Abstract: A conductive polymer dispersion is provided which is capable of easily forming a conductive coating film having both excellent water resistance and excellent solvent resistance. The conductive polymer dispersion of the present invention includes a ?-conjugated conductive polymer, a polyanion, a polyester resin having an alkali metal salt of an acid group, and a glycidyl group-containing acrylic resin. In the conductive polymer dispersion, the ratio (?/?) of total mass ? of the polyester resin and the glycidyl group-containing acrylic resin to total mass ? of the ?-conjugated conductive polymer and the polyanion is in a range of 6.90 to 62.5.

Abstract: A conductive polymer dispersion is provided which is capable of easily forming a conductive coating film having both excellent water resistance and excellent solvent resistance. The conductive polymer dispersion of the present invention includes a ?-conjugated conductive polymer, a polyanion, a polyester resin having an alkali metal salt of an acid group, and a glycidyl group-containing acrylic resin. In the conductive polymer dispersion, the ratio (?/?) of total mass ? of the polyester resin and the glycidyl group-containing acrylic resin to total mass ? of the ?-conjugated conductive polymer and the polyanion is in a range of 6.90 to 62.5.

Abstract: The present invention provides a method for manufacturing a film for a film capacitor in which a film can be prepared by melt extrusion molding in a thin film having a thickness of 10 ?m or less and in which a cost can be cut by simplifying a manufacturing step thereof and a film for a film capacitor. It is a method for manufacturing a film for a film capacitor comprising the steps of charging a melt extrusion molding equipment 10 with a molding material 1 to mold a film 20 for a film capacitor by extruding from a dice 12, interposing the above extruded and molded film 20 for a film capacitor between a pressing roll 31 and a metal roll 32 to cool it and winding up the cooled film 20 for a film capacitor having a thickness of 10 ?m or less in order on a winding tube 41 of a winding device 40, wherein the molding material 1 is prepared by adding a fluorocarbon resin to a PEI resin having a glass transition point of 200° C.