Abstract: A process is provided for producing a foamed article of a thermoplastic resin composition having a relatively thicker solid skin layer exhibiting better appearance without occurrence of a swirl mark and having a foam structure of relatively uniform foam cell size with better foam cell configuration, which is light-weighing and superior in stiffness, in an easy and efficient manner, by causing the resin composition to foam up in a cavity of a mold.

Abstract: A process for producing a foamed article of a thermoplastic resin composition having a relatively thicker solid skin layer exhibiting better appearance without occurrence of swirl mark and having a foam structure of relatively uniform foam cell size with better foam cell configuration, which is light-weighing and superior in the stiffness, in an easy and efficient manner, by causing the said resin composition to foam up in a cavity of a mold, which process comprises

Abstract: A process for preparing a composite foamed molded article according to the invention includes the steps of setting a skin material in the vicinity of an upper mold for stamping-mold kept at a temperature of 10 to 50.degree. C.; feeding a molten polypropylene resin composition for a substrate containing a foaming agent kept at a temperature of not lower than a decomposition temperature of the foaming agent and within the range of 180 to 240.degree. C. onto a surface of a lower mold for stamping-mold kept at a temperature of 30 to 80.degree. C.; closing the mold within 10 seconds after feeding of the composition to clamp the molds at a pressure of 20 to 70 kg/cm.sup.2 ; lifting the upper mold before a thickness of each of hardened layers formed on both surfaces of the composition layer reaches 1.0 mm to open the mold at a distance between the upper mold and lower mold of 1.

Abstract: A process for preparing a two-ply foam molded article, characterized by heating a foamable polyolefin sheet which is in its not yet foamed state to form a foamed polyolefin layer, integrally laminating a fabric on one side of the resulting foamed polyolefin layer which is still in a melted and softened state to form a laminate and simultaneously draw-forming the resulting laminate to shape the two-ply foam molded article.