Abstract: There is provide a method for manufacturing analytical semiconductor samples by using an apparatus for manufacturing analytical semiconductor samples, which minimizes a feedback time by manufacturing a viewing surface that is environment-friendly and has a large area. The method comprising mounting the analytical semiconductor samples to a holder; discharging deionized (DI) water to an upper surface of a polishing plate through a DI water nozzle; grinding the analytical semiconductor samples with the upper surface of the polishing plat; determining whether a desired viewing surface of the analytical semiconductor samples has been acquired after the grinding of the analytical semiconductor samples; and transferring the analytical semiconductor samples to analyze the viewing surface of the ground analytical semiconductor samples based on a determination that the desired viewing surface of the analytical semiconductor samples has been acquired.

Abstract: Provided is a hot rolled steel sheet having excellent strength and elongation. The hot rolled steel sheet contains, by wt %: carbon (C): 0.05% or more and less than 0.4%, manganese (Mn): 10% to 15%, aluminum (Al): 2% or less, silicon (Si): 0.1 to 2%, molybdenum (Mo): 0.5% or less (excluding 0), vanadium (V): 0.5% or less (excluding 0), phosphorus (P): 0.01% or less, sulfur (S): 0.01% or less, and a remainder of iron (Fe) and inevitable impurities. The hot rolled steel sheet has a microstructure of the hot rolled steel sheet containing, by area %, tempered martensite: 50% to 70%, secondary martensite: 20% or less (excluding 0), epsilon martensite: 2% or less (excluding 0), and retained austenite: 8% to 30%. The hot rolled steel sheet has a tensile strength of at least 1500 MPa, a yield strength of at least 900 MPa and elongation of at least 20%.

Abstract: Provided is a hot rolled steel sheet having excellent strength and elongation. The hot rolled steel sheet contains, by wt %: carbon (C): 0.05% or more and less than 0.4%, manganese (Mn): 10% to 15%, aluminum (Al): 2% or less, silicon (Si): 0.1 to 2%, molybdenum (Mo): 0.5% or less (excluding 0), vanadium (V): 0.5% or less (excluding 0), phosphorus (P): 0.01% or less, sulfur (S): 0.01% or less, and a remainder of iron (Fe) and inevitable impurities. The hot rolled steel sheet has a microstructure of the hot rolled steel sheet containing, by area %, tempered martensite: 50% to 70%, secondary martensite: 20% or less (excluding 0), epsilon martensite: 2% or less (excluding 0), and retained austenite: 8% to 30%. The hot rolled steel sheet has a tensile strength of at least 1500 MPa, a yield strength of at least 900 MPa and elongation of at least 20%.