Abstract: A fluororesin which does not cause cone break, when used for insulating a core wire having a diameter of 0.05 to 0.07 mm under the conditions of a resin temperature of 320 to 370° C., a drawdown rate [DDR] of 80 to 120, a draw rate balance [DRB] of 1.0, a wire coating speed of 700 feet/minute and an insulating thickness of 30 to 50 ?m.

Abstract: A lubrication part serving as a bearing metal is provided in a scroll compressor at a sliding part between a cylindrical part of a slide busing and an extension of a movable scroll. An inner periphery of the lubrication part is formed so that its iron substrate is given a surface roughness Ra of 3.7 ?m and a resin layer containing FEP and PTFE is then provided on the roughened substrate surface.

Abstract: It is an object of the present invention to provide a fluororesin excellent in thin wall forming ability and capable of forming electric wire insulatings having good flame retardancy, thermal stability and electrical characteristics. The present invention relates to a fluororesin which does not cause cone break, when used for insulating a core wire having a diameter of 0.05 to 0.07 mm under the conditions of a resin temperature of 320 to 370° C., a drawdown rate [DDR] of 80 to 120, a draw rate balance [DRB] of 1.0, a wire coating speed of 700 feet/minute and a insulating thickness of 30 to 50 ?m.

Abstract: A composite papyraceous material comprising a fibrous polytetrafluoroethylene (in particular, fibrous powder thereof) and fibrous polyimide.