Abstract: A method for manufacturing a grain-oriented electrical steel sheet according to an aspect of the present invention includes a step of obtaining a hot-rolled steel sheet by carrying out hot rolling on a slab containing a predetermined component composition with a remainder including Fe and impurities, a step of obtaining a hot-rolled annealed sheet by carrying out hot-rolled sheet annealing as necessary, a step of carrying out pickling to obtain a pickled sheet, a step of carrying out cold rolling to obtain a cold-rolled steel sheet, a step of carrying out primary recrystallization annealing, a step of applying an annealing separating agent including MgO to a surface and then carrying out final annealing to obtain a final-annealed sheet, and a step of applying an insulating coating and then carrying out flattening annealing.

Abstract: A method for manufacturing a grain-oriented electrical steel sheet according to an aspect of the present invention includes a step of obtaining a hot-rolled steel sheet by carrying out hot rolling on a slab containing a predetermined component composition with a remainder including Fe and impurities, a step of obtaining a hot-rolled annealed sheet by carrying out hot-rolled sheet annealing as necessary, a step of carrying out pickling to obtain a pickled sheet, a step of carrying out cold rolling to obtain a cold-rolled steel sheet, a step of carrying out primary recrystallization annealing, a step of applying an annealing separating agent including MgO to a surface and then carrying out final annealing to obtain a final-annealed sheet, and a step of applying an insulating coating and then carrying out flattening annealing.

Abstract: Provided is a method of manufacturing a grain-oriented electrical steel sheet including: a heating process of heating a slab having a predetermined chemical composition at T1° C. of 1150° C. to 1300° C., retaining the slab for 5 minutes to 30 hours, lowering the temperature of the slab to T2° C. of T1?50° C. or lower, heating the slab at T3° C. of 1280° C. to 1450° C., and retaining the slab for 5 minutes to 60 minutes; a hot-rolling process of hot-rolling the slab that is heated to obtain a hot-rolled steel sheet; a cold-rolling process; an intermediate annealing process of performing intermediate annealing with respect to the hot-rolled steel sheet at least one time before the cold-rolling process or before a final pass of the cold-rolling process after interrupting the cold-rolling; an annealing separating agent applying process; and a secondary film applying process. In the cold-rolling process, a retention treatment is performed during a plurality of passes.

Abstract: Provided is a method of manufacturing a grain-oriented electrical steel sheet including: a heating process of heating a slab having a predetermined chemical composition at T1° C. of 1150° C. to 1300° C., retaining the slab for 5 minutes to 30 hours, lowering the temperature of the slab to T2° C. of T1?50° C. or lower, heating the slab at T3° C. of 1280° C. to 1450° C., and retaining the slab for 5 minutes to 60 minutes; a hot-rolling process of hot-rolling the slab that is heated to obtain a hot-rolled steel sheet; a cold-rolling process; an intermediate annealing process of performing intermediate annealing with respect to the hot-rolled steel sheet at least one time before the cold-rolling process or before a final pass of the cold-rolling process after interrupting the cold-rolling; an annealing separating agent applying process; and a secondary film applying process. In the cold-rolling process, a retention treatment is performed during a plurality of passes.