Abstract: Drill bit insert with a sintered cemented carbide body including a hard phase of tungsten carbide (WC) and a binder phase wherein the cemented carbide comprises 5.0-7.0 wt % Co, 0.10-0.35 wt % Cr, and a Cr/Co weight ratio of 0.015-0.058. The cemented carbide body has a hardness of 1520-1660 Hv30 and a toughness of K1c?10.0 both measured in the bulk at the center of the longitudinal axis through the center of the insert, or ?5 mm from any surface of the insert. The insert further has a surface toughness K1c?12.0 measured at 0.5 mm below the surface of the body in a transverse direction to the longitudinal axis the insert. The invention also relates to a drill bit comprising the insert and the use of such a drill bit for drilling.

Abstract: Drill bit insert with a sintered cemented carbide body including a hard phase of tungsten carbide (WC) and a binder phase wherein the cemented carbide comprises 5.0-7.0 wt % Co, 0.10-0.35 wt % Cr, and a Cr/Co weight ratio of 0.015-0.058. The cemented carbide body has a hardness of 1520-1660 Hv30 and a toughness of K1c?10.0 both measured in the bulk at the center of the longitudinal axis through the center of the insert, or ?5 mm from any surface of the insert. The insert further has a surface toughness K1c?12.0 measured at 0.5 mm below the surface of the body in a transverse direction to the longitudinal axis the insert. The invention also relates to a drill bit comprising the insert and the use of such a drill bit for drilling.

Abstract: Forming coated cemented carbide inserts, particularly useful in fine turning of super alloys. The inserts are characterized by a composition of a cemented carbide of WC, about 4.0 wt-% Co to about 7.0 wt-% Co, about 0.25 wt-% Cr to 0.50 wt-% Cr, and a coercivity (Hc) of about 28 kA/m to about 38 kA/m. The coating comprises a single (Ti1-xSix)N-layer, where x is between about 0.1 and about 0.25, with a crystal structure of NaCl type and a total thickness between about 0.5 ?m and about 2.0 ?m with a strong (200)-texture.

Abstract: Forming coated cemented carbide inserts, particularly useful in fine turning of super alloys. The inserts are characterized by a composition of a cemented carbide of WC, about 4.0 wt-% Co to about 7.0 wt-% Co, about 0.25 wt-% Cr to 0.50 wt-% Cr, and a coercivity (Hc) of about 28 kA/m to about 38 kA/m. The coating comprises a single (Ti1-xSix)N-layer, where x is between about 0.1 and about 0.25, with a crystal structure of NaCl type and a total thickness between about 0.5 ?m and about 2.0 ?m with a strong (200)-texture.

Abstract: Coated cemented carbide inserts, particularly useful in fine turning of super alloys, are disclosed. The inserts are characterized by a composition of a cemented carbide of WC, about 4.0 wt-% Co to about 7.0 wt-% Co, about 0.25 wt-% Cr to 0.50 wt-% Cr, and a coercivity (Hc) of about 28 kA/m to about 38 kA/m. The coating comprises a single (Ti1-xSix)N-layer, where x is between about 0.1 and about 0.25, with a crystal structure of NaCl type and a total thickness between about 0.5 ?m and about 2.0 ?m with a strong (200)-texture.

Abstract: The invention relates to a method of making cemented carbides having surfaces free free of detrimental binder phase layer. This is achieved by the inclusion of controlled amounts of carbonitride in the carbide composition. The invention also relates to the cemented carbides so formed.

Abstract: Coated cemented carbide inserts, particularly useful in fine turning of super alloys, are disclosed. The inserts are characterized by a composition of a cemented carbide of WC, about 4.0 wt-% Co to about 7.0 wt-% Co, about 0.25 wt-% Cr to 0.50 wt-% Cr, and a coercivity (Hc) of about 28 kA/m to about 38 kA/m. The coating comprises a single (Ti1-xSix)N-layer, where x is between about 0.1 and about 0.25, with a crystal structure of NaCl type and a total thickness between about 0.5 ?m and about 2.0 ?m with a strong (200)-texture.

Abstract: The invention relates to a method of making cemented carbides having surfaces free free of detrimental binder phase layer. This is achieved by the inclusion of controlled amounts of carbonitride in the carbide composition. The invention also relates to the cemented carbides so formed.

Abstract: There is disclosed a method of producing, in large volume and at low cost, titanium carbide, nitride and carbonitride whiskers, with preferably submicron diameters, to be used as reinforcing material. The whiskers are suitable for use as a reinforcement material in a wide range of materials, including metals, intermetallics, plastics, ceramics and metallic bonded hard material. Titanium oxide, hydroxide or alkali compounds thereof are mixed with a carbon source with a volatile part which volatiles at temperatures exceeding 500.degree. C. and in an amount to satisfy the stoichiometric requirements of the carbide or nitride. A halogenide salt is used as a volatilization agent for titanium as well as a catalyst able to dissolve Ti plus C and/or N, such as Ni or Co. The reactant powders are blended in some typical manner, e.g., by using a high speed blender so as to intimately mix them.

Abstract: There is disclosed a method of producing whiskers in large volumes and at low cost to be used as reinforcing material. The whiskers are solid solutions between two or more transition metal carbides, nitrides and carbonitrides, (Me.sub.1-X-Y.sub.Me'.sub.X+Y)C.sub.1-Z N.sub.Z, having preferably submicron diameters, where Me' is one or more transition metals other than Me. The whiskers are suitable for use as a reinforcement material in a wide range of materials, including metals, intermetallics, plastics, ceramics and metallic bonded hard material. Transition metal oxides, hydroxides or alkali compounds thereof are mixed with carbon powder. The carbon source is added in an amount to satisfy the stoichiometric requirements of the carbide or nitride. A halogenide salt is used as a volatilization agent for the transition metals and a catalyst such as Ni or Co that is able to dissolve transition metals plus C and/or N. The reactant powders are blended so as to intimately mix them.