Abstract: A polarizer that can be used for forming a liquid crystal display or an electroluminescent display with less display irregularities and excellent display characteristics is provided. The polarizer contains a dichroic material in a matrix, and its in-plane retardation at a measurement wavelength providing no absorption is in a range of 950 to 1350 nm. The measurement wavelength is preferably a wavelength that the dichroic material provides no absorption, and it is 1000 nm, for example.

Abstract: The present invention provides a method for manufacturing a polarizing film, by which, even when a wide raw film is used, it is possible to obtain a polarizing film that achieves excellent optical characteristics as well as uniformity in in-plane optical characteristics. The method includes the steps of dyeing a polymer film; stretching the dyed film; and drying the film that has undergone the dyeing and stretching steps while conveying the film with rolls. In the drying step, at least two rolls are used as the rolls and the film is dried under a condition that a ratio (R/W) of a distance (R) between the adjacent rolls to an initial width (W) of the polymer film is not less than 0.5 and not more than 4.0.

Abstract: A polarizing film is provided that prevents display unevenness and can form a liquid crystal display and an electroluminescence display that exhibit excellent display characteristics. The polarizing film is produced in the following manner. That is, a hydrophilic polymer film is conveyed by means of a guide roll so as to be impregnated in an aqueous solvent in a swelling bath and is allowed to swell. In this swelling step, at least a first guide roll is arranged in the swelling bath, and when the polymer film is impregnated in and allowed to travel in the aqueous solvent, the polymer film is brought into contact with the first guide roll within a time up to when swelling reaches a saturation state. Further, the polymer film is dyed using a dichroic substance and stretched.

Abstract: A method for producing a multilayer laminated film comprising: laminating a resin film having a moisture percentage of 10% by weight to 60% by weight with a first transparent film and a second transparent film each having a moisture percentage of 0.

Abstract: A method for producing a multilayer laminated film comprising: laminating a resin film having a moisture percentage of 10% by weight to 60% by weight with a first transparent film and a second transparent film each having a moisture percentage of 0.

Abstract: An adhesive for polarizing plate used in order to provide a transparent protective film on at least one surface of a polarizer, comprising a crosslinking agent in the range of more than 30 parts by weight and 46 parts by weight or less relative to 100 parts by weight of a polyvinyl alcohol-based resin having an acetoacetyl group, is excellent in water resistance.

Abstract: An adhesive of the invention for polarizing plates used for forming an adhesive layer in a polarizing plate in which a polarizer and a transparent protective film is are adhering with each other via the adhesive layer, wherein the adhesive for polarizing plates is an aqueous solution containing a polyvinyl alcohol-based resin having an acetoacetyl group and a crosslinking agent, and the aqueous solution has a pH of 4.3 or less. The adhesive of the invention for polarizing plates is good in durability and long in pot life.

Abstract: The present invention provides a method for manufacturing a polarizing film, by which, even when a wide raw film is used, it is possible to obtain a polarizing film that achieves excellent optical characteristics as well as uniformity in in-plane optical characteristics. The method includes the steps of dyeing a polymer film; stretching the dyed film; and drying the film that has undergone the dyeing and stretching steps while conveying the film with rolls. In the drying step, at least two rolls are used as the rolls and the film is dried under a condition that a ratio (R/W) of a distance (R) between the adjacent rolls to an initial width (W) of the polymer film is not less than 0.5 and not more than 4.0.

Abstract: A polarizer that can be used for forming a liquid crystal display or an electroluminescent display with less display irregularities and excellent display characteristics is provided. The polarizer contains a dichroic material in a matrix, and its in-plane retardation at a measurement wavelength providing no absorption is in a range of 950 to 1350 nm. The measurement wavelength is preferably a wavelength that the dichroic material provides no absorption, and it is 1000 nm, for example.

Abstract: A method for producing a multilayer laminated film comprising: laminating a resin film having a moisture percentage of 10% by weight to 60% by weight with a first transparent film and a second transparent film each having a moisture percentage of 0.

Abstract: A method of producing a polarizing plate of the present invention comprises the steps of: bonding a protective film to at least one side of a polarizing film that is produced through at least uniaxial stretching and has an absorption axis in the uniaxial stretching direction, and removing by cutting at least one of the edges of the polarizing film that are substantially parallel to the direction of the absorption axis before the bonding the protective film. The method widen the effective width of the polarizing plate, and a large size polarizing plate was obtained.

Abstract: An adhesive of the invention for polarizing plates used for forming an adhesive layer in a polarizing plate in which a polarizer and a transparent protective film is are adhering with each other via the adhesive layer, wherein the adhesive for polarizing plates is an aqueous solution containing a polyvinyl alcohol-based resin having an acetoacetyl group and a crosslinking agent, and the aqueous solution has a pH of 4.3 or less. The adhesive of the invention for polarizing plates is good in durability and long in pot life.

Abstract: A process for producing a polarizing film including a step of stretching a raw film, wherein the ratio (L/W) of stretching distance (L) to width of initial raw film (W) is from 0.5 to 30.

Abstract: The present invention relates to a method for determining haplotypes or diplotypes of a MDR1 gene targeting the 5? upstream regulatory region of MDR1 gene encoding P-gp, an ABC transporter which is may be expressed in the apical membrane side and may transport a wide range of substrates. By detecting a polymorphism at ?934 and/or ?692, in addition to a position selected from ?2903, ?2410, ?2352, ?1910, ?1717, and ?1325 in a nucleotide sequence of the 5? upstream regulatory region of MDR1 gene, haplotypes or diplotypes of the 5?upstream regulatory region of MDR1 gene may be determinable. The above positions to detect polymorphism are indicated in relation to a first base of ATG start codon which is set to +1. ATG start codon is located in exon 2, and the transcription start site corresponds to ?699 in this numbering system.

Abstract: A polarizer that can be used for forming a liquid crystal display or an electroluminescent display with less display irregularities and excellent display characteristics is provided. The polarizer contains a dichroic material in a matrix, and its in-plane retardation at a measurement wavelength providing no absorption is in a range of 950 to 1350 nm. The measurement wavelength is preferably a wavelength that the dichroic material provides no absorption, and it is 1000 nm, for example.

Abstract: An adhesive for polarizing plate used in order to provide a transparent protective film on at least one surface of a polarizer, comprising a crosslinking agent in the range of more than 30 parts by weight and 46 parts by weight or less relative to 100 parts by weight of a polyvinyl alcohol-based resin having an acetoacetyl group, is excellent in water resistance.

Abstract: A polarizing film is provided that prevents display unevenness and can form a liquid crystal display and an electroluminescence display that exhibit excellent display characteristics. The polarizing film is produced in the following manner. That is, a hydrophilic polymer film is conveyed by means of a guide roll so as to be impregnated in an aqueous solvent in a swelling bath and is allowed to swell. In this swelling step, at least a first guide roll is arranged in the swelling bath, and when the polymer film is impregnated in and allowed to travel in the aqueous solvent, the polymer film is brought into contact with the first guide roll within a time up to when swelling reaches a saturation state. Further, the polymer film is dyed using a dichroic substance and stretched.

Abstract: A process for producing a polarizing film including a step of stretching a raw film, wherein the ratio (L/W) of stretching distance (L) to width of initial raw film (W) is from 0.5 to 30.