Abstract: The creped multi-ply tissue products are durable, smooth and have low levels of Slough. In certain instances, the creped multi-ply tissue products are produced using a creping composition comprising a non-crosslinked latex polymer. The creped multi-ply tissue products may have a geometric mean tensile (GMT) from about 700 to about 1,500 g/3?, a basis weight from about 45 to about 60 gsm and a Slough less than about 2.00 mg, such as from about 0.10 to about 2.00 mg. The inventive tissue products also have good durability, such as a Durability Index from about 10.0 to about 20.0, smooth surfaces, such as a TS750 value from about 15.0 to 40.0 and low stiffness, such as a Stiffness Index less than about 10.0.

Abstract: Disclosed are multi-ply tissue products comprising a non-crosslinked binder that are durable and dispersible. The products generally have a Slosh time less than 2 minutes, such as less than about 60 seconds, such as less than about 45 seconds. Surprisingly, the foregoing Slosh times are achieved despite the tissue products having relatively high cross-machine direction (CD) wet tensile strength, such as greater than about 100 g/3?. Typically, increasing wet tensile strength, particularly wet CD tensile strength, negatively effects dispersability and increases Slosh time. Despite this trend, the present invention surprisingly provides a tissue product having a relatively high degree of wet strength and good dispersability.

Abstract: Disclosed are non-treated, creped tissue webs, and tissue products produced therefrom, having low stiffness and surface lint. The inventive products may be produced by a print creping process adapted to dispose a non-crosslinked latex polymer on at least one of the outer surfaces of the tissue product. The non-crosslinked latex polymer creping composition does not negatively affect stiffness such that the products generally have a Stiffness Index less than about 5.0, such as from about 2.5 to about 5.0.

Abstract: Disclosed are non-treated, creped tissue webs, and tissue products produced therefrom, having low stiffness and surface lint. The inventive products may be produced by a print creping process adapted to dispose a non-crosslinked latex polymer on at least one of the outer surfaces of the tissue product. The non-crosslinked latex polymer creping composition does not negatively affect stiffness such that the products generally have a Stiffness Index less than about 5.0, such as from about 2.5 to about 5.0.

Abstract: Disclosed are multi-ply tissue products comprising a non-crosslinked binder that are durable and dispersible. The products generally have a Slosh time less than 2 minutes, such as less than about 60 seconds, such as less than about 45 seconds. Surprisingly, the foregoing Slosh times are achieved despite the tissue products having relatively high cross-machine direction (CD) wet tensile strength, such as greater than about 100 g/3?. Typically, increasing wet tensile strength, particularly wet CD tensile strength, negatively effects dispersability and increases Slosh time. Despite this trend, the present invention surprisingly provides a tissue product having a relatively high degree of wet strength and good dispersability.

Abstract: Disclosed are multi-ply tissue products comprising a non-crosslinked binder that are durable, smooth and with low levels of Slough. In certain instances the creped tissue product have a geometric mean tensile (GMT) from about 700 to about 1,500 g/3?, a basis weight from about 45 to about 60 gsm and a Slough less than about 2.00 mg, more preferably less than about 1.50 mg, such as from about 0.10 to about 2.00, such as from about 0.25 to about 1.50 mg. The inventive tissue products also have good durability, such as a Durability Index from about 10.0 to about 20.0, smooth surfaces, such as a TS750 value from about 15.0 to 40.0 and low stiffness, such as a Stiffness Index less than about 10.0.

Abstract: Disclosed are multi-ply tissue products comprising a non-crosslinked binder that are durable and dispersible. The products generally have a Slosh time less than 2 minutes, such as less than about 60 seconds, such as less than about 45 seconds. Surprisingly, the foregoing Slosh times are achieved despite the tissue products having relatively high cross-machine direction (CD) wet tensile strength, such as greater than about 100 g/3?. Typically, increasing wet tensile strength, particularly wet CD tensile strength, negatively effects dispersability and increases Slosh time. Despite this trend, the present invention surprisingly provides a tissue product having a relatively high degree of wet strength and good dispersability.

Abstract: Disclosed are multi-ply tissue products comprising a non-crosslinked binder that are durable, smooth and with low levels of Slough. In certain instances the creped tissue product have a geometric mean tensile (GMT) from about 700 to about 1,500 g/3?, a basis weight from about 45 to about 60 gsm and a Slough less than about 2.00 mg, more preferably less than about 1.50 mg, such as from about 0.10 to about 2.00, such as from about 0.25 to about 1.50 mg. The inventive tissue products also have good durability, such as a Durability Index from about 10.0 to about 20.0, smooth surfaces, such as a TS750 value from about 15.0 to 40.0 and low stiffness, such as a Stiffness Index less than about 10.0.

Abstract: Disclosed are multi-ply tissue products comprising a non-crosslinked binder that are durable, smooth and with low levels of Slough. In certain instances the creped tissue product have a geometric mean tensile (GMT) from about 700 to about 1,500 g/3?, a basis weight from about 45 to about 60 gsm and a Slough less than about 2.00 mg, more preferably less than about 1.50 mg, such as from about 0.10 to about 2.00, such as from about 0.25 to about 1.50 mg. The inventive tissue products also have good durability, such as a Durability Index from about 10.0 to about 20.0, smooth surfaces, such as a TS750 value from about 15.0 to 40.0 and low stiffness, such as a Stiffness Index less than about 10.0.

Abstract: Disclosed are multi-ply tissue products comprising a non-crosslinked binder that are durable and dispersible. The products generally have a Slosh time less than 2 minutes, such as less than about 60 seconds, such as less than about 45 seconds. Surprisingly, the foregoing Slosh times are achieved despite the tissue products having relatively high cross-machine direction (CD) wet tensile strength, such as greater than about 100 g/3?. Typically, increasing wet tensile strength, particularly wet CD tensile strength, negatively effects dispersability and increases Slosh time. Despite this trend, the present invention surprisingly provides a tissue product having a relatively high degree of wet strength and good dispersability.

Abstract: Disclosed are multi-ply tissue products comprising a non-crosslinked binder that are durable, smooth and with low levels of Slough. In certain instances the creped tissue product have a geometric mean tensile (GMT) from about 700 to about 1,500 g/3? a basis weight from about 45 to about 60 gsm and a Slough less than about 2.00 mg, more preferably less than about 1.50 mg, such as from about 0.10 to about 2.00, such as from about 0.25 to about 1.50 mg. The inventive tissue products also have good durability, such as a Durability Index from about 10.0 to about 20.0, smooth surfaces, such as a TS750 value from about 15.0 to 40.0 and low stiffness, such as a Stiffness Index less than about 10.0.

Abstract: Disclosed are non-treated, creped tissue webs, and tissue products produced therefrom, having low stiffness and surface lint. The inventive products may be produced by a print creping process adapted to dispose a non-crosslinked latex polymer on at least one of the outer surfaces of the tissue product. The non-crosslinked latex polymer creping composition does not negatively affect stiffness such that the products generally have a Stiffness Index less than about 5.0, such as from about 2.5 to about 5.0.

Abstract: Disclosed are multi-ply tissue products comprising a non-crosslinked binder that are durable and dispersible. The products generally have a Slosh time less than 2 minutes, such as less than about 60 seconds, such as less than about 45 seconds. Surprisingly, the foregoing Slosh times are achieved despite the tissue products having relatively high cross-machine direction (CD) wet tensile strength, such as greater than about 100 g/3?. Typically, increasing wet tensile strength, particularly wet CD tensile strength, negatively effects dispersability and increases Slosh time. Despite this trend, the present invention surprisingly provides a tissue product having a relatively high degree of wet strength and good dispersability.

Abstract: Disclosed are multi-ply tissue products comprising a non-crosslinked binder that are durable, smooth and with low levels of Slough. In certain instances the creped tissue product have a geometric mean tensile (GMT) from about 700 to about 1,500 g/3? a basis weight from about 45 to about 60 gsm and a Slough less than about 2.00 mg, more preferably less than about 1.50 mg, such as from about 0.10 to about 2.00, such as from about 0.25 to about 1.50 mg. The inventive tissue products also have good durability, such as a Durability Index from about 10.0 to about 20.0, smooth surfaces, such as a TS750 value from about 15.0 to 40.0 and low stiffness, such as a Stiffness Index less than about 10.0.

Abstract: Disclosed are multi-ply tissue products comprising a non-crosslinked binder that are durable and dispersible. The products generally have a Slosh time less than 2 minutes, such as less than about 60 seconds, such as less than about 45 seconds. Surprisingly, the foregoing Slosh times are achieved despite the tissue products having relatively high cross-machine direction (CD) wet tensile strength, such as greater than about 100 g/3?. Typically, increasing wet tensile strength, particularly wet CD tensile strength, negatively effects dispersability and increases Slosh time. Despite this trend, the present invention surprisingly provides a tissue product having a relatively high degree of wet strength and good dispersability.

Abstract: A dispersible wet wipe includes a layer of cellulosic fibers. In one embodiment, a first binder is applied in a coating comprising randomly distributed deposits of the binder. A second binder is applied in an intermittent pattern on the surface to define first regions on the surface that include first binder but no second binder and to define second regions on the surface that include both first binder and second binder. The first and second binders can have the same chemical composition. In a second embodiment, a first binder is applied to a web surface in a first pattern, and, after applying the first binder, a second binder is applied to the web surface in a second pattern that is different than the first pattern. In a third embodiment, a binder is applied to a web surface in a pattern, the pattern having first regions and second regions, wherein the add-on level of the binder in the first regions is lower than the add-on level of the binder in the second regions.

Abstract: A dispersible wet wipe includes a layer of cellulosic fibers. In one embodiment, a first binder is applied in a coating N comprising randomly distributed deposits of the binder. A second binder is applied in an intermittent pattern on the surface to define first regions on the surface that include first binder but no second binder and to define second regions on the surface that include both first binder and second binder. The first and second binders can have the same chemical composition. In a second embodiment, a first binder is applied to a web surface in a first pattern, and, after applying the first binder, a second binder is applied to the web surface in a second pattern that is different than the first pattern. In a third embodiment, a binder is applied to a web surface in a pattern, the pattern having first regions and second regions, wherein the add-on level of the binder in the first regions is lower than the add-on level of the binder in the second regions.

Abstract: A method of making a dispersible wet wipe includes providing a web of cellulosic fibers. In one embodiment, a first binder is applied to a web surface in a coating that comprises randomly distributed deposits of the first binder. A second binder is applied an intermittent pattern on the web surface to define first regions on the first surface that include first binder but no second binder and to define second regions on the first surface that include both first binder and second binder. In a second embodiment, a first binder is applied to a web surface in a first pattern, and, after applying the first binder, a second binder is applied to the web surface in a second pattern that is different than the first pattern. In a third embodiment, a binder is applied to a web surface in a pattern, the pattern having first regions and second regions, wherein the add-on level of the binder in the first regions is lower than the add-on level of the binder in the second regions.

Abstract: A dispersible moist wipe generally comprises a nonwoven tissue web having regenerated fibers in an amount of about 10 to about 30 percent by weight and natural fibers in an amount of about 70 to about 90 percent by weight. The regenerated fibers and the natural fibers are hydroentangled such that the web has a geometric mean tensile strength of at least 250 grams per inch and a slosh-box break-up time of less than 155 minutes.