Abstract: It has been discovered that the properties of sheet or film materials of broad molecular weight distribution ethylene/propylene rubber impact-modified heterophasic copolymer (ICP) can be improved by blending the ICP with a second polyolefin. The second polyolefin may be a syndiotactic polypropylene (sPP), a random copolymer (RCP) of propylene and comonomer (e.g. ethylene and/or butene) made using a Ziegler-Natta or metallocene catalyst, medium density polyethylene (MDPE), linear low density polyethylene (LLDPE), or low crystalline copolymer of propylene/?-olefin. Improvements include, but are not necessarily limited to, reduced motor amps, lower secant modulus, increased dart drop strength, increased gloss, reduced haze, increased elongation to yield, elimination of stress whitening, improved puncture resistance, and decreased seal initiation temperature. This sheet of film materials may be co-extruded with other resins or laminated with other materials after extrusion.

Abstract: It has been discovered that the properties of sheet or film materials of broad molecular weight distribution ethylene/propylene rubber impact-modified heterophasic copolymer (ICP) can be improved by blending the ICP with a second polyolefin. The second polyolefin may be a syndiotactic polypropylene (sPP), a random copolymer (RCP) of propylene and comonomer (e.g. ethylene and/or butene) made using a Ziegler-Natta or metallocene catalyst, medium density polyethylene (MDPE), linear low density polyethylene (LLDPE), or low crystalline copolymer of propylene/?-olefin. Improvements include, but are not necessarily limited to, reduced motor amps, lower secant modulus, increased dart drop strength, increased gloss, reduced haze, increased elongation to yield, elimination of stress whitening, improved puncture resistance, and decreased seal initiation temperature. This sheet of film materials may be co-extruded with other resins or laminated with other materials after extrusion.

Abstract: It has been discovered that the properties of sheet or film materials of broad molecular weight distribution ethylene/propylene rubber impact-modified heterophasic copolymer (ICP) can be improved by blending the ICP with a second polyolefin. The second polyolefin may be a syndiotactic polypropylene (sPP), a random copolymer (RCP) of propylene and comonomer (e.g. ethylene and/or butene) made using a Ziegler-Natta or metallocene catalyst, medium density polyethylene (MDPE), linear low density polyethylene (LLDPE), or low crystalline copolymer of propylene/?-olefin. Improvements include, but are not necessarily limited to, reduced motor amps, lower secant modulus, increased dart drop strength, increased gloss, reduced haze, increased elongation to yield, elimination of stress whitening, improved puncture resistance, and decreased seal initiation temperature. This sheet of film materials may be co-extruded with other resins or laminated with other materials after extrusion.

Abstract: It has been discovered that the properties of sheet or film materials of broad molecular weight distribution ethylene/propylene rubber impact-modified heterophasic copolymer (ICP) can be improved by blending the ICP with a second polyolefin. The second polyolefin may be a syndiotactic polypropylene (sPP), a random copolymer (RCP) of propylene and comonomer (e.g. ethylene and/or butene) made using a Ziegler-Natta or metallocene catalyst, medium density polyethylene (MDPE), linear low density polyethylene (LLDPE), or low crystalline copolymer of propylene/?-olefin. Improvements include, but are not necessarily limited to, reduced motor amps, lower secant modulus, increased dart drop strength, increased gloss, reduced haze, increased elongation to yield, elimination of stress whitening, improved puncture resistance, and decreased seal initiation temperature. This sheet of film materials may be co-extruded with other resins or laminated with other materials after extrusion.

Abstract: It has been discovered that the properties of sheet or film materials of broad molecular weight distribution ethylene/propylene rubber impact-modified heterophasic copolymer (ICP) can be improved by blending the ICP with a second polyolefin. The second polyolefin may be a syndiotactic polypropylene (sPP), a random copolymer (RCP) of propylene and comonomer (e.g. ethylene and/or butene) made using a Ziegler-Natta or metallocene catalyst, medium density polyethylene (MDPE), linear low density polyethylene (LLDPE), or low crystalline copolymer of propylene/?-olefin. Improvements include, but are not necessarily limited to, reduced motor amps, lower secant modulus, increased dart drop strength, increased gloss, reduced haze, increased elongation to yield, elimination of stress whitening, improved puncture resistance, and decreased seal initiation temperature. This sheet of film materials may be co-extruded with other resins or laminated with other materials after extrusion.

Abstract: An improved method of manufacturing blown polyolefin films with increased bubble stability and higher blown film production rates is disclosed. A method in which the amounts and ratios of known antioxidant polymer film additives (phosphites and phenolics) are controlled to provide limited long chain branching (LCB) and greater rheological breadth in a polyethylene melt to improve both processing characteristics and mechanical properties in the resulting film.

Abstract: A method of modifying a polyethylene material is accomplished by providing a polyethylene resin. The initial rheological breadth of the polyethylene resin is determined. The resin is then modified to adjust the rheological breadth of the polyethylene from the initial rheological breadth to a different rheological breadth that corresponds to a desired resin property, such as haze. A method for predicting clarity and rheological breadth properties is also provided, which utilizes a template of measured properties for polyethylene resins.

Abstract: High density polyethylene barrier grade films comprising at least one layer of polymer wherein the polymer comprises a density greater than about 0.955 g/cc and a rheological breadth parameter of greater than about 0.22 are disclosed. Methods for producing such films on a film line with a neck height configuration of greater than about 15 inches are disclosed.

Abstract: A method of modifying a polyethylene material is accomplished by providing a polyethylene resin. The initial rheological breadth of the polyethylene resin is determined. The resin is then modified to adjust the rheological breadth of the polyethylene from the initial rheological breadth to a different rheological breadth that corresponds to a desired resin property, such as haze. A method for predicting clarity and rheological breadth properties is also provided, which utilizes a template of measured properties for polyethylene resins.

Abstract: An improved method of manufacturing blown polyolefin films with increased bubble stability and higher blown film production rates is disclosed. A method in which the amounts and ratios of known antioxidant polymer film additives (phosphites and phenolics) are controlled to provide limited long chain branching (LCB) and greater rheological breadth in a polyethylene melt to improve both processing characteristics and mechanical properties in the resulting film.

Abstract: High density polyethylene barrier grade films comprising at least one layer of polymer wherein the polymer comprises a density greater than about 0.955 g/cc and a rheological breadth parameter of greater than about 0.22 are disclosed. Methods for producing such films on a film line with a neck height configuration of greater than about 15 inches are disclosed.