Abstract: To provide a polyester resin for an antifouling coating material that has improved storage stability while maintaining low VOC, thereby allowing preparation in a one-pack form, and that allows increased curability to be achieved and can provide a satisfactory antifouling property and coating property for prolonged periods, as well as a method for producing it, and an antifouling coating material composition. The polyester resin for an antifouling coating material is obtained by reacting a (a) trihydric or greater alcohol, a (b) dibasic acid or its anhydride and a (c) divalent alcohol, and then further reacting with an (d) alicyclic dibasic acid or its anhydride.

Abstract: A urethane resin composition obtained by a method comprising the steps of: melt mixing an isocyanate (B), an antioxidant (C), a release agent (D) and a dispersing agent (E) to obtain a molten mixture, and mixing the molten mixture and a polyol (A): wherein the release agent (D) is a compound represented by the following formula (1): [Chemical Formula 1] R1—COOH??(1) the dispersing agent (E) is a compound represented by the following formula (2) having a weight-average molecular weight Mw of no greater than 16000: and the content of the dispersing agent (E) in the urethane resin composition is 0.1 to 5.0 wt %.

Abstract: A urethane (meth)acrylate composition includes a product of a reaction of a polyester polyol made from a polycarboxylic acid and a polyhydric alcohol, a polyisocyanate, and an active hydrogen-containing (meth)acrylate. Part of the polyhydric alcohol is a diol having a straight chain of 3 to 7 carbon atoms and a side chain on the straight chain. The polyisocyanate includes at least one of hexamethylene diisocyanate, diphenylmethane diisocyanate, hydrogenated diphenylmethane diisocyanate, and tetramethylene diisocyanate.