Abstract: Magnetic iron oxide pigments useful in manufacturing magnetic recording media are prepared by a method which comprises coating a magnetic iron oxide core particle material having the composition FeO, wherein x is from 1.33 to 1.5, in a first step with a preliminary coating of a cobalt-containing bertholloid material or a material having the composition Co.sub.x Fe.sup.II.sub.l-x Fe.sup.III.sub.2 O.sub.4 wherein x is greater than zero but less than or equal to 1 and then in a second step the preliminary coated particle is coated with a cobalt compound.

Abstract: Acicular magnetic iron oxide pigments are disclosed which have a Co content of 1 to 5% by weight and an FeO content of 5 to 12% by weight. The pigments may optionally contain an additional dopant selected from zinc, phosphate and SiO.sub.2. The pigments are useful in magnetic recording media such as video tapes.

Abstract: Magnetic iron oxide pigments useful in magnetic signal recordings having a dependence of coercivity on temperature in the temperature range of from 76K to 298K of less than 0.13 kA/mK and having a coercivity on powder compressed to 0.9 g/cm.sup.3 of greater than 51 kA/m are prepared by coating a magnetic iron oxide core material having the composition FeO.sub.x where x is a number from 1.33 to 1.5 in a first step with a compound containing divalent and trivalent iron having a ratio of Fe(III): Fe(II) from 0.01 to less than 2, and then in a second step coating the pre-coated core with a second coating of a cobalt compound.

Abstract: Magnetic iron oxide pigments having a monomolecular coating of a cobalt compound useful in magnetic signal recordings having a dependence of coercivity on temperature in the temperature range of from 76 K to 298 K of less than 0.13 kA/mK and having a coercivity on powder compressed to 0.9 g/cm.sup.3 of greater than 51 kA/m are prepared applying a preliminary coating of Fe.sub.3 O.sub.4 or a bertholloid compound to a magnetic iron oxide core material having the composition FeO.sub.x where x is a number from 1.33 to 1.55 and then covering the preliminary coating with a cobalt compound.

Abstract: Isometric oxidation resistant and heat resistant iron oxide black pigments having a foreign metal content of less than 5 ppm of each of As, Pb and Ba, less than 200 ppm total of Ca, BaSO.sub.4, Zn, Sb and Cr and from 0.05 to 2% by weight, calculated as trivalent or tetra-valent oxides, of B, Al, Ga, Si, Ge and Sn, are useful in coloring lacquers, thermoplastic synthetic resins and building materials as well as for low coercivity iron oxide black pigments in magnetic toners.

Abstract: In improved cobalt coated magnetic iron oxide having increased coercive field strength and highly efficient for use in magnetic recording devices and processes is produced by subjecting uncoated magnetic iron oxide particles to an acid treatment and then epitaxially coating the treated particles with cobalt.

Abstract: A process for increasing the color purity of iron oxide pigment particles admixed with color-modifying impurities and obtained by the Penniman process or the aniline process, comprising introducing the particles into a magnetic field, and removing from the magnetic field two fractions of different magnetizability, the first fraction being iron oxide pigment particles of increased color purity and the second fraction being enriched in impurities.

Abstract: In the production of needle-shaped magnetic iron oxide pigments by treating iron with a nitro-aromatic in the presence of .alpha.-FeOOH nuclei to form .alpha.-FeOOH particles and an amino-aromatic, and thereafter dehydrating the .alpha.-FeOOH particles and reducing them, the improvement which comprises forming the .alpha.-FeOOH nuclei at about 0.degree. to 90.degree. C. in a suspension of metallic iron, an iron-(II)-salt and a nitro-aromatic by adding a basic precipitant in about 10 to 95% of the amount required for the complete precipitation of the iron in the iron-(II)-salt. Advantageously the metallic iron comprises cast iron, the nitro-aromatic comprises nitrobenzene, the amino-aromatic comprises aniline, the basic precipitant comprises at least one of ammonia and a basically reacting alkali metal, alkaline earth metal or ammonium salt, the nuclei formation is carried out at about 10.degree. to 60.degree. C.