Abstract: Chemorheologically viscosity tailored matrix resin formulations for use in forming prepregs and composite articles are disclosed. These formulations have a specified viscosity profile obtained from a curable matrix resin and an effective amount of a reactive resin curing agent reactive at room temperature and a latent resin curing agent substantially nonreactive at room temperature. The latent resin curing agent is activated upon heating or radiation. The matrix resin formulation is adapted upon formulation to have a viscosity sufficiently low enough to enable the matrix resin to impregnate fibers or broadgoods at room temperature without the necessity for the application of heat or solvent and which, upon standing at room temperature after impregnation into the fibers or broadgoods to form a prepreg composition, rises in viscosity.

Abstract: Composite pressure vessels having improved fiber strength translation of the unidirectional, axial, impregnated strand are obtained by a process in which chemorheologically viscosity tailored matrix resin formulations containing surface-active agents or compounds acting as surface-active agents are employed. The use of chemorheologically viscosity tailored matrix resin formulations containing surface-active agents reduces the strength variation of pressure vessels produced from prepregs of the disclosed matrix resin formulations.

Abstract: Composite pressure vessels having improved fiber strength translation of the unidirectional, axial, impregnated strand or tow strength delivered in tensile strength of hoop fibers of the composite pressure vessel are obtained by a process in which chemorheologically viscosity tailored matrix resin formulations containing surface-active agents or compounds acting as surface-active agents are employed. The use of chemorheologically viscosity tailored matrix resin formulations containing such agents in such a process also reduces the strength variation of pressure vessels produced from prepreg of the matrix resin formulations containing surface-active agents or compounds acting as surface-active agents.

Abstract: Chemorheologically viscosity tailored matrix resin formulation for use in forming prepregs and filament wound composite articles and having a specified viscosity profile comprising a curable matrix resin and an effective amount of a reactive resin curing agent reactive at room temperature and a latent resin curing agent substantially non-reactive at room temperature but activated upon heating or radiation such that the matrix resin formulation is adapted upon formulation to have a viscosity sufficiently low enough to enable the matrix resin to impregnate a filament or fiber at room temperature without the necessity for the application of heat or solvent and which, upon standing at room temperature after impregnation into the fiber or filament to form a prepreg composition, rises in viscosity to a viscosity level sufficiently high to prevent substantially any bleed of the matrix resin from winding tension upon spooling of the prepreg yet of sufficiently low enough viscosity to allow the prepreg to tack and dra

Abstract: Lightweight filament wound composites are provided which comprise fibers in a cured matrix resin. The resin, in its uncured state, comprises an aromatic vinyl hydrocarbon monomer and a chain-extended carboxy-terminated poly(1,2-butadiene) made by reacting a carboxy-terminated poly(1,2-butadiene) and a difunctional compound in an equivalents ratio of difunctional compound/carboxyl of about 0.5/1.