Abstract: An electrode material (1) includes: a porous support (2); and silver chloride (4) supported on the porous support (2). The porous support (2) is, for example, silica. The silica may be: wet-process silica such as precipitated silica or gelation method silica; dry-process silica; or the like.

Abstract: An electrode material (1) includes: a porous support (2); and silver chloride (4) supported on the porous support (2). The porous support (2) is, for example, silica. The silica may be: wet-process silica such as precipitated silica or gelation method silica; dry-process silica; or the like.

Abstract: A positive electrode active material contains conductive silica and sulfur filled in pores of the conductive silica. The conductive silica is preferably a composite containing silica gel and fine particulate carbon dispersed in the silica gel. The positive electrode includes the aforementioned positive electrode active material. A rechargeable battery includes the aforementioned positive electrode.

Abstract: A composition and a method for producing a composition are provided for negative electrode active materials, a negative electrode, and a nonaqueous electrolyte rechargeable battery, which are capable of improving cycle properties. The composition for negative electrode active materials includes a co-dispersion of a silica gel and a fine particulate carbon; and silicon particles contained in the co-dispersion, and so forth.

Abstract: Porous silica-carbon composites are obtained by mixing fine particulate carbon dispersed in water by a surfactant, alkali metal silicate aqueous solution, and mineral acid so as to produce co-dispersion in which silica hydrosol, produced by reaction of the alkali metal silicate and the mineral acid, and the fine particulate carbon are uniformly dispersed, and gelling silica hydrosol, contained in the co-dispersion, and making the co-dispersion into porous bodies. The porous silica-carbon composites are prepared so as to have specific surface area from 20 to 1000 m2/g, pore volume from 0.3 to 2.0 ml/g, and average pore diameter from 2 to 100 nm.

Abstract: Porous silica-carbon composites are obtained by mixing fine particulate carbon dispersed in water by a surfactant, alkali metal silicate aqueous solution, and mineral acid so as to produce co-dispersion in which silica hydrosol, produced by reaction of the alkali metal silicate and the mineral acid, and the fine particulate carbon are uniformly dispersed, and gelling silica hydrosol, contained in the co-dispersion, and making the co-dispersion into porous bodies. The porous silica-carbon composites are prepared so as to have specific surface area from 20 to 1000 m2/g, pore volume from 0.3 to 2.0 ml/g, and average pore diameter from 2 to 100 nm.