Abstract: Provided is a fluororubber composition capable of providing a crosslinked fluororubber article that exhibits not only heat resistance, but also excellent mechanical properties at high temperatures. The fluororubber composition includes a fluororubber (A), a carbon black (B), and an aromatic petroleum resin (E), and the fluororubber composition has a difference ?G? (G? (1%)?G? (100%)) of not lower than 120 kPa and not higher than 3,000 kPa, where G? (1%) denotes a shear modulus at a dynamic strain of 1%, G? (100%) denotes a shear modulus at a dynamic strain of 100%, and G? (1%) and G? (100%) are determined by a dynamic viscoelasticity test carried out on an unvulcanised rubber with a rubber process analyzer (RPA) in a condition that the measurement frequency is 1 Hz and the measurement temperature is 100° C.

Abstract: A fluororubber composition including a fluororubber having an iodine content of 10 to 90 mol % for the total mole of the polymer end groups and a carbon black (B), wherein a difference (?G?), represented by G?(1%)-G?(100%), is not lower than 120 kPa and not higher than 3,000 kPa, where G?(1%) denotes a shear modulus at a dynamic strain of 1% under an uncrosslinked state and G?(100%) denotes a shear modulus at a dynamic strain of 100% under an uncrosslinked state, and G?(1%) and G?(100%) are determined by a dynamic viscoelasticity test with a rubber process analyzer (RPA) in a condition that the measurement frequency is 1 Hz and the measurement temperature is 100° C.

Abstract: A fluororubber composition which includes a fluororubber (A) and a carbon black (B). The fluororubber (A) is a vinylidene fluoride-based fluororubber including a structural unit (VdF unit) derived from vinylidene fluoride and a structural unit derived from at least one monomer selected from the group consisting of hexafluoropropylene (HFP), 2,3,3,3-tetrafluoro propylene, and perfluoro(alkyl vinyl ether) (PAVE). The molar ratio of the VdF unit to the structural unit derived from at least one monomer selected from the group consisting of HFP, 2,3,3,3-tetrafluoro propylene, and PAVE is 50/50 to 78/22. The fluororubber composition has a difference ?G? (G? (1%)-G? (100%)) of not lower than 120 kPa and not higher than 3,000 kPa, where G? (1%) denotes a modulus of shearing elasticity at a dynamic strain of 1%, G? (100%) denotes a modulus of shearing elasticity at a dynamic strain of 100%, and G? (1%) and G? (100%) are determined by a dynamic viscoelasticity test.

Abstract: The invention provides a fluororubber composition able to produce a crosslinked fluororubber article that exhibits not only heat resistance, but also excellent mechanical properties at high temperatures, and a method for producing same. The fluororubber composition contains: a fluororubber (A); and carbon black (B), wherein when the aforementioned fluororubber composition is immersed for 160 hours in an extraction solvent of acetone and hexane at an acetone:hexane mass ratio of 42.29:57.71 at 40° C. and an extraction residue that is not extracted and remains as a solid is separated from the aforementioned extraction solvent and dried and then the dry weight of the extraction residue is measured, the quantity of a solvent-insoluble polymer is not lower than 5%.

Abstract: Provided is a fluororubber composition capable of providing a crosslinked fluororubber article that exhibits not only heat resistance, but also excellent mechanical properties at high temperatures. The fluororubber composition includes a fluororubber (A), a carbon black (B), and an aromatic petroleum resin (E), and the fluororubber composition has a difference ?G? (G? (1%)?G? (100%)) of not lower than 120 kPa and not higher than 3,000 kPa, where G? (1%) denotes a shear modulus at a dynamic strain of 1%, G? (100%) denotes a shear modulus at a dynamic strain of 100%, and G? (1%) and G? (100%) are determined by a dynamic viscoelasticity test carried out on an unvulcanised rubber with a rubber process analyzer (RPA) in a condition that the measurement frequency is 1 Hz and the measurement temperature is 100° C.

Abstract: There is provided a polyol-crosslinkable fluorine-containing elastomer composition which is excellent in chemical resistance, solvent resistance (especially resistance to an acidic solvent) and fuel resistance (especially biofuel resistance) and is crosslinkable at the same crosslinking speed as in the case of using calcium hydroxide in a usual amount even without blending calcium hydroxide (or decreasing a blending amount of calcium hydroxide). The fluorine-containing elastomer composition comprises a polyol-crosslinkable fluorine-containing elastomer, a polyol crosslinking agent and a silicate of an alkali metal.

Abstract: A fluororubber composition which includes a fluororubber (A) and a carbon black (B). The fluororubber (A) is a vinylidene fluoride-based fluororubber including a structural unit (VdF unit) derived from vinylidene fluoride and a structural unit derived from at least one monomer selected from the group consisting of hexafluoropropylene (HFP), 2,3,3,3-tetrafluoro propylene, and perfluoro(alkyl vinyl ether) (PAVE). The molar ratio of the VdF unit to the structural unit derived from at least one monomer selected from the group consisting of HFP, 2,3,3,3-tetrafluoro propylene, and PAVE is 50/50 to 78/22. The fluororubber composition has a difference ?G? (G? (1%)-G? (100%)) of not lower than 120 kPa and not higher than 3,000 kPa, where G? (1%) denotes a modulus of shearing elasticity at a dynamic strain of 1%, G? (100%) denotes a modulus of shearing elasticity at a dynamic strain of 100%, and G? (1%) and G? (100%) are determined by a dynamic viscoelasticity test.

Abstract: A fluororubber composition including a fluororubber having an iodine content of 10 to 90 mol % for the total mole of the polymer end groups and a carbon black (B), wherein a difference (?G?), represented by G?(1%)-G?(100%), is not lower than 120 kPa and not higher than 3,000 kPa, where G?(1%) denotes a shear modulus at a dynamic strain of 1% under an uncrosslinked state and G?(100%) denotes a shear modulus at a dynamic strain of 100% under an uncrosslinked state, and G?(1%) and G?(100%) are determined by a dynamic viscoelasticity test with a rubber process analyzer (RPA) in a condition that the measurement frequency is 1 Hz and the measurement temperature is 100° C.

Abstract: The invention provides a method for producing a fluororubber composition that is able to give a crosslinked article that exhibits not only heat resistance, but also excellent mechanical properties at high temperatures. A method for producing a fluororubber composition includes: a step (1-1) of mixing a fluororubber (A) and a carbon black (B) by means of an internal mixer until the maximum temperature reaches 80 to 220° C. so as to obtain an intermediate composition; a step (1-2) of cooling the intermediate composition to a temperature of less than 50° C.; and a step (2-1) of mixing the cooled intermediate composition until the maximum temperature reaches not lower than 10° C. but lower than 80° C. so as to obtain a fluororubber composition.

Abstract: The invention provides a fluororubber composition able to produce a crosslinked fluororubber article that exhibits not only heat resistance, but also excellent mechanical properties at high temperatures, and a method for producing same. The fluororubber composition contains: a fluororubber (A); and carbon black (B), wherein when the aforementioned fluororubber composition is immersed for 160 hours in an extraction solvent of acetone and hexane at an acetone:hexane mass ratio of 42.29:57.71 at 40° C. and an extraction residue that is not extracted and remains as a solid is separated from the aforementioned extraction solvent and dried and then the dry weight of the extraction residue is measured, the quantity of a solvent-insoluble polymer is not lower than 5%.

Abstract: There is provided a polyol-crosslinkable fluorine-containing elastomer composition which is excellent in chemical resistance, solvent resistance (especially resistance to an acidic solvent) and fuel resistance (especially biofuel resistance) and is crosslinkable at the same crosslinking speed as in the case of using calcium hydroxide in a usual amount even without blending calcium hydroxide (or decreasing a blending amount of calcium hydroxide). The fluorine-containing elastomer composition comprises a polyol-crosslinkable fluorine-containing elastomer, a polyol crosslinking agent and a silicate of an alkali metal.

Abstract: A molded article prepared by polyol-crosslinking a fluorine-containing elastomer composition containing a polyol-crosslinkable fluorine-containing elastomer, a polyol crosslinking agent and a silicate of an alkali metal.

Abstract: The present invention provides a laminated article having improved adhesion of the fluorine-containing resin layer to the elastomer layer. The laminated article comprises a fluorine-containing resin layer (a) formed using a fluorine-containing resin having a carbonyl group, an olefin group or an amino group at an end of a polymer trunk chain or an end of a polymer side chain, and an elastomer layer (b) formed using an elastomer composition.

Abstract: The present invention provides a laminated article having improved adhesion of the fluorine-containing resin layer to the elastomer layer. The laminated article comprises a fluorine-containing resin layer (a) formed using a fluorine-containing resin having a carbonyl group, an olefin group or an amino group at an end of a polymer trunk chain or an end of a polymer side chain, and an elastomer layer (b) formed using an elastomer composition.

Abstract: There is provided a polyol-crosslinkable fluorine-containing elastomer composition which is excellent in chemical resistance, solvent resistance (especially resistance to an acidic solvent) and fuel resistance (especially biofuel resistance) and is crosslinkable at the same crosslinking speed as in the case of using calcium hydroxide in a usual amount even without blending calcium hydroxide (or decreasing a blending amount of calcium hydroxide). The fluorine-containing elastomer composition comprises a polyol-crosslinkable fluorine-containing elastomer, a polyol crosslinking agent and a silicate of an alkali metal.