Abstract: A method for manufacturing a Ni-based alloy article which elutes little Ni even when used in a high-temperature water environment for a long period comprises heating the Ni-based alloy in a carbon dioxide-containing atmosphere for a set period of time at an elevated temperature to form an oxide film comprising chromium oxide on a surface thereof. Using carbon dioxide as an oxidizing gas produces an oxide film of generally uniform thickness along a length of the article being treated so that resistance to nickel elution is more uniform over the entire article.

Abstract: To form a chromium oxide film on the inner surface of a Cr containing nickel-base alloy tube inexpensively and uniformly, the Cr containing nickel-base alloy tube is heated in atmospheric gas of carbon dioxide gas and non-oxidation gas to form an oxide film consisting of chromium oxide having a thickness of 0.2 to 1.5 ?m on the inner surface of the Cr containing nickel-base alloy tube. The atmospheric gas may contain oxygen gas of 5 vol % or less and/or water vapor of 7.5 vol % or less.

Abstract: A method for manufacturing a Ni-based alloy article which elutes little Ni even when used in a high-temperature water environment for a long period comprises heating the Ni-based alloy in a carbon dioxide-containing atmosphere for a set period of time at an elevated temperature to form an oxide film comprising chromium oxide on a surface thereof. Using carbon dioxide as an oxidizing gas produces an oxide film of generally uniform thickness along a length of the article being treated so that resistance to nickel elution is more uniform over the entire article.

Abstract: A method of producing an iron-based dispersion-strengthened alloy tube (2-1) by utilizing a rolling machine having grooved rolls (5, 5-1) and a mandrel (9)for forming the tube (2-1) from a raw rolling tube (2). In the method, a length of contact between a rolling surface (6, 6-1) of a caliber formed by the grooved rolls and an outer circumference of the rolling tube is set to be 0.9 times or more of a circumferential length of the rolling tube over the entire area of the rolling region. It is preferred that the method be performed by a Pilger type rolling machine.