Abstract: A sand mold shaping material contains an aggregate comprising inorganic particles, and microcapsules enclosing a binder which causes the aggregate to bind. The binder is a liquid binder that is in a liquid phase at room temperature, and is enclosed in an outer shell comprising a resin that forms the microcapsule. The sand mold shaping material is in a dry state when used to fill a molding die for shaping.

Abstract: A sand mold shaping material contains an aggregate comprising inorganic particles, and microcapsules enclosing a binder which causes the aggregate to bind. The binder is a liquid binder that is in a liquid phase at room temperature, and is enclosed in an outer shell comprising a resin that forms the microcapsule. The sand mold shaping material is in a dry state when used to fill a molding die for shaping.

Abstract: There are disclosed a laser clad valve seat raw-material powder superior in productivity, cladding property, wear resistance and finishing property, and a laser clad valve seat using the same superior in wear resistance. The row-material powder comprises a powder mixture comprising: 80 to 99% by weight of a Cu-based alloy powder comprising 0.5 to 5% by weight of B, 0 to 20% by weight of Ni, 0 to 10% by weight of Fe plus Co, 0 to 5% by weight of Si, 0 to 3% by weight of Al, and the balance Cu and unavoidable impurities; and 1-20% by weight of an Fe or Co based alloy powder having a Vickers hardness of 500 HV or higher and an average particle diameter of 50 to 200 ?m of and comprising 5 to 40% by weight of Mo, 0 to 25% by weight of Cr, 0 to 5% by weight of Si, and the balance Fe or Co and unavoidable impurities.

Abstract: There are disclosed a laser clad valve seat raw-material powder superior in productivity, cladding property, wear resistance and finishing property, and a laser clad valve seat using the same superior in wear resistance. The row-material powder comprises a powder mixture comprising: 80 to 99% by weight of a Cu-based alloy powder comprising 0.5 to 5% by weight of B, 0 to 20% by weight of Ni, 0 to 10% by weight of Fe plus Co, 0 to 5% by weight of Si, 0 to 3% by weight of Al, and the balance Cu and unavoidable impurities; and 1-20% by weight of an Fe or Co based alloy powder having a Vickers hardness of 500HV or higher and an average particle diameter of 50 to 200 ?m of and comprising 5 to 40% by weight of Mo, 0 to 25% by weight of Cr, 0 to 5% by weight of Si, and the balance Fe or Co and unavoidable impurities.

Abstract: A method for heat treating a mold cast product by releasing the product from a mold and hardening the product. Since the mold release is performed when a surface layer of the product held in contact with the mold has a hardening allowing temperature and after it becomes a shell-shaped solidified layer, the product immediately after release from the mold has a heat suitable for hardening. Using this heat, the product is thereafter hardened by means of a cooling agent. As a result, a heating process required for hardening can be omitted, thereby achieving energy conservation.

Abstract: A mold casting process comprises, after pouring of a molten metal into a mold, rapidly cooling that surface layer of a cast product which is in contact with a mold, and releasing the resulting product from the mold when the surface layer thereof has been converted into a shell-like solidified layer. Such process is used for casting a mechanical part blank and apparatus for carrying out the process is provided.

Abstract: A mold casting process comprises, after pouring of a molten metal into a mold, rapidly cooling that surface layer of a cast product which is in contact with a mold, and releasing the resulting product from the mold when the surface layer thereof has been converted into a shell-like solidified layer. Such process is used for casting a mechanical part blank and apparatus for carrying out the process is provided.

Abstract: A mold casting process comprises, after pouring of a molten metal into a mold, rapidly cooling that surface layer of a cast product which is in contact with a mold, and releasing the resulting product from the mold when the surface layer thereof has been converted into a shell-like solidified layer. Such process is used for casting a mechanical part blank and apparatus for carrying out the process is provided.