Abstract: An Fe-based, primary, ultrafine crystalline alloy ribbon having a composition represented by the general formula of Fe100-x-y-z-a-bNixCuyNbzSiaBb, wherein x, y, z, a and b are numbers (atomic %) meeting the conditions of 4?x?6, 0.1?y?2, 0.1?z?4, 7?a?18, and 4?b?12; an as-cast structure in which fine crystal grains having a grain size distribution of 300 nm or less are dispersed in a proportion of more than 0% and 7% or less by volume in an amorphous matrix; and a thickness of 13-23 ?m.

Abstract: An amorphous alloy ribbon free from embrittlement and crystallization and having excellent surface conditions and shape in edge portions is produced by (a) preparing an alloy melt having a composition comprising 13 atomic % or less of B and 15 atomic % or less of at least one selected from the group consisting of transition elements of Groups 4A, 5A and 6A, the balance being substantially Fe; (b) ejecting the alloy melt at a temperature from the melting point of the alloy +50° C. to the melting point of the alloy +250° C. through a nozzle onto the cooling roll rotating at a peripheral speed of 35 m/second or less, a distance between a tip end of the nozzle and the cooling roll being 200 &mgr;m or less; (c) starting to supply a gas based on CO2 to the alloy melt after the surface temperature of the cooling roll has become substantially constant; and (d) grinding the cooling roll while supplying the gas based on CO2.

Abstract: An amorphous alloy ribbon free from embrittlement and crystallization and having excellent surface conditions and shape in edge portions is produced by (a) preparing an alloy melt having a composition comprising 13 atomic % or less of B and 15 atomic % or less of at least one selected from the group consisting of transition elements of Groups 4A, 5A and 6A, the balance being substantially Fe; (b) ejecting the alloy melt at a temperature from the melting point of the alloy +50° C. to the melting point of the alloy +250° C. through a nozzle onto the cooling roll rotating at a peripheral speed of 35 m/second or less, a distance between a tip end of the nozzle and the cooling roll being 200 &mgr;m or less; (c) starting to supply a gas based on CO2 to the alloy melt after the surface temperature of the cooling roll has become substantially constant; and (d) grinding the cooling roll while supplying the gas based on CO2.

Abstract: A soft magnetic alloy strip is manufactured by a single roll method. The soft magnetic alloy strip is 0.2×d mm or less (, which “d” is a width of the strip,) in warpage in the widthwise direction of the strip, and has a continuous, long length not less than 50 m, in which a width of an air pockets occurring on a roll contact face is not more than 35 &mgr;m, a length of the air pockets is not more than 150 &mgr;m, and the centerline average roughness Ra of the roll contact face is not more than 0.5 &mgr;m.

Abstract: A method for winding a rapidly quenched thin metal ribbon has the steps of (1) ejecting a molten metal onto a rotating cooling roll to rapidly solidify the molten metal to form a thin metal ribbon, (2) peeling the thin metal ribbon from the cooling roll to let the thin metal ribbon to freely move from the cooling roll, and (3) bringing a rotating winding roll having an adhesive thereon into contact with the freely moving thin metal ribbon at an intermediate point thereof, so that the thin metal ribbon is wound around the winding roll with an excess portion of the thin metal ribbon forward of the intermediate point cut off.

Abstract: A method for winding a rapidly quenched thin metal ribbon has the steps of (1) ejecting a molten metal onto a rotating cooling roll to rapidly solidify the molten metal to form a thin metal ribbon, (2) peeling the thin metal ribbon from the cooling roll to let the thin metal ribbon to freely move from the cooling roll, and (3) bringing a rotating winding roll having an adhesive thereon into contact with the freely moving thin metal ribbon at an intermediate point thereof, so that the thin metal ribbon is wound around the winding roll with an excess portion of the thin metal ribbon forward of the intermediate point cut off.