Abstract: Provided is a moisture absorbent in liquid form that can effectively inhibit oil bleeding after application. The present invention relates to a moisture absorbent in liquid form, which is a liquid composition including a moisture absorbable particle and a binder, wherein (1) the binder includes a two-liquid component type silicone, and (2) a viscosity (20° C.) as the liquid composition is 10 to 300 Pa·s.

Abstract: Provided is a moisture absorbent in liquid form that can effectively inhibit oil bleeding after application. The present invention relates to a moisture absorbent in liquid form, which is a liquid composition including a moisture absorbable particle and a binder, wherein (1) the binder includes a two-liquid component type silicone, and (2) a viscosity (20° C.) as the liquid composition is 10 to 300 Pa·s.

Abstract: A moisture-absorbing sheet including a hygroscopic molded article containing a resin component and a hygroscopic agent, wherein (1) calcium oxide-based particles having a specific surface area of 0.5 m2/g to 20 m2/g and an average particle diameter of 0.5 ?m to 50 ?m are included as the hygroscopic agent; (2) a fibrillated fluororesin is included as the resin component; and (3) the sheet has: (a) a weight increase ratio of 1% or less after being allowed to stand for 2 hours in an atmosphere at a temperature of 20° C. and a relative humidity of 65%; and (b) a weight increase ratio of 5% or more after being allowed to further stand for 36 hours after being allowed to stand for 36 hours in an atmosphere at a temperature of 20° C. and a relative humidity of 65%.

Abstract: A moisture-absorbing sheet including a hygroscopic molded article containing a resin component and a hygroscopic agent, wherein (1) calcium oxide-based particles having a specific surface area of 0.5 m2/g to 20 m2/g and an average particle diameter of 0.5 ?m to 50 ?m are included as the hygroscopic agent; (2) a fibrillated fluororesin is included as the resin component; and (3) the sheet has: (a) a weight increase ratio of 1% or less after being allowed to stand for 2 hours in an atmosphere at a temperature of 20° C. and a relative humidity of 65%; and (b) a weight increase ratio of 5% or more after being allowed to further stand for 36 hours after being allowed to stand for 36 hours in an atmosphere at a temperature of 20° C. and a relative humidity of 65%.