Abstract: The present invention is to provide a coating composition capable of forming a protective film excellent in adhesion properties. Such a coating composition comprises a specific polymer containing carboxyl group, a specific multifunctional epoxide-containing compound having two or more epoxy groups, an organic solvent, and an amino-containing silane coupling agent represented by the following general formula (I): H2N—R1—Si—(OR2)3  (I) wherein, R1 is an unsubstituted alkylene group, and R2's are independently an unsubstituted alkyl group.

Abstract: The present invention is to provide a coating composition capable of forming a protective film excellent in adhesion properties.

Abstract: A photosensitive resin composition comprising (a) a photosensitizer having in its structure 1,2-diazidonaphthoquinone structure, and a methylene-bridged structure composed of two or more methyl-substituted phenol derivatives, (b) a polymer having both hydroxyl group and carboxyl group, or a combination of a polymer having hydroxyl group and one having carboxyl group, (c) a crosslinking agent capable of crosslinking hydroxyl group and carboxyl group, and (d) a solvent. This composition can form highly transparent films, and, in addition, patterns having high contrast can be obtained when this composition is used as a photoresist.

Abstract: Provided is a process for manufacturing sintered polybenzimidazole (PBI) articles at high yields, said articles having neither voids nor porous, low-strength parts resulting from oxidative deterioration. To produce said sintered PBI articles from a particulate PBI resin, said PBI resin is compacted in a closed mold, the mold is heated up to a predetermined temperature of from 350.degree. to 600.degree. C. without applying any external pressure thereto, then, after having heated up to said predetermined temperature, the mold is pressed to have a predetermined external pressure of from 140 to 1400 kg/cm2 at said predetermined temperature whereby the resin is sintered for from 60 to 350 minutes under that conditions, and finally the sintered PBI article is cooled and taken out of the mold.