Abstract: A resin composition consisting of: (1) 100 parts by weight of an aromatic polycarbonate resin; (2) 0.008 to 0.13 part by weight of an alkali metal salt of a perfluoroalkylsulfonic acid having a fluoride ion content measured by ion chromatography of 0.2 to 1 ppm in terms of weight based on the weight of component B; and (3) 0.01 to 5 parts by weight of silicone having a Si—H group and a phenyl group. A process of manufacturing the resin composition and a method of preventing the melt dripping during combustion of the resin composition. The flame retardancy of the above aromatic polycarbonate resin composition comprising the fluorine-containing organic metal salt compound is improved.

Abstract: There is provided a direct backlight type liquid crystal display device having high light diffusability, keeping excellent color and having high brightness.

Abstract: A resin composition comprising: (1) 100 parts by weight of an aromatic polycarbonate resin (component A); (2) 0.005 to 0.6 part by weight of a fluorine-containing organic metal salt having a fluoride ion content measured by ion chromatography of 0.2 to 20 ppm in terms of weight (component B); and (3) at least one component selected from the group consisting of a flame retardant (component C), a fatty acid ester (component D), an ultraviolet light absorber (component E), polytetrafluoroethylene having fibril formability (component F), a filler (component G), a silicate mineral (component H) and a titanium dioxide pigment (component I). A process of manufacturing the resin compositon and a method of preventing the melt dripping during combustion of the resin composition. The flame retardancy of the above aromatic polycarbonate resin composition comprising the fluorine-containing organic metal salt compound is improved.

Abstract: The object of the present invention is to provide a polycarbonate resin composition which has excellent transparency and durability against molding heat, which gives a molded article having an excellent mold release property, reduced strains, improved cracking resistance and, preferably, weatherability, and which is particularly suitable for a transparent member for a vehicle, pellets thereof and a molded article thereof, and the present invention provides a polycarbonate resin composition obtained by blending 100 parts by weight of a polycarbonate resin (Component A) and 0.005 to 2 parts by weight of a full ester (Component B) from an aliphatic polyhydric alcohol having 4 to 8 hydroxyl groups and 5 to 30 carbon atoms and an aliphatic carboxylic acid having 10 to 22 carbon atoms, said Component B having a 5% weight loss temperature, measured by TGA (thermogravimetric analysis), of 250 to 360° C. and having an acid value of 4 to 20, pellets thereof and a molded article thereof.

Abstract: A polycarbonate resin composition comprising 100 parts by weight of a polycarbonate resin (component A), 0.01 to 10 parts by weight of at least one ultraviolet light absorber (component B) selected from the group of a specific cyclic imino ester, and 0.01 to 1 part by weight of a fatty acid ester compound (component C) which is an ester of a polyhydric alcohol and an aliphatic carboxylic acid and has a molecular weight of 500 to 2,000 g/mol, as well as molded articles thereof. The polycarbonate resin composition provides molded articles having excellent transparency, color and resistance to ultraviolet radiation, is excellent in heat stability at the time of molding and releasability and fully suppresses the production of a deposit on a metal mold.

Abstract: There is provided a direct backlight type liquid crystal display device having high light diffusability, keeping excellent color and having high brightness.

Abstract: A polycarbonate resin composition comprising 100 parts by weight of a polycarbonate resin (component A), 0.01 to 10 parts by weight of at least one ultraviolet light absorber (component B) selected from the group of a specific cyclic imino ester, and 0.01 to 1 part by weight of a fatty acid ester compound (component C) which is an ester of a polyhydric alcohol and an aliphatic carboxylic acid and has a molecular weight of 500 to 2,000 g/mol, as well as molded articles thereof. The polycarbonate resin composition provides molded articles having excellent transparency, color and resistance to ultraviolet radiation, is excellent in heat stability at the time of molding and releasability and fully suppresses the production of a deposit on a metal mold.

Abstract: The object of the present invention is to provide a polycarbonate resin composition which has excellent transparency and durability against molding heat, which gives a molded article having an excellent mold release property, reduced strains, improved cracking resistance and, preferably, weatherability, and which is particularly suitable for a transparent member for a vehicle, pellets thereof and a molded article thereof, and the present invention provides a polycarbonate resin composition obtained by blending 100 parts by weight of a polycarbonate resin (Component A) and 0.005 to 2 parts by weight of a full ester (Component B) from an aliphatic polyhydric alcohol having 4 to 8 hydroxyl groups and 5 to 30 carbon atoms and an aliphatic carboxylic acid having 10 to 22 carbon atoms, said Component B having a 5% weight loss temperature, measured by TGA (thermogravimetric analysis), of 250 to 360° C. and having an acid value of 4 to 20, pellets thereof and a molded article thereof.