Abstract: This ferritic stainless steel contains, by mass %, C: 0.001% to 0.030%; Si: 0.01% to 1.00%. Mn: 0.01% to 2.00%, P: 0.050% or less, S: 0.0100% or less, Cr: 11.0% to 30.0%, Mo: 0.01% to 3.00%, Ti: 0.001% to 0.050%, Al: 0.001% to 0.030%, Nb: 0.010% to 1.000%, and N: 0.050% or less, with a remainder being Fe and inevitable impurities, wherein an amount of Al, an amount of Ti, and an amount of Si (mass %) satisfy Al/Ti?8.4Si-0.78.

Abstract: This ferritic stainless steel sheet contains, in terms of % by mass, 0.02% or less of C, 0.02% or less of N, 0.10% to 0.60% of Si, 0.10% to 0.80% of Mn, 15.0% to 21.0% of Cr, more than 2.00% to 3.50% or less of Cu, 0.30% to 0.80% of Nb, 1.00% to 2.50% of Mo, and 0.0003% to 0.0030% of B, with a remainder being Fe and unavoidable impurities, wherein a maximum particle size of ?-Cu that is present in a structure is 20 nm to 200 nm.

Abstract: Ferritic stainless steel hot rolled sheet and steel strip excellent in toughness and corrosion resistance which have a predetermined chemical composition, have a Charpy impact value at 0° C. of 10 J/cm2 or more, and have a thickness of 5.0 to 9.0 mm.

Abstract: This ferritic stainless steel contains, by mass %, C: 0.001% to 0.030%; Si: 0.01% to 1.00%. Mn: 0.01% to 2.00%, P: 0.050% or less, S: 0.0100% or less, Cr: 11.0% to 30.0%, Mo: 0.01% to 3.00%, Ti: 0.001% to 0.050%, Al: 0.001% to 0.030%, Nb: 0.010% to 1.000%, and N: 0.050% or less, with a remainder being Fe and inevitable impurities, wherein an amount of Al, an amount of Ti, and an amount of Si (mass %) satisfy Al/Ti?8.4Si-0.78.

Abstract: This hot-rolled ferritic stainless steel sheet has a steel composition containing, in terms of % by mass: 0.02% or less of C; 0.02% or less of N; 0.1% to 1.5% of Si; 1.5% or less of Mn; 0.035% or less of P; 0.010% or less of S; 1.5% or less of Ni; 10% to 20% of Cr; 1.0% to 3.0% of Cu; 0.08% to 0.30% of Ti; and 0.3% or less of Al, with the balance being Fe and unavoidable impurities, and the hot-rolled ferritic stainless steel sheet has a Vickers hardness of less than 235 Hv.

Abstract: To provide a ferritic stainless steel sheet which has high scale spalling even at a high temperature around 1000° C. Provided is a ferritic stainless steel sheet having excellent Mn-containing oxide film-forming ability and scale spalling ability, containing, in terms of mass %: C: 0.001 to 0.020%, N: 0.001 to 0.020%, Si: 0.10 to 0.40%, Mn: 0.20 to 1.00%, Cr: 16.0 to 20.0%, Nb: 0.30 to 0.80%, Mo: 1.80 to 2.40%, W: 0.05 to 1.40%, Cu: 1.00 to 2.50%, and B: 0.0003 to 0.0030%, in which the above-mentioned components are contained satisfying the formula (1) below, and the balance is composed of Fe and inevitable impurities. At least one of N, Al, V, Mg, Sn, Co, Zr, Hf, and Ta may be added in a predetermined content range.

Abstract: To provide a ferritic stainless steel sheet which has high scale spalling even at a high temperature around 1000° C. Provided is a ferritic stainless steel sheet having excellent Mn-containing oxide film-forming ability and scale spalling ability, containing, in terms of mass %: C: 0.001 to 0.020%, N: 0.001 to 0.020%, Si: 0.10 to 0.40%, Mn: 0.20 to 1.00%, Cr: 16.0 to 20.0%, Nb: 0.30 to 0.80%, Mo: 1.80 to 2.40%, W: 0.05 to 1.40%, Cu: 1.00 to 2.50%, and B: 0.0003 to 0.0030%, in which the above-mentioned components are contained satisfying the formula (1) below, and the balance is composed of Fe and inevitable impurities. At least one of N, Al, V, Mg, Sn, Co, Zr, Hf, and Ta may be added in a predetermined content range.

Abstract: This ferritic stainless steel contains, by mass %, C: 0.001% to 0.030%; Si: 0.01% to 1.00%, Mn: 0.01% to 2.00%, P: 0.050% or less, S: 0.0100% or less, Cr: 11.0% to 30.0%, Mo: 0.01% to 3.00%, Ti: 0.001% to 0.050%, Al: 0.001% to 0.030%, Nb: 0.010% to 1.000%, and N: 0.050% or less, with a remainder being Fe and inevitable impurities, wherein an amount of Al, an amount of Ti, and an amount of Si (mass %) satisfy Al/Ti?8.4Si?0.78.

Abstract: This hot-rolled ferritic stainless steel sheet has a steel composition containing, in terms of % by mass: 0.02% or less of C; 0.02% or less of N; 0.1% to 1.5% of Si; 1.5% or less of Mn; 0.035% or less of P; 0.010% or less of S; 1.5% or less of Ni; 10% to 20% of Cr; 1.0% to 3.0% of Cu; 0.08% to 0.30% of Ti; and 0.3% or less of Al, with the balance being Fe and unavoidable impurities, and the hot-rolled ferritic stainless steel sheet has a Vickers hardness of less than 235 Hv.

Abstract: Ferritic stainless steel hot rolled sheet and steel strip excellent in toughness and corrosion resistance which have a predetermined chemical composition, have a Charpy impact value at 0° C. of 10 J/cm2 or more, and have a thickness of 5.0 to 9.0 mm.

Abstract: This hot-rolled ferritic stainless steel sheet has a steel composition containing, in terms of % by mass: 0.02% or less of C; 0.02% or less of N; 0.1% to 1.5% of Si; 1.5% or less of Mn; 0.035% or less of P; 0.010% or less of S; 1.5% or less of Ni; 10% to 20% of Cr; 1.0% to 3.0% of Cu; 0.08% to 0.30% of Ti; and 0.3% or less of Al, with the balance being Fe and unavoidable impurities, and the hot-rolled ferritic stainless steel sheet has a Vickers hardness of less than 235 Hv.

Abstract: Ferritic stainless steel sheet which has a high oxidation resistance and scale spallation resistance even at a high temperature near 1000° C., characterized by containing C: 0.020% or less, N: 0.020% or less, Si: over 0.10 to 0.35%, Mn: 0.10 to 0.60%, Cr: 16.5 to 20.0%, Nb: 0.30 to 0.80%, Mo: over 2.50 to 3.50%, and Cu: 1.00 to 2.50%, having an amount of increase of oxidation after a continuous oxidation test in the air at 1000° C. for 200 hours of 4.0 mg/cm2 or less, and having an amount of scale spallation of 1.0 mg/cm2 or less.

Abstract: This ferritic stainless steel sheet contains, in terms of % by mass, 0.02% or less of C, 0.02% or less of N, 0.10% to 0.60% of Si, 0.10% to 0.80% of Mn, 15.0% to 21.0% of Cr, more than 2.00% to 3.50% or less of Cu, 0.30% to 0.80% of Nb, 1.00% to 2.50% of Mo, and 0.0003% to 0.0030% of B, with a remainder being Fe and unavoidable impurities, wherein a maximum particle size of ?-Cu that is present in a structure is 20 nm to 200 nm.

Abstract: Ferritic stainless steel sheet for an exhaust part which has little deterioration in strength even if undergoing long term heat history and is low in cost, excellent in heat resistance and workability characterized by containing, characterized by containing, by mass %, C: less than 0.010%, N: 0.020% or less, Si: over 0.1% to 2.0%, Mn: 2.0% or less, Cr: 12.0 to 25.0%, Cu: over 0.9 to 2%, Ti: 0.05 to 0.3%, Nb: 0.001 to 0.1%, Al: 1.0% or less, and B: 0.0003 to 0.003%, having a Cu/(Ti+Nb) of 5 or more, and having a balance of Fe and unavoidable impurities.

Abstract: To provide a ferritic stainless steel sheet which has high scale spalling even at a high temperature around 1000° C. Provided is a ferritic stainless steel sheet having excellent Mn-containing oxide film-forming ability and scale spalling ability, containing, in terms of mass %: C: 0.001 to 0.020%, N: 0.001 to 0.020%, Si: 0.10 to 0.40%, Mn: 0.20 to 1.00%, Cr: 16.0 to 20.0%, Nb: 0.30 to 0.80%, Mo: 1.80 to 2.40%, W: 0.05 to 1.40%, Cu: 1.00 to 2.50%, and B: 0.0003 to 0.0030%, in which the above-mentioned components are contained satisfying the formula (1) below, and the balance is composed of Fe and inevitable impurities. At least one of N, Al, V, Mg, Sn, Co, Zr, Hf, and Ta may be added in a predetermined content range.

Abstract: The present invention provides ferritic stainless steel sheet which is excellent in heat resistance at 950° C. and workability at ordinary temperature, that is, ferritic stainless steel sheet excellent in heat resistance and workability which is characterized by containing, by mass %, C: 0.02% or less, N: 0.02% or less, Si: over 0.1 to 1.0%, Mn: 0.5% or less, P: 0.020 to 0.10%, Cr: 13.0 to 20.0%, Nb: 0.5 to 1.0%, Cu: 1.0 to 3.0%, Mo: 1.5 to 3.5%, W: 2.0% or less, B: 0.0001 to 0.0010%, and Al: 0.01 to 1.0% and having a balance of Fe and unavoidable impurities, where Mo+W is made 2.0 to 3.5%.

Abstract: This hot-rolled ferritic stainless steel sheet has a steel composition containing, in terms of % by mass: 0.02% or less of C; 0.02% or less of N; 0.1% to 1.5% of Si; 1.5% or less of Mn; 0.035% or less of P; 0.010% or less of S; 1.5% or less of Ni; 10% to 20% of Cr; 1.0% to 3.0% of Cu; 0.08% to 0.30% of Ti; and 0.3% or less of Al, with the balance being Fe and unavoidable impurities, and the hot-rolled ferritic stainless steel sheet has a Vickers hardness of less than 235 Hv.

Abstract: A heat-resistant ferritic stainless steel sheet having excellent oxidation resistance while being low in cost and optimal for use in exhaust system components, wherein mass % falls within the following ranges: C: 0.015% or less, N: 0.020% or less, P: 0.04% or less, S: 0.001% or less, Si: 0.3-1.5% or less, Mn: 0.3-0.7% or less, Cr: 11.0-17.0%, Cu: 0.8-1.5%, Ni: 0.05-1.0%, V: 0.5% or less, Al: over 0.01 up to 0.1%, Ti: 10(C+N) to 0.3%. Also, the element content of the elements in the ferritic stainless steel sheet having excellent oxidation and thermal resistance has been mutually adjusted in a manner such that the value of ? defined in formula (1) is 35 or less. ?=23[% Ni]+9[% Cu]+7[% Mn]?11.5[% Cr]?11.

Abstract: Ferritic stainless steel sheet for an exhaust part which has little deterioration in strength even if undergoing long term heat history and is low in cost, excellent in heat resistance and workability characterized by containing, characterized by containing, by mass %, C: less than 0.010%, N: 0.020% or less, Si: over 0.1% to 2.0%, Mn: 2.0% or less, Cr: 12.0 to 25.0%, Cu: over 0.9 to 2%, Ti: 0.05 to 0.3%, Nb: 0.001 to 0.1%, Al: 1.0% or less, and B: 0.0003 to 0.003%, having a Cu/(Ti+Nb) of 5 or more, and having a balance of Fe and unavoidable impurities.

Abstract: Ferritic stainless steel sheet which has a high oxidation resistance and scale spallation resistance even at a high temperature near 1000° C., characterized by containing C: 0.020% or less, N: 0.020% or less, Si: over 0.10 to 0.35%, Mn: 0.10 to 0.60%, Cr: 16.5 to 20.0%, Nb: 0.30 to 0.80%, Mo: over 2.50 to 3.50%, and Cu: 1.00 to 2.50%, having an amount of increase of oxidation after a continuous oxidation test in the air at 1000° C. for 200 hours of 4.0 mg/cm2 or less, and having an amount of scale spallation of 1.0 mg/cm2 or less.