Abstract: An extrusion molded gasket and a method of making such a gasket comprising one or more annular sections configured to engage a door rim of an appliance tub, one or more annular sections configured to engage the appliance tub, and one or more sealing sections disposed therebetween, wherein the gasket comprises at least one thermoplastic vulcanizate comprising at least 15 wt %, by weight of the thermoplastic vulcanizate (TPV), of a cross-linkable ethylene-based elastomer and within a range from 5 to 30 wt %, by weight of the TPV, of at least one thermoplastic, the TPV having a Shore Hardness within a range from 35 A to 100 A (or 50 D), and wherein the TPV is extrusion molded into the gasket

Abstract: An elastomeric composition is provided that includes from 1 to 100 parts by weight per hundred parts by weight rubber (phr) of a first propylene-?-olefin-diene (PEDM) terpolymer comprising 70 wt % to 92.5 wt % propylene, 7.5 wt % to 30 wt % a C2 or C4-C12 ?-olefin, and 3.5 wt % to 20 wt % diene, said wt % based on the weight of the PEDM terpolymer. The PEDM terpolymer V may have a Mooney viscosity (ML(1+4)) of 25 MU to 100 MU. The composition may further include from 0 to 99 phr of an ethylene-based copolymer comprising 40 wt % to 95 wt % ethylene.

Abstract: Rubber compounds that comprise rubber and propylene-a-olefin-diene (PE(D)M) polymers may be useful in tire-related articles (e.g., tire sidewalls, inner tubes, and innerliners). Such a rubber compound may comprise: about 5 phr to about 50 phr of the PE(D)M polymer that comprises about 65 wt % to about 99.5 wt % propylene, about 0.

Abstract: A rubber compound suitable for making industrial conveyor belts and power transmission belts may comprise: 100 parts by weight per hundred parts by weight rubber (phr) of a rubber; and 1 phr to 30 phr of a propylene-?-olefin-diene (PE(D)M) polymer comprising 65 wt % to 97.5 wt % propylene, 2.5 wt % to 35 wt % C2 or C4-C20 ?-olefin, and 0.2 wt % to 20 wt % diene, said wt % based on the weight of the PE(D)M polymer, and wherein the PE(D)M polymer has (a) Mooney viscosity (ML(1+4) @ 125° C.) of 1 to 100, (b) melt flow rate of 0.1 g/min to 100 g/min, and (c) a weight average molecular weight to n-average molecular weight (Mw/Mn) ratio of 1.5 to 3.0.

Abstract: Provided are compositions comprising: (a) an ethylene-propylene-diene terpolymer having a Mooney viscosity [ML(1+4) 125° C.] of about 25 to about 300 and an ethylene content of at least about 60 wt % of the ethylene-propylene-diene terpolymer; and (b) a polyolefin elastomer. The presence of the polyolefin elastomer improves rheological properties of the composition to an extent that does not significantly compromise other properties, such as tensile strength at break and compression set.

Abstract: Provided are compositions comprising: (a) an ethylene-propylene-diene terpolymer having a Mooney viscosity [ML(1+4) 125° C.] of about 25 to about 300 and an ethylene content of at least about 60 wt % of the ethylene-propylene-diene terpolymer; and (b) a polyolefin elastomer. The presence of the polyolefin elastomer improves rheological properties of the composition to an extent that does not significantly compromise other properties, such as tensile strength at break and compression set.