Abstract: A porous shaped catalyst support body comprising at least 85% by weight of alpha-alumina, wherein the support has a total pore volume in the range from 0.5 to 2.0 mL/g as determined by mercury porosimetry, and a pore structure characterized by a geometric tortuosity ? in the range from 1.0 to 2.0; and an effective diffusion parameter ? in the range from 0.060 to 1.0; wherein geometric tortuosity ? and effective diffusion parameter ? are determined by image analysis algorithms from computer-assisted 3D reconstructions of focused ion beam scanning electron microscope analyses. The structure of the support has a high total pore volume, such that impregnation with a large amount of silver is possible, while the surface area is kept sufficiently high in order to assure optimal dispersion of the catalytically active species, especially metal species. The support has a pore structure that leads to a maximum rate of mass transfer within the support.

Abstract: A process for producing a porous alpha-alumina catalyst support, comprising i) preparing a precursor material comprising, based on inorganic solids content, at least 50 wt.-% of a transition alumina having a loose bulk density of at most 600 g/L, a pore volume of at least 0.6 mL/g and a median pore diameter of at least 15 nm; and at most 30 wt.-% of an alumina hydrate; ii) forming the precursor material into shaped bodies; and iii) calcining the shaped bodies to obtain the porous alpha-alumina catalyst support. The catalyst support has a high overall pore volume, thus allowing for impregnation with a high amount of silver, while keeping its surface area sufficiently large so as to provide optimal dispersion of catalytically active species, in particular metal species. The invention further relates to a shaped catalyst body for producing ethylene oxide by gas-phase oxidation of ethylene, comprising at least 15 wt.

Abstract: A shaped catalyst body for producing ethylene oxide by gas-phase oxidation of ethylene, having a BET surface area in the range of 2 to 20 m2/g and comprising silver and a rhenium promotor deposited on a porous alpha-alumina catalyst support, characterized in that the support has a calcination history of at least 1460° C. The catalyst support has a high surface area and little ethylene oxide isomerization and/or decomposition activity. The invention further relates to a porous alpha-alumina catalyst support having a BET surface area of 1.7 to 10 m2/g, the porous alpha-alumina catalyst support being obtainable by a) preparing a precursor material comprising a transition alumina and/or an alumina hydrate; b) forming the precursor material into shaped bodies; and c) calcining the shaped bodies at a temperature of 1460° C. to 1700° C. to obtain the porous alpha-alumina support.

Abstract: A tableted catalyst support, characterized by an alpha-alumina content of at least 85 wt.-%, a pore volume of at least 0.40 mL/g, as determined by mercury porosimetry, and a BET surface area of 0.5 to 5.0 m2/g. The tableted catalyst support is an alpha-alumina catalyst support obtained with high geometrical precision and displaying a high overall pore volume, thus allowing for impregnation with a high amount of silver, while exhibiting a surface area sufficiently large so as to provide optimal dispersion of catalytically active species, in particular metal species. The invention further provides a process for producing a tableted alpha-alumina catalyst support, which comprises i) forming a free-flowing feed mixture comprising, based on inorganic solids content, at least 50 wt.-% of a transition alumina; ii) tableting the free-flowing feed mixture to obtain a compacted body; and iii) heat treating the compacted body at a temperature of at least 1100° C., preferably at least 1300° C.

Abstract: A process for producing a catalytically active multielement oxide comprising the elements Mo, W, V and Cu, wherein at least one source of the elemental constituents W of the multielement oxide is used to produce an aqueous solution, the resultant aqueous solution is admixed with sources of the elemental constituents Mo and V of the multielement oxide, drying of the resultant aqueous solution produces a powder P, the resultant powder P is optionally used to produce geometric shaped precursor bodies, and the powder P is or the geometric shaped precursor bodies are subjected to thermal treatment to form the catalytically active composition, wherein the aqueous solution used for drying comprises from 1.6% to 5.0% by weight of W and from 7.2% to 26.0% by weight of Mo, based in each case on the total amount of aqueous solution.

Abstract: The present invention relates to the use of gamma iron(III) oxide (?-Fe2O3) containing particles for the prevention of biofouling and/or growth of microorganisms. Furthermore, it relates to a method for preventing biofouling of a substrate and to a method of imparting biocidal properties to the surface of a substrate.

Abstract: The invention relates to novel silver vanadium phosphates, catalysts based on these silver vanadium phosphates and the use of these catalysts for carrying out organic reactions in the gas phase.