Abstract: The invention discloses a nickel based brazing filler metal in form of an alloy containing or consisting of between 20 wt % and 35 wt % chromium, between 7 wt % and 15 wt % iron and between 2.5 wt % and 9 wt % silicon, between 0 wt % and 15 wt % molybdenum, unavoidable impurities and the balance being nickel. The solidus temperature of the brazing filler shall be between 1140° C. and 1240° C. The brazing filler metal is suitable for production of catalytic converters and heat exchangers. The invention also discloses a brazing method.

Abstract: An iron-chromium based brazing filler metal is provided which exhibits an excellent wetting behavior on a stainless steel base material. The brazing filler metal produces a brazed joint which exhibits high strength and good corrosion resistance. The brazing filler metal is suitable for brazing stainless steel and other materials where corrosion resistance and high strength is required. Typical examples of applications are heat exchangers and catalytic converters. The iron-chromium based brazing filler metal powder according to the invention comprises: between 11 and 35 wt % chromium, between 0 and 30 wt % nickel, between 2 and 20 wt % copper, between 2 and 6 wt % silicon, between 4 and 8 wt % phosporous, between 0-10 wt % manganese, and at least 20 wt % iron.

Abstract: A filter comprising a porous sintered stainless steel is provided. The filter includes 10-30% chromium, 5-25% nickel, 0.5-3% manganese; 1-4% silicon, and 0-3% molybdenum with the remainder being iron and inevitable impurities. The sintered steel has a density less than 80% of full density. The use of a stainless steel powder for the preparation of a filter having improved permeability at high temperatures also is described.

Abstract: The invention concerns a stainless steel powder comprising at least 10% chromium by weight. The powder further comprises vanadium in an amount of at least 4 times the amount of carbon and nitrogen. Preferably the steel powder comprises 10-30% chromium, 0.1-1% vanadium, 0.5-1.5% silicon, at least 0.1% carbon and at least 0.07% nitrogen. The invention also concerns a powder metallurgical composition containing said steel powder, a process for preparing and a compacted and sintered part made of said composition.

Abstract: The present invention concerns a powder metal composition for producing powder metal components comprising a Co-based pre-alloyed powder, with irregularly shaped particles comprising at least 15% by weight Cr and less than 0.3% by weight C, admixed with graphite. The invention also concerns a method for producing PM components by pressing of articles to shape from the powder metal composition according to the invention and sintering them.

Abstract: The invention concerns a method of improving the dynamic properties of compacted and sintered products having a density between 6.8 and 7.6 g/cm3, preferably between 7.0 and 7.4 g/cm3. According to this method an iron based powder, graphite and a solid particular lubricant having a vaporizing temperature less the sintering temperature, preferably less than about 800° C. is compacted and sintered and the maximum particle size of the lubricant is selected so that the largest pores of a compacted and sintered product prepared from the composition are equal to or less than the largest pores obtained in a compacted and sintered product prepared from the composition without lubricant. The invention also concerns composition of an iron based powder, graphite and a solid particular lubricant having a vaporizing temperature less the sintering temperature, preferably less than about 800° C. and a maximum particle size less than about 0.

Abstract: The present invention concerns compacted and optionally presintered bodies, which are prepared from metal powders and which have densified surfaces, obtained by shot peening or rolling.