Abstract: A polymerisable dental composite material comprising (i) 60 to 85% by weight of an inorganic filler component comprising at least one tectosilicate and optionally at least one dental glass and/or at least one amorphous metal oxide, (ii) 10 to 40% by weight of a mixture of at least two different urethane(meth)acrylates, (iii) 0.01 to 5% by weight of at least one di-, tri-, tetra- or multi-functional monomer not being a urethane(meth)acrylate, (iv) 0.01 to 10% by weight of at least one initiator, an initiator system and optionally at least one stabiliser and optionally at least one pigment, wherein the total composition of the composite material amounts to 100% by weight, and a polymerised composite material having a flexural strength of greater than or equal to 240 MPa and an elastic modulus of 16 to 20 GPa for the production of indirect dentures.

Abstract: A polymerizable dental composite material comprising (i) 70 to 85% by weight of an inorganic filler component comprising at least one dental glass and optionally at least one amorphous metal oxide, (ii) 10 to 30% by weight of a mixture of at least two different urethane (meth)acrylates, (iii) 0.01 to 5% by weight of at least one di-, tri-, tetra- or multi-functional monomer not being a urethane (meth)acrylate, (iv) 0.01 to 10% by weight of at least one initiator, of an initiator system as well as optionally of at least one stabilizer and optionally of at least one pigment, wherein the total composition of the composite material amounts to 100% by weight, as well as a polymerized composite material having a flexural strength of greater than or equal to 200 MPa and an elastic modulus of 15 to 20 GPa for producing indirect dentures.

Abstract: A polymerisable dental composite material comprising (i) 70 to 85% by weight of an inorganic filler component comprising at least one dental glass and optionally at least one amorphous metal oxide, (ii) 10 to 30% by weight of at least one monomer comprising 1,3-bis(5?-alkyl-3?,8?-dioxo-2?-aza-4?,7?-dioxa-decyl-9?-en)phenyl and/or 1,3-bis(5?,9?-dialkyl-3?,8?-dioxo-2?-aza-4?,7?-dioxa-decyl-9?-en)phenyl, (iii) 0.01 to 5% by weight of at least one di-, tri-, tetra- or multi-functional monomer not being a urethane (meth)acrylate, (iv) 0.01 to 10% by weight of at least one initiator, of an initiator system and optionally of at least one stabilizer and optionally of at least one pigment, wherein the total composition of the composite material amounts to 100% by weight, and a polymerized composite material having a flexural strength of greater than or equal to 190 MPa and an elastic modulus of 12 to 21 GPa for the production of indirect dentures.

Abstract: A polymerisable dental composite material comprising (i) 70 to 85% by weight of an inorganic filler component comprising at least one dental glass and optionally at least one amorphous metal oxide, (ii) 10 to 30% by weight of a mixture of at least two different urethane(meth)acrylates, (iii) 0.01 to 5% by weight of at least one di-, tri-, tetra- or multi-functional monomer not being a urethane(meth)acrylate, (iv) 0.01 to 10% by weight of at least one initiator, of an initiator system and optionally of at least one stabilizer and optionally of at least one pigment, wherein the total composition of the composite material amounts to 100% by weight, as well as a polymerized composite material having a flexural strength of greater than or equal to 200 MPa and an elastic modulus of 15 to 20 GPa for the production of indirect dentures.

Abstract: A polymerisable dental composite material comprising (i) 70 to 85% by weight of an inorganic filler component comprising at least one dental glass and optionally at least one amorphous metal oxide, (ii) 10 to 30% by weight of at least one monomer comprising 1,3-bis(5?-alkyl-3?,8?-dioxo-2?-aza-4?,7?-dioxa-decyl-9?-en)phenyl and/or 1,3-bis(5?,9?-dialkyl-3?,8?-dioxo-2?-aza-4?,7?-dioxa-decyl-9?-en)phenyl, (iii) 0.01 to 5% by weight of at least one di-, tri-, tetra- or multi-functional monomer not being a urethane (meth)acrylate, (iv) 0.01 to 10% by weight of at least one initiator, of an initiator system and optionally of at least one stabilizer and optionally of at least one pigment, wherein the total composition of the composite material amounts to 100% by weight, and a polymerized composite material having a flexural strength of greater than or equal to 190 MPa and an elastic modulus of 12 to 21 GPa for the production of indirect dentures.

Abstract: A polymerisable dental composite material comprising (i) 70 to 85% by weight of an inorganic filler component comprising at least one dental glass and optionally at least one amorphous metal oxide, (ii) 10 to 30% by weight of a mixture of at least two different urethane (meth)acrylates, (iii) 0.01 to 5% by weight of at least one di-, tri-, tetra- or multi-functional monomer not being a urethane (meth)acrylate, (iv) 0.01 to 10% by weight of at least one initiator, of an initiator system and optionally of at least one stabilizer and optionally of at least one pigment, wherein the total composition of the composite material amounts to 100% by weight, as well as a polymerized composite material having a flexural strength of greater than or equal to 200 MPa and an elastic modulus of 15 to 20 GPa for the production of indirect dentures.

Abstract: A polymerisable dental composite material comprising (i) 60 to 85% by weight of an inorganic filler component comprising at least one tectosilicate and optionally at least one dental glass and/or at least one amorphous metal oxide, (ii) 10 to 40% by weight of a mixture of at least two different urethane(meth)acrylates, (iii) 0.01 to 5% by weight of at least one di-, tri-, tetra- or multi-functional monomer not being a urethane(meth)acrylate, (iv) 0.01 to 10% by weight of at least one initiator, an initiator system and optionally at least one stabiliser and optionally at least one pigment, wherein the total composition of the composite material amounts to 100% by weight, and a polymerised composite material having a flexural strength of greater than or equal to 240 MPa and an elastic modulus of 16 to 20 GPa for the production of indirect dentures.

Abstract: A polymerizable dental composite material comprising (i) 70 to 85% by weight of an inorganic filler component comprising at least one dental glass and optionally at least one amorphous metal oxide, (ii) 10 to 30% by weight of a mixture of at least two different urethane (meth)acrylates, (iii) 0.01 to 5% by weight of at least one di-, tri-, tetra- or multi-functional monomer not being a urethane (meth)acrylate, (iv) 0.01 to 10% by weight of at least one initiator, of an initiator system as well as optionally of at least one stabilizer and optionally of at least one pigment, wherein the total composition of the composite material amounts to 100% by weight, as well as a polymerized composite material having a flexural strength of greater than or equal to 200 MPa and an elastic modulus of 15 to 20 GPa for producing indirect dentures.

Abstract: Method for adjusting or improving or optimizing the usage properties of filler(s)-containing, flowable dental material, which involves relating to at least one measuring value representing the tackiness to at least one measuring value representing the texturing or plasticity or consistency. Flowable, usage-optimized, usually non-polymerized dental composites contain, as fillers, at least one glass filler and at least one filler from the group of chipped polymers or pre-polymer fillers based on ground polymer that is pre-polymerized together with inorganic particles, and, as additive(s), at least one compound represented through formula H—Y—Z (I), where: Y=—O—, —S—, —CO—, —OSi(OR1)2—, —OE Z=H, OH, SH, NH2, COOH, COOR2 E=—CnHmOp- R1=H, C1-C4-Alkyl R2=C1-C15-Alkyl, interrupted by one or more O atoms. C2-C14-Alkyl, n=2 bis 5 m=4 bis 11 p=n.

Abstract: Method for adjusting or improving or optimising the usage properties of filler(s)-containing, flowable dental material, which involves relating to at least one measuring value representing the tackiness to at least one measuring value representing the texturing or plasticity or consistency. Flowable, usage-optimised, usually non-polymerised dental composites contain, as fillers, at least one glass filler and at least one filler from the group of chipped polymers or pre-polymer fillers based on ground polymer that is pre-polymerised together with inorganic particles, and, as additive(s), at least one compound represented through formula H—Y—Z (I), where: Y?—O—, —S—, —CO—, —OSi(OR1)2—, —OE Z?H, OH, SH, NH2, COOH, COOR2 E=—CnHmOp- R1?H, C1-C4-Alkyl R2?C1-C15-Alkyl, interrupted by one or more O atoms.

Abstract: Dental composites comprising monomers, crosslinking agents, fillers, and initiators, in which the crosslinking agent comprises more than 50% by weight of the acrylate monomer TCD-DI-HEA, and the cyctotoxicity of the cured composite as determined according to the standard requirements of ISO 10993-5 and DIN EN ISO 7405 is assessed into the category “no cytotoxic potential”.