Abstract: An abrasion resistant steel excellent in bending formability and suitable for members, e.g., power shovels, which come into contact with earth and sand, and a production method thereof are provided. Specifically, the steel contains, on a percent by mass basis, 0.05% to 0.35% of C, 0.05% to 1.0% of Si, 0.1% to 2.0% of Mn, 0.1% to 1.2% of Ti, 0.1% or less of Al, at least one element of 0.1% to 1.0% of Cu, 0.1% to 2.0% of Ni, 0.1% to 1.0% of Cr, 0.05% to 1.0% of Mo, 0.05% to 1.0% of W, and 0.0003% to 0.0030% of B, if necessary at least one element of 0.005% to 1.0% of Nb and 0.005% to 1.0% of V, and the remainder including Fe and incidental impurities, where DI* represented by the following formula is less than 60: DI*=33.85×(0.1×C*)0.5×(0.7×Si+1)×(3.33×Mn+1)×(0.35×Cu+1)×(0.36×Ni+1)×(2.16×Cr+1)×(3×Mo*+1)×(1.5×W*+1)??(1) where C*=C?1/4×(Ti?48/14N), Mo*=Mo×(1?0.5×(Ti?48/14N)), and W*=W×(1?0.5×(Ti?48/14N)).

Abstract: A mount assembly having mounts which are provided on optical devices to be detachably attached to each other and which have mount surfaces which come into contact with each other when the optical devices are attached to each other through the mounts, wherein at least one of the mounts includes in combination a mount body which is made of synthetic resin and which is provided with the mount surface and a reinforcing metal ring member.

Abstract: A method for manufacturing titanium clad steel plate by forming a slab assembly having an alloy steel substrate, a titanium metal or alloy cladding on said substrate and a Ni-Cr alloy foil or film having opposed surfaces between said alloy steel and said cladding. The Ni-Cr alloy foil or film has one surface in surface contact with the cladding and the opposed surface in surface contact with the alloy steel substrate. The Ni-Cr alloy contains 32.5 to 40 wt. % Cr and 55 to 65 wt. % Ni. The slab assembly is heated at a temperature of 850.degree. to 1010.degree. C. The heated slab assembly is hot rolled with a reduction ratio of 30% or more to form the titanium clad steel plate.

Abstract: A high strength and corrosion resistant titanium alloy having excellent corrosion-wear properties may be prepared in that Al and Mo are added as alloying elements in specific amounts, and if Zr in a specific amount is further added, the strength and the corrosion-wear properties would be more improved.

Abstract: The formation of nitrogen monoxide in treatment of metals with nitric acid or a mixed acid can be prevented by adding at least one of ammonium peroxodisulfate and hydrogen peroxide to nitric acid or a mixed acid consisting mainly of nitric acid and sulfuric acid.