Abstract: Method for producing molybdenum metal powder. The invention includes introducing a supply of ammonium molybdate precursor material into a furnace in a first direction and introducing a reducing gas into a cooling zone in a second direction opposite to the first direction. The ammonium molybdate precursor material is heated at an initial temperature in the presence of the reducing gas to produce an intermediate product that is heated at a final temperature in the presence of the reducing gas, thereby creating the molybdenum metal powder comprising particles having a surface area to mass ratio of between about 1 m2/g and about 4 m2/g, as determined by BET analysis, and a flowability of between about 29 s/50 g and 86 s/50 g as determined by a Hall Flowmeter. The molybdenum metal powder is moved through the cooling zone.

Abstract: Molybdenum metal powder. Molybdenum metal powder includes molybdenum metal particles having a surface-area-to-mass ratio of between about 1 m2/g and about 4 m2/g, as determined by BET analysis, and a flowability of between about 29 s/50 g and 86 s/50 g as determined by a Hall Flowmeter.

Abstract: Densified molybdenum metal powder. Densified molybdenum metal powder has substantially generally spherical particles, surface-area-to-mass ratio of no more than about 0.5 m2/g as determined by BET analysis, and a flowability greater than about 32 s/50 g as determined by a Hall Flowmeter.

Abstract: Molybdenum metal powder has surface-area-to-mass-ratios in a range of between about 1.0 meters2/gram (m2/g) and about 3.0 m2/g, as determined by BET analysis, in combination with a particle size wherein at least 30% of the particles are larger than a size +100 standard Tyler mesh sieve. A method for producing molybdenum metal powder includes providing a supply of ammonium molybdate and a reducing gas; causing an exothermic reaction between the ammonium molybdate and the reducing gas at a first temperature to produce an intermediate reaction product and a supplemental reducing gas; causing an endothermic reaction between the intermediate reaction product and the reducing gas at a final temperature to produce the molybdenum metal powder.

Abstract: Densified molybdenum metal powder. Densified molybdenum metal powder has substantially generally spherical particles, surface-area-to-mass ratio of no more than about 0.5 m2/g as determined by BET analysis, and a flowability greater than about 32 s/50 g as determined by a Hall Flowmeter.

Abstract: Densified molybdenum metal powder and method for producing same. Densified molybdenum powder has substantially generally spherical particles, surface area to mass ratio of no more than about 0.5 m2/g as determined by BET analysis, and a flowability greater than about 32 s/50g as determined by a Hall Flowmeter. A method for producing densified molybdenum metal powder includes providing a supply of precursor material of molybdenum metal powder particles reduced from ammonium molybdate; providing a supply of reducing gas; densifying the precursor material in the presence of the reducing gas; and producing the densified molybdenum metal powder.

Abstract: Molybdenum metal powder. Molybdenum metal powder includes molybdenum metal particles having a surface-area-to-mass ratio of between about 1 m2/g and about 4 m2/g, as determined by BET analysis, and a flowability of between about 29 s/50 g and 86 s/50 g as determined by a Hall Flowmeter.

Abstract: Method for producing molybdenum metal powder. The invention includes introducing a supply of ammonium molybdate precursor material into a furnace in a first direction and introducing a reducing gas into a cooling zone in a second direction opposite to the first direction. The ammonium molybdate precursor material is heated at an initial temperature in the presence of the reducing gas to produce an intermediate product that is heated at a final temperature in the presence of the reducing gas, thereby creating the molybdenum metal powder comprising particles having a surface area to mass ratio of between about 1 m2/g and about 4 m2/g, as determined by BET analysis, and a flowability of between about 29 s/50 g and 86 s/50 g as determined by a Hall Flowmeter. The molybdenum metal powder is moved through the cooling zone.

Abstract: Molybdenum metal powder has surface-area-to-mass-ratios in a range of between about 1.0 meters2/gram (m2/g) and about 3.0 m2/g, as determined by BET analysis, in combination with a particle size wherein at least 30% of the particles are larger than a size +100 standard Tyler mesh sieve. A method for producing molybdenum metal powder includes providing a supply of ammonium molybdate and a reducing gas; causing an exothermic reaction between the ammonium molybdate and the reducing gas at a first temperature to produce an intermediate reaction product and a supplemental reducing gas; causing an endothermic reaction between the intermediate reaction product and the reducing gas at a final temperature to produce the molybdenum metal powder.

Abstract: Molybdenum metal powder, and method for production thereof. Molybdenum metal powder has surface-area-to-mass-ratios in a range of between about 1.0 meters2/gram (m2/g) and about 3.0 m2/g, as determined by BET analysis, in combination with a particle size wherein at least 30% of the particles have a particle size larger than a size +100 standard Tyler mesh sieve. In addition, molybdenum metal powder 10 may be further distinguished by flowability in a range of between about 29 seconds/50 grams (s/50 g) and about 64 s/50 g, as determined by a Hall Flowmeter. A method of producing molybdenum powder may comprise providing a supply of ammonium molybdate, heating the ammonium molybdate at an initial temperature in the presence of a reducing gas to produce an intermediate product, and heating the intermediate product at a final temperature in the presence of the reducing gas, producing molybdenum metal powder.