Abstract: A measurement data synchronization method for synchronizing, through use of a data analysis apparatus, time series outputted from first through fifth measuring instruments, includes a step ST1 for acquiring first through fifth reference data outputted from the first through fifth measuring instruments when a reference signal including a stationary interval and a rising interval is inputted to the measuring instruments simultaneously, steps ST3-ST5 for generating first through fifth filter processed data by applying median filter processing to the first through fifth reference data to extract the median value in a prescribed duration, a step ST6 for calculating first through fifth rising times as timing information of rising from each of the first through fifth filter processed data, and a step ST7 for synchronizing first through fifth measurement data outputted from the measuring instruments on the basis of the first through fifth rising times.

Abstract: In a method of the present invention for manufacturing a welded clad steel tube, an alloy including a corrosion-resisting or heat-resisting alloy is overlaid on a raw steel tube to manufacture a cold steel tube. Then, a cold or warm working is subjected to the clad steel tube. The clad steel tube is subjected to a heat treatment at a temperature exceeding a recrystallization temperature of the alloy.

Abstract: This invention is of a Cr--Mo steel pipe of a wall thickness of 13 mm or less, containing C: 0.03-0.10 wt %, Si: 0.50-1.00 wt %, Mn: 0.30-0.60 wt %, P.ltoreq.0.007 wt %, S.ltoreq.0.020 wt %, Cr: 1.00-1.50 wt %, Mo: 0.45-0.65 wt %, Al: 0.002-0.010 wt % and N: 0.002-0.010 wt % and the remainder consisting of Fe and unavoidable impurities for which preheating and postheating treatments for the prevention of weld cracking and stress corrosion cracking can be effectively omitted, said steel pipe of this invention being suitable for steam piping applications such as STPA23 used in power generation plants, etc.

Abstract: A Cr-Mo steel pipe having a wall thickness of 5 to 25 mm consisting essentially of 0.03 to 0.10 wt. % C, 0.5 to 1.0 wt. % Si, 0.3 to 0.6 wt. % Mn, 0.02 wt. % or less P, 0.007 wt. % or less S, 1.0 to 1.5 wt. % Cr, 0.45 to 0.65 wt. % Mo, 0.002 to 0.1 wt. % Al, 0.002 to 0.01 wt. % N, and the balance being Fe and unavoidable impurities. In the method of welding the Cr-Mo steel pipe, the Cr-Mo steel pipe is welded by shielded metal arc welding without a preheat treatment and/or a post weld heat treatment.