace in an annealing gas atmosphere, wherein the cold strip thus annealed is provided with a zinc coating in a zinc bath, and wherein the coated cold strip is post-annealed at a galvannealing temperature no lower than 500° C. and no higher than 540° C. The invention also relates to a galvannealed metal sheet which possesses improved adhesion of the coating layer to the base material and proposes a method which is suited for the manufacture of metal sheet having such properties.

Abstract: The present invention relates to a method for the manufacture of galvannealed metal sheet, wherein a hot strip is produced from an IF steel containing 0.01 to 0.1 wt. % silicon, wherein the hot strip is coiled at a coiler temperature no lower than 700° C. and no higher than 750° C., wherein a cold strip is rolled from the coiled hot strip, wherein the cold strip is recrystallisation-annealed in an annealing furnace in an annealing gas atmosphere, wherein the cold strip thus annealed is provided with a zinc coating in a zinc bath, and wherein the coated cold strip is post-annealed at a galvannealing temperature no lower than 500° C. and no higher than 540° C. The invention also relates to a galvannealed metal sheet which possesses improved adhesion of the coating layer to the base material and proposes a method which is suited for the manufacture of metal sheet having such properties.