Abstract: An alloy for biomedical use includes Zr as a main component, Nb the content of which is not less than 0.1% by weight and not greater than 25% by weight, Mo the content of which is not less than 0.1% by weight and not greater than 25% by weight, and Ta the content of which is not less than 0.1% by weight and not greater than 25% by weight. A tensile strength of the alloy is not less than 1000 MPa. A total content of Nb, Mo, and Ta in the alloy is not less than 2% by weight and not greater than 50% by weight. Mass susceptibility of the alloy is not greater than 1.50×10?6 cm3/g. A Young's modulus of the alloy is not greater than 100 GPa. Also disclosed is a medical product including the alloy and a method for producing the alloy.

Abstract: An alloy for biomedical use includes Zr as a main component, Nb the content of which is not less than 0.1% by weight and not greater than 25% by weight, Mo the content of which is not less than 0.1% by weight and not greater than 25% by weight, and Ta the content of which is not less than 0.1% by weight and not greater than 25% by weight. A tensile strength of the alloy is not less than 1000 MPa. A total content of Nb, Mo, and Ta in the alloy is not less than 2% by weight and not greater than 50% by weight. Mass susceptibility of the alloy is not greater than 1.50×10?6 cm3/g. A Young's modulus of the alloy is not greater than 100 GPa. Also disclosed is a medical product including the alloy and a method for producing the alloy.

Abstract: A piston ring having improved scuffing resistance, cracking resistance and fatigue resistance, consists of a high-chromium martensitic stainless steel and a sliding nitriding layer formed on the surface of said steel. The stainless steel consists of C: 0.3 to 1.0%; Cr: 14.0 to 21.0%, N: 0.05 to 0.50%, at least one of Mo, V, W and Nb: 0.03 to 3.0% in total, Si: 0.1 to 1.0%, Mn 0.1 to 1.0%, P: 0.05% or less, S: 0.05% or less, the balance being Fe and unavoidable impurities. The sliding nitriding layer comprises on its surface hard particles mainly consisting of nitrides in a range of from 0.2 to 2.0 ?m of average particle size, 7 ?m or less of the longest diameter, and from 5 to 30% in area ratio.

Abstract: A piston ring having improved scuffing resistance, cracking resistance and fatigue resistance, consists of a high-chromium martensitic stainless steel and a sliding nitriding layer formed on the surface of said steel. The stainless steel consists of C: 0.3 to 1.0%; Cr: 14.0 to 21.0%, N: 0.05 to 0.50%, at least one of Mo, V, W and Nb: 0.03 to 3.0% in total, Si: 0.1 to 1.0%, Mn 0.1 to 1.0%, P: 0.05% or less, S: 0.05% or less, the balance being Fe and unavoidable impurities. The sliding nitriding layer comprises on its surface hard particles mainly consisting of nitrides in a range of from 0.2 to 2.0 &mgr;m of average particle size, 7 &mgr;m or less of the longest diameter, and from 5 to 30% in area ratio.