Abstract: A thermoplastic composition including a polycarbonatesiloxane-arylate; a phthalone compound; and optionally an additional component different from the polycarbonatesiloxane-arylate and the phthalone compound; wherein the phthalone compound has a formula: wherein Z1 represents the atoms necessary to complete a 9- to 13-membered single or fused aromatic ring structure, Z2 represents the atoms necessary to complete a pyridine or quinoline ring, each R1 and each R2 are independently halogen, an alkyl group, an aryl group, a heterocyclic group, an alkoxy group, an aryloxy group, an aromatic or aliphatic thioether group, an aromatic or aliphatic carboxylic acid ester group, or an aromatic or aliphatic amide group, a is an integer from 0 to 6, b is an integer from 0 to 4, n is 1 or 2, and X is present only if n=2 and is a single bond or a divalent organic radical bonded to the Z1 ring structure through an ether, ketone, or thio linkage.

Abstract: Methods for measuring certain properties of a crosslinked polycarbonate are disclosed. The storage modulus of a crosslinked polycarbonate is measured over a specified temperature range, and the average magnitude of the storage modulus over that temperature range is obtained. The average magnitude can be correlated to both crosslinking within the polycarbonate, and to the flame performance of the crosslinked polycarbonate.

Abstract: A thermoplastic composition including a polyaryl ester, a polymer different from the polyaryl ester, and a phthalone compound according to the formula (I) wherein Z1 represents the atoms necessary to complete a 9- to 13-membered single or fused aromatic ring structure, Z2 represents the atoms necessary to complete a pyridine or quinoline ring, each R1 and each R2 are independently halogen, an alkyl group, an aryl group, a heterocyclic group, an alkoxy group, an aryloxy group, an aromatic or aliphatic thioether group, an aromatic or aliphatic carboxylic acid ester group, or an aromatic or aliphatic amide group, a is 0 to 6, b is 0 to 4, n is 1 or 2, and X is present only if n=2 and is a single bond or a divalent organic radical bonded to the Z1 ring structure through an ether, ketone, or thio linkage.

Abstract: A thermoplastic composition comprises, based on the total weight of the polymers in the thermoplastic composition, a polycarbonatesiloxane-arylate; 2 to 15 wt % or 2 to 8 wt % or 1 to 4 wt % of a core-shell impact modifier; a flame retardant comprising a bromine-containing polymer or oligomer effective to provide 1.5 wt % to 5 wt % of bromine; an aromatic organophosphorus compound, effective to provide 0.1 to 1 wt % of phosphorus, or a combination comprising at least one of the foregoing; and optionally 0 to 80 wt % or 0 to 60 wt % of a polyetherimide.

Abstract: Processes for increasing the chemical resistance of a surface of a formed article are disclosed. The formed article is produced from a polymeric composition comprising a photoactive additive containing photoactive groups derived from a monofunctional benzophenone. The surface of the formed article is then exposed to ultraviolet light to cause crosslinking of the photoactive additive and produce a crosslinked surface. The crosslinking enhances the chemical resistance of the surface. Various means for controlling the depth of the crosslinking are also discussed.

Abstract: Photoactive additives, such as cross-linkable polycarbonate resins, are disclosed. The additive is formed from the reaction of a monohydroxybenzophenone, a dihydroxybenzophenone, a diol chain extender, and one or more linker moieties having functional groups that react with the phenolic groups on the other ingredients. If desired, a secondary linker moiety and/or an end-capping agent can be used. When added to a base polymeric resin, the photoactive additive permits crosslinking when exposed to ultraviolet light.

Abstract: Polymeric blends having improved flame retardance properties and good ductility at low temperatures are disclosed. The blend is formed from (A) a photoactive additive containing a photoactive group derived from a monofunctional benzophenone; and (B) a polymer resin which is different from the photoactive additive. The additive can be a compound, oligomer, or polymer. When exposed to ultraviolet light, crosslinking will occur between the photoactive additive and the polymer resin, enhancing the chemical resistance and flame retardance while maintaining ductility.

Abstract: A thermoplastic composition is disclosed that includes a polyaryl ester polymer or copolymer and a phthalone compound according to the formula wherein Z1 represents the atoms necessary to complete a 9- to 13-membered single or fused aromatic ring structure, Z2 represents the atoms necessary to complete a pyridine or quinoline ring, each R1 and each R2 can independently be halogen, an alkyl group, an aryl group, a heterocyclic group, an alkoxy group, an aryloxy group, an aromatic or aliphatic thioether group, an aromatic or aliphatic carboxylic acid ester group, or an aromatic or aliphatic amide group, a is an integer from 0 to 6, b is an integer from 0 to 4, n is 1 or 2, and X is present only if n=2 and is a single bond or a divalent organic radical bonded to the Z1 ring structure through an ether, ketone, or thio linkage.

Abstract: A thermoplastic composition includes a poly(carbonate-arylate ester); and an organophosphorus compound in an amount effective to provide 0.1 to 1.0 wt % phosphorus based on the total weight of the composition, wherein an article molded from the composition has a smoke density after four minutes (Ds-4) of less than or equal to 300 determined according to ISO 5659-2 on a 3 mm thick plaque and a maximum average rate of heat release emission (MAHRE) of less than or equal to 90 kW/m2 determined according to ISO 5660-1 on a 3 mm thick plaque.

Abstract: A multilayer sheet including: a base layer including a polycarbonatesiloxane-arylate; and a cap layer disposed on a side of the base layer, wherein the cap layer includes poly(ethylene terephthalate), poly(vinyl fluoride), poly(vinylidene fluoride), a silicone hardcoat, or a combination comprising at least one of the foregoing.

Abstract: Interior aircraft components comprise a thermoplastic composition comprising: a first polymer comprising bisphenol A carbonate units and monoaryl arylate units, or a second polymer comprising bisphenol A carbonate units, monoaryl arylate units, and siloxane units, or a combination comprising at least one of the foregoing polymers; and an organophosphorus compound; wherein a sample of the thermoplastic composition has: an OSU integrated 2 minute heat release test value of less than 65 kW-min/m2 and a peak heat release rate of less than 65 kW/m2, an E662 smoke test DsMax value of less than 200, a flame time of less than 15 seconds, a burn length of less than 6 inches, and a drip extinguishing time of less than 5 seconds, an energy in multiaxial impact of 100 J or more and a ductility in multiaxial impact of 100%.

Abstract: Polycarbonate articles having improved properties due to their substantially cross-linked nature are disclosed. The substantially cross-linked articles are formed by forming a product from a polymeric composition comprising a cross-linkable polycarbonate resin containing a photoactive group derived from a benzophenone, and exposing the formed product to an effective dosage of ultraviolet radiation to cause substantial cross-linking throughout the article. Such cross-linking can also be used to obtain films having good scratch resistance properties.

Abstract: Processes for increasing the chemical resistance of a surface of a formed product are disclosed. The formed product is produced from a polymeric composition comprising a photoactive additive containing photoactive groups derived from a dihydroxybenzophenone. The surface of the formed product is then exposed to ultraviolet light to cause crosslinking of the photoactive additive and produce a crosslinked surface. The crosslinking enhances the chemical resistance of the surface. Various means for controlling the depth of the crosslinking are also discussed.

Abstract: Disclosed herein are compositions including a cross-linked polycarbonate. The cross-linked polycarbonate may be derived from a polycarbonate having about 0.5 mol % to about 5 mol % endcap groups derived from a monohydroxybenzophenone. A plaque including the composition can achieve a UL94 5VA rating. Also disclosed herein are articles including the compositions, methods of using the compositions, and processes for preparing the compositions.

Abstract: Disclosed herein are processes for preparing articles from compositions including a cross-linked polycarbonate. The cross-linked polycarbonate may be derived from a polycarbonate having about 0.5 mol % to about 5 mol % endcap groups derived from a monohydroxybenzophenone. The article is molded, then exposed to UV radiation. A plaque including the composition can achieve a UL94 5VA rating.

Abstract: A thermoplastic composition comprises, based on the total weight of the thermoplastic composition, 10 to 45 wt. % of a poly(etherimide); 35 to 90 wt. % of a poly(carbonate-siloxane); 0.5 to 20 wt. % of compatibilizer polycarbonate component comprising a poly(carbonate-arylate ester); up to 15 wt. % of an ultraviolet light stabilizer; and 0 to 30 wt. % of TiO2; wherein a sample of the composition has a notched Izod impact energy of at least 200 J/m at 23° C. measured in accordance to ASTM D256; and an at least 50% higher notched Izod impact energy value compared to the composition without the compatibilizer component measured in accordance to ASTM D256.

Abstract: A thermoplastic composition comprises, based on the total weight of the thermoplastic composition, 10 to 45 wt. % of a poly(etherimide); 35 to 90 wt. % of a polycarbonate component comprising a polycarbonate homopolymer, a poly(carbonate-siloxane), or a combination thereof; 0.5 to 20 wt. % of a compatibilizer polycarbonate component comprising a poly(carbonate-arylate ester), a phthalimidine copolycarbonate, or a combination thereof; up to 5 wt. % of an ultraviolet light stabilizer; and 0 to 20 wt. % of TiO2, wherein a sample of the composition has a 50% higher notched Izod impact energy value compared to the composition without the compatibilizer component.

Abstract: Disclosed herein are compositions including a cross-linked polycarbonate. The cross-linked polycarbonate may be derived from a polycarbonate having about 0.5 mol % to about 5 mol % endcap groups derived from a monohydroxybenzophenone. A plaque including the composition can achieve a UL94 5VA rating. Also disclosed herein are articles including the compositions, methods of using the compositions, and processes for preparing the compositions.

Abstract: Methods for measuring certain properties of a crosslinked polycarbonate are disclosed. The storage modulus of a crosslinked polycarbonate is measured over a specified temperature range, and the average magnitude of the storage modulus over that temperature range is obtained. The average magnitude can be correlated to both crosslinking within the polycarbonate, and to the flame performance of the crosslinked polycarbonate.

Abstract: A railway vehicle component, wherein the component is a partition or a light cover, and wherein the component is molded or formed from a thermoplastic polymer composition comprising: a siloxane-containing copolymer in an amount effective to provide a total of 0.2 to 6.5 wt % of siloxane units based on the total weight of the polymers in the thermoplastic polymer composition, a bromine-containing polymer in an amount effective to provide 9 to 13 wt % of bromine, based on the total weight of the polymers in the thermoplastic polymer composition, and optionally a third polymer, wherein the wt % of the siloxane-containing copolymer, the bromine-containing polymer, and the optional third polymer, sum to 100 wt %, and 0.05 to 10 wt % of a light diffuser additive, based on the total weight of polymers in the thermoplastic polymer composition.