Abstract: A super-precision rolling bearing includes a first ring having a first raceway, a second ring having a second raceway, and a plurality of rolling elements arranged between the first and second raceways. The first and/or second ring is made of a hardened and tempered nitriding steel core having a first predetermined hardness and a nitrided surface layer coating at least the first raceway and containing nitrides in an amount to give the nitrided steel layer a second predetermined hardness greater than the first predetermined hardness.

Abstract: A bearing component composed of a chromium-molybdenum-vanadium alloyed tool steel is produced by a process that includes: (i) performing a first preheating within a temperature range of 600-650° C., (ii) performing a second preheating within a temperature range of 850-900° C., (iii) austenitizing in vacuum at 1000-1180° C. for 20-40 min, (iv) gas quenching at a minimum of 4-5 bar overpressure, and (v) tempering by performing either a double temper at 520-560° C. for 1.5-2.5 hours in each temper, or a triple temper at 520-560° C. for 0.5-1.5 hours in each temper. The steel alloy may be composed (in mass percent) of 1.32-1.45 C, 0.32-0.50 Si, 0.26-0.48 Mn, 4.0-4.85 Cr, 3.35-3.55 Mo, 3.55-3.85 V, 0-0.13 W, 0-0.20 Ni, 0-0.15 Cu, 0-0.8 Co, 0-0.03 P, and 0-0.03 S, the balance being iron and unavoidable impurities. Mo may be replaced with W or vice versa in a replacement ratio Mo:W of 1:2.