Abstract: A process for the preparation of substantially polycrystalline silicon carbide fibers is provided. The fibers may be fabricated to have a small diameter and are thermally stable at high temperatures. The process is carried out by initially forming fibers from a preceramic polymeric precursor comprising methylpolysilane resins. The fibers are then infusibilized to render them nonmelting followed by a pyrolysis step in which the fibers are heated to a temperature in excess of 1600.degree. C. in a nonoxidizing atmosphere to form substantially polycrystalline silicon carbide fibers. The substantially polycrystalline silicon carbide fibers which are formed by the process of the present invention have at least 75% crystallinity and have a density of at least about 2.9 gm/cm.sup.3. The polymeric precursor or the fibers contain, or have incorporated therein, at least about 0.2% by weight boron.